Acta Metall Sin  1998, Vol. 34 Issue (11): 1163-1166    DOI:

Current Issue | Archive | Adv Search |

EFFECT OF METALLURGICAL FACTORS ON THE RESISTANCE OF CAVITATION EROSION OF Ni_3Al BASED ALLOYS

YE Wujun;FENG Di;CHEN Beijing;LUO Heli (Central Iron and Steel Research institute; BeiJing 100081)

YE Wujun;FENG Di;CHEN Beijing;LUO Heli (Central Iron and Steel Research institute; BeiJing 100081). EFFECT OF METALLURGICAL FACTORS ON THE RESISTANCE OF CAVITATION EROSION OF Ni_3Al BASED ALLOYS. Acta Metall Sin, 1998, 34(11): 1163-1166.

Abstract References Related Articles Recommended Metrics Download:  PDF(362KB)  Export:  BibTeX | EndNote (RIS)       Abstract  Effect of Al, Cr, Fe and Mo concentrate on the resistance of cavitation erosion of Ni3Al based alloys was studies, the results show that Zr and B toughened Ni3Al alloy with Al concentrate of 6%-9% possesses excellent resistance of cavitation erosion and the decrease of the γ' forming elements concentrate causes the decline of the resistance of cavitation erosion. The introduction of Fe and Mo somewhat decreases the resistance to cavitation erosion. Key words:  Ni_3Al alloy      cavitation erosion      Received:  18 November 1998      Service E-mail this article Add to citation manager E-mail Alert RSS Collect articles（0） Articles by authors URL:  https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1998/V34/I11/1163 1 Sikka V K, Mavity J T. Mater Sci Eng, 1992; A153:172 2 Johnson M L,Mikkola D E,Wright R N .Intermetallics,1995:(3):389 3 Han G W,Feng D,Ye W J.High Technolo lett,1993;(10):13 4 Ye W J,Feng D.J Iron Steel Res,1997;9:231 5 David S A,Jemian W A,Liu C T,Horton J A. Weld J, 1985;(1):225? [1] LIU Haixia, CHEN Jinhao, CHEN Jie, LIU Guanglei. Characteristics of Waterjet Cavitation Erosion of 304 Stainless Steel After Corrosion in NaCl Solution[J]. 金属学报, 2020, 56(10): 1377-1385. [2] Yanxin QIAO,Shuo WANG,Bin Liu,Yugui ZHENG,Huabing LI,Zhouhua JIANG. SYNERGISTIC EFFECT OF CORROSION AND CAVITATION EROSION OF HIGH NITROGEN STAINLESS STEEL[J]. 金属学报, 2016, 52(2): 233-240. [3] LIU Shihan CHEN Darong. MECHANICS MECHANISM OF DUPLEX STEEL CAVITATION DAMAGE[J]. 金属学报, 2009, 45(5): 519-526. [4] JIANG Shengli; ZHENG Yugui; YAO Zhiming. Damage Behavior of 20SiMn Low Alloy Steel in Slurry with Different Particle Sizes[J]. 金属学报, 2004, 40(2): 163-167 . [5] ZHANG Guangping;WANG Zhongguang (State Key Laboratory for Fracture and Fatigue of Materials; Institute of Metal Research; Chinese Academy of Sciences;Shenyang 110015). EFFECTS OF CRYSTAL ORIENTATION AND LOAD MODE ON FATIGUE BEHAVIOR IN Ni_3Al ALLOY SINGLE CRYSTALS[J]. 金属学报, 1997, 33(10): 1009-1014. [6] JIN Cheng;LIN Dongliang Shanghai University of Technology Shanghai Jiaotong University. INFLUENCE OF STRESS ON COMPOSITION OF OXIDE SCALE IN Ni_3Al ALLOYS[J]. 金属学报, 1993, 29(10): 73-75. [7] ZHENG Qiguang;LI Jiarong;LI Zaiguang Huazhohg University of Science and Technology; Wuhan; HU Weiguang PLA Unit No. 38609; TIAN Hongye PLA Factory No. 4808. EFFECT OF LASER TREATMENT ON CAVITATION EROSION RESISTANCE OF DIESEL CYLINDER[J]. 金属学报, 1991, 27(3): 116-120. No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed