The difference of haemocompatibility of medical 316L stainless steel passivated by nitric acid (NT) and citric acid (CT) was studied. Platelet adhesion and protein adsorption were studied to evaluate the haemocompatibility of the 316L stainless steel passivated by the two different methods. XPS analysis, water contact angle and surface charge measurement were used to analyze the surface properties of the steel such as chemical composition and depth distribution of the main elements in passivated films, surface energy and surface charge. The results showed that the 316L steel passivated by citric acid displayed better haemocompatibility, which could be related to the higher surface energy and relatively lower surface charge. The results also showed that the polar component of surface energy was of linear relation with the albumin adsorption on 316L stainless steel while the surface charge had the same relation with fibrinogen adsorption.
SHI Yong-Juan
,
REN Yi-Bin
,
YANG Ke
,
ZHANG Bing-Chun
. THE EFFECT OF PASSIVATION ON THE HAEMOCOMPATIBILITY OF 316L STAINLESS STEEL[J]. Acta Metall Sin, 2011
, 47(12)
: 1575
-1580
.
DOI: 10.3724/SP.J.1037.2011.00520
[1] Shahryari A,Azari F, Vali H, Omanovic S. Acta Biomater, 2010; 6: 695
[2] Shih C C, Shih C M, Su Y Y, Su L H J, Chang M S, Lin S J. Corros Sci, 2004; 46: 427
[3] Shahryari A, Omanovic S, Szpunar J A. Mater Sci Eng, 2008; C28: 94
[4] Barbosa M A. Corros Sci, 1983; 23: 1293
[5] Noh J S, Laycock N J, Gao W, Wells D B. Corros Sci, 2000; 42: 2069
[6] Hong T, Ogushi T, Nagumo M. Corros Sci, 1996; 38: 881
[7] Ma L Y, Ding Y, Ma L Q, Yao C R, Shen W D. Surf Technol, 2007; 36: 39
(马李洋, 丁毅, 马立群, 姚春荣, 沈卫东. 表面技术, 2007; 36: 39)
[8] Rodrigues S N, Gon¸calves I C, Martins M C L, Barbosa M A, Ratner B D. Biomaterials, 2006; 27: 5357
[9] Mitsakakis K, Lousinian S, Logothetidis S. Biomol Eng, 2007; 24: 119.
[10] Huang Y, Xiaoying L, Qian W, Tang Z, Zhong Y. Acta Biomater, 2010; 6: 2083.
[11] Gray J J. Curr Opin Struct Biol, 2004; 14: 110
[12] Anselme K. Biomaterials, 2000; 21: 667
[13] MacDonald D E, Rapuano B E, Deo N, Stranick M, Somasundaran P, Boskey A L. Biomaterials, 2004; 25: 3135
[14] Cacciafesta P, Humphris A D L, Jandt K D, Miles M J. Langmuir, 2000; 16: 8167
[15] Gon¸calves I C, Martins M C L, Barbosa M A, Ratner B D. Biomaterials, 2005; 26: 3891
[16] Dion I, Baquey C, Candelon B, Monties J. Int J Artif Organs, 1992; 15: 617
[17] Yuan Y, Liu C, Yin M. J Mater Sci: Mater Med, 2008; 19: 2187
[18] Kaelble D H, Moacanin J. Polymer, 1977; 18: 475
[19] Michiardi A, Aparicio C, Ratner B D, Planell J A, Gil J. Biomaterials, 2007; 28: 586
[20] Nyilas E, Ward Jr R. J Biomed Mater Res, 1977; 11: 69
[21] Depalma V, Baier R, Ford J, Gott V, Furuse A. J Biomed Mater Res, 1972; 6: 37