STRESS ORIENTED HYDROGEN INDUCED CRACKING BEHAVIOR OF HEAT AFFECTED ZONE OF L360MCS STEEL IN WET H2S ENVIRONMENT
Received date: 2009-10-10
Revised date: 2010-01-28
Online published: 2010-05-11
Supported by
Supported by National Natural Science Foundation of China (No.50871122), Specialized Research Fund for the Doctoral Program of Higher Education (No.20070425021})
Stress oriented hydrogen induced cracking (SOHIC) behavior of heat affected zone (HAZ) of L360MCS steel in wet H$_{2}$S
environment was studied by separating crack, SEM and EDS. The cracks are formed by four--point bending test in
wet H$_{2}$S environment. The microstructure of HAZ is obviously different from
the base metal, and the hardness of HAZ is lower than those of the base metal and welding joint. The fracture
surface of the cracks was separated and the hydrogen blisters were torn off. The cross section and fracture surface of
the cracks are analyzed by SEM and EDS. Results show that the cracks of SOHIC appeared as axial crack and vertical
crack, and the former is preferential. The appearance of cracks is associated with the low hardness value of
HAZ. The dimension of hydrogen blasters in tension stress zone of bended specimen is bigger than that in
unstressed specimen, which is due to hydrogen concentration in bended specimen is higher. Both axial and vertical
cracks nucleate independently and propagate in the quasi--cleavage manner. Tension stress not only increases the
supersaturated hydrogen concentration in tension stress zone but directly promotes vertical crack propagation.
Axial crack nucleates at MnS, CaS and precipitated phase, and propagates under internal hydrogen pressure.
Vertical crack mainly nucleates on precipitated phase and propagates under both internal hydrogen pressure and
tensile stress.
ZHOU Cheng-Shuang . STRESS ORIENTED HYDROGEN INDUCED CRACKING BEHAVIOR OF HEAT AFFECTED ZONE OF L360MCS STEEL IN WET H2S ENVIRONMENT[J]. Acta Metall Sin, 2010 , 46(5) : 547 -553 . DOI: 10.3724/SP.J.1037.2009.00669
[1] Pargeter R J. In: NACE, ed., Corrosion 2007, Houston, TX: NACE, 2007: 115
[2] Guo H, Li G F, Cai X, Yang W. Acta Metall Sin, 2004; 40: 967
(郭浩, 李光福, 蔡珣 , 杨武. 金属学报, 2004; 40: 967)
[3] Ren X C, Wu M, Chu W Y, Li J X, Jiao L J, Jiang B, Chen G, Cui Y H. Acta Metall Sin, 2007; 43: 149
(任学冲, 武明, 褚武扬, 李金许, 乔利杰, 江波, 陈 刚, 崔银会. 金属学报, 2007; 43: 149)
[4] Liu Z Y, Zhai G L, Dui C W, Li X G. Acta Metall Sin, 2008; 44: 209
(刘智勇, 翟国丽, 杜翠薇, 李晓刚. 金属学报, 2008; 44: 209)
[5] Guo J, Yang S W, Shang C J, Wang Y, He X L. Corros Sci, 2008; 51: 242
[6] Ernesto V, Andrej A. Eng Fail Anal, 2009; 16: 164
[7] Cayard M S, Kane R D, Cooke D L. In: NACE, ed., Corrosion 97, Houston, TX: NACE, 1997: 525
[8] Cayard M S, Kane R D, Horvath R J. In: NACE ed., Corrosion 2002, Houston, TX: NACE, 2002: 554
[9] Orie K E, Fletcher F B. In: NACE, ed., Corrosion 99, Houston, TX: NACE, 1999: 632
[10] NACE International. NACE Standard MR0177–2005, Houston, 2005
[11] ASTM. ASTM Standard G39–99, Philadelphia, 2005
[12] NACE International. NACE Standard MR0284–2003, Houston, 2003
[13] Zhao M C, Shan Y Y, Qu J B, Xiao F R, Zhong Y, Yang K. In: CSM ed., CSM 2001 Annual Meeting Proceedings. Beijing: Metallurgical Industry Press, 2001: 891
(赵明纯, 单以银, 曲锦波, 肖福仁, 仲勇, 杨柯. 见中国金属学会主编, 2001年中国钢铁年会论文集.
北京: 冶金工业出版社, 2001: 891)
[14] Lee H W. Mater Sci Eng, 2007; A445: 328
[15] Sojka J, Jerome M, Sozanska M, Vanova P, Rytirova L, Jonsta P. Mater Sci Eng, 2008; A430: 237
[16] Wan K K, Seong U K, Boo Y Y, Kyoo Y K. Corros Sci, 2008; 50: 3336
[17] Parkins R N. Corrosion, 1987; 43: 130
[18] Chu R, Chen W, Wang S H. Corrosion, 2004; 60: 275
[19] Lynch S P. In: NACE, ed., Corrosion 2007, Houston, TX: NACE, 2007: 493
[20] Maroecic P, Mclellan R B. Acta Metall, 1998; 46: 5593
[21] Zang D, MeLellan R B. Acta Metall, 1999; 47: 1671
[22] Harada S, Ono D, Sugimoto H, Fukai Y. J Alloys Compd, 2007; 446: 474
[23] Rebak R B, Xia Z, Safruddin R, Szklarska S Z. Corrosion, 1996; 52: 396
/
| 〈 |
|
〉 |