The lattice constants of the matrix phase γ and the precipitated phase γ' in a wafer-like nickel-base single crystal superalloy DD10 were determined by four-axis X-ray diffractometer (XRD). The variations of the lattice constants and lattice mismatches of γ and γ' phases in the alloy wafer with different thicknesses, i.e., different interphase restriction conditions were obtained. A critical thickness of the alloy wafer to reach an unstable stress state was defined based on the observed changes of lattice mismatch associated with a transformation of stress state from the 3D bulk state to 2D plane state. The lattice mismatches corresponding to different mismatch stress states were calculated. The lattice constants of the γ and γ' phases under a relaxed non--mismatch stress state were evaluated based on certain assumptions. The results showed that after the thickness of the alloy wafer reached the critical value, the lattice constant of the γ' phase decreased linearly with the decrease of the thickness, whereas that of the γ phase kept nearly constant, resulting in a linear increase of the absolute value of lattice mismatch. Accompanied with the thinning process, the crystal lattice misorientation and the mosaicity increased, the γ/γ' interphase restraint reduced and the interphase stress relaxed, and the measured stress state changed to the plane state. The estimated critical thickness and the lattice constants under non-mismatch stress state could provide references for the design of the components and the measurement of the residual stress in the superalloy.
YU Wei-Dao
,
WU Mi-Dong
,
YU Su-Cheng
,
LI Wu-Hui
. X-RAY DIFFRACTION ANALYSIS ON THE THICKNESS EFFECT OF γ/γ' LATTICE MISMATCHE IN NICKEL BASE SINGLE CRYSTAL SUPERALLOY DD10[J]. Acta Metall Sin, 2011
, 47(11)
: 1418
-1425
.
DOI: 10.3724/SP.J.1037.2011.00307
[1] Glatzel U, Feller–Kniepmejer M. Scr Metall, 1989; 23: 1839
[2] Kuhn H A, Biermann H, Ungar T, Mughrabi H. Acta Metall, 1991; 39: 2783
[3] Socrate S, Parks D M. Acta Metall Mater, 1993; 41: 2185
[4] Mukherji D, Gilhs R, Barbier B, Genovese D D, Hasse B, Strunz P, Wroblewski T, Fuess H, Rosler J. Scr Mater, 2003; 48: 333
[5] Meng F L, Tian S G, Wang M G, Yu X F, Du H Q, Shui L, Hu Z Q. Chin J Mater Res, 2007; 21: 228
(孟凡来, 田素贵, 王明罡, 于兴福, 杜洪强, 水丽, 胡壮麒. 材料研究学报, 2007; 21: 228)
[6] Hu Z Q, Peng P, Liu Y, Jin T, Sun X F. Acta Metall Sin, 2002; 38: 1121
(胡壮麒, 彭平, 刘 轶, 金涛, 孙晓峰, 管恒荣. 金属学报, 2002; 38: 1121)
[7] Marty B, Moretto P, Gergaud P, Lebrun J L, Ostolaza K, Ji V. Acta Mater, 1997; 45: 791
[8] Wu E D, Zhang J, Chen B, Sun G A, Ji V, Hughes D, Pirling T. J Phys: Condens Matter, 2008; 20: 104255
[9] Merchant H D. J Electron Mater, 1997; 26: 833
[10] Hyun S, Brown W L, Vinci R P. Appl Phys Lett, 2003; 83: 4411
[11] Gilles R, Mukherji D, Hoelzel M, Strunz P, Toebbens D M, Barbier B. Acta Mater, 2006; 54: 1313
[12] Mukherji D, Wahi R P. Scr Mater, 1997; 36: 1233
[13] M¨uller L, Glatzel U, Feller–Kniepmeier M. Acta Metall Mater, 1992; 40: 1321
[14] Muller L, Link T, Feller–Kniepmeier M. Scr Metall, 1992; 26: 1298
[15] Floreen S. Eng Fract Mech, 1979; 11: 55
[16] Yue Z F, Lu Z Z, Zhou L, Zheng C Q. Acta Metal Sin, 1997; 33: 265
(岳珠峰, 吕震宙, 周 利, 郑长卿. 金属学报, 1997; 33: 265)
[17] Orosz R, Krupp U, Christ H J, Monceau D. Oxid Met, 2007; 68: 165
[18] Pant P, Schwarz K W, Baker S P. Acta Mater, 2003; 51: 3243
[19] Ganghoffer J F, Hazotte A, Denis S, Simon A. Scr Metall Mater, 1991; 25: 2491