RESERCH OF THE INITIAL ATMOSPHERIC CORROSION OF CARBON STEEL Q235 IN DIFFERENT CONCENTRATION OF SO2

Acta Metall Sin

2008, Vol. 44

Issue (6): 729-734 DOI:

Research Articles

Current Issue | Archive | Adv Search

RESERCH OF THE INITIAL ATMOSPHERIC CORROSION OF CARBON STEEL Q235 IN DIFFERENT CONCENTRATION OF SO2

wang chuan

中国科学院金属研究所材料环境腐蚀研究中心

Cite this article:

wang chuan. RESERCH OF THE INITIAL ATMOSPHERIC CORROSION OF CARBON STEEL Q235 IN DIFFERENT CONCENTRATION OF SO2. Acta Metall Sin, 2008, 44(6): 729-734 .

Download:

PDF(2203KB)
Export: BibTeX | EndNote (RIS)

Abstract The influence of the different concentration of SO2 on the initial atmospheric corrosion of carbon steel Q235 was investigated.The corrosion kinetics of carbon steel Q235 in different condition was researched .The variation of thickness loss of Q235 in different concentration of SO2 made a great difference. Fourier transform infrared spectroscopy(FTIR) and electron dispersion X-ray analysis(SEM／EDAX)were used to characterize the corrosion products of Q235．The effect of S and O elements in the layer of rust are discussed the mechanism of rust nests is analysed. A probable mechanism is presented to explain the experimental results．

Key words:

Received: 31 August 2007

ZTFLH:	TF803.2
	TG172.3

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	wang chuan

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y2008/V44/I6/729

[1]Wang Z Y.Total Corros Control,1995;9(4):1 (王振尧．全面腐蚀控制，1995；9(4)：1)
[2]Lin C,Li X G,Wang G Y.Corros Sci Prot Technol,2004; 16:90 (林翠，李晓刚，王光雍．腐蚀科学与防护技术，2004；16：90)
[3]Weissenriederz J,Leygraf C.J Electrochem Soc,2004;151 (3):165
[4]Weissenriederz J,Kleber C,Schreiner M.J Electrochem Soc,2004;151:497
[5]Wang 3 H,Wei F I,Chang Y S.Mater Chem Phys,1997; 47:1
[6]Asami K,Kikuchi M.Corros Sci,2003;45:2671
[7]Hoed S,Mazaudier F,Dilhnann Ph,Santarini G.Corros Sci,2004;46:1431
[8]Emirates S.En9 Res,2006;11(1):1
[9]Oesch S.Corros Sci,1996;38:1357
[10]Wang Z Y,Wang C,Han W.Equip Environ Eng,2006; 3(5):16 (王振尧，汪川，韩薇．装备环境工程，2006；3(5)：16
[11]Lin C.PhD Thesis,University Science and Technology Beijing,Beijing,2004 (林翠．北京科技大学博士学位论文，北京，2004)
[12]Qu Q,Yan C W,Cao C N.Acta Metall Sin,2002;38: 1062 (屈庆，严川伟，曹楚南．金属学报，2002；38：1062)
[13]Yang X M.Spectrosc Spectral Anal,2006;26:2047 (杨晓梅．光谱学与光谱分析，2006；26：2047)
[14]Persson D,Leygraf C.J Electrochem Soc,1993;140:1257
[15]Yang X M.Ningxia Univ(Nat Sci),1999;20:47 (杨晓梅．宁夏人学学报(自然科学版)，1999；20：47)
[16]Leidheiser H,Music S.Corros Sci,1982;22:1089
[17]Singh A K,Ericsson T,Gullman J.Corros Sci,1985;25: 931
[18]Misawa T,Kyuno T,Suctaka W.Corros Sci,1971;11:35
[19]Cox A,Lyon S B.Corros Sci,1994;36:1177
[20]Liu X C,An C Q.The Corrosion of Metal.Beijing:Na- tional Defence Industry Press,2002:229 (刘秀晨，安成强．金属腐蚀学．北京：国防工业出版社，2002：229)
[21]Lyon S B,Thomson G E,Johnson J B.Corrosion,1987; 43:719
[22]Philip A,Schweitaer P E.Atmospheric Degradation and Corrosion Control.New York:Marcel Dekker Inc Press, 1999:42
[23]Graedel T E,Frankenthal R P.J Electrochem Soc,1990, 137:2385
[24]Marcus P,Oudar J.Corrosion Mechanism in Theory and Practice.New York:Marcel Dekker Inc Press,2002:54
[25]Leygraf C,Graedel T.Atmospheric Corrosion.New York: John Wiley & Sons Press,2000:72
[26]Cox A,Lyon S B.Corros Sci,1994;36:1193

[1]	WANG Luning, LIU Lijun, YAN Yu, YANG Kun, LU Lili. *Influences of Protein Adsorption on the in vitro* Corrosion of Biomedical Metals**[J]. 金属学报, 2021, 57(1): 1-15.
[2]	TUNG Feng'en;WANG Yuming Institute of Materials Science; Jilin University; Changchun. X-RAY ANALYSIS OF WORK-HARDENING PROCESS FOR POLYCRYSTALLINE а-BRASS DURING UNIAXIAL TENSILE TEST[J]. 金属学报, 1989, 25(2): 82-84.
[3]	WANG Jinliang, WANG Chenchong, HUANG Minghao, HU Jun, XU Wei. The Effects and Mechanisms of Pre-Deformation with Low Strain on Temperature-Induced Martensitic Transformation[J]. 金属学报, 2021, 57(5): 575-585.
[4]	DU Hegui;LIU Xin Northeast University of Technology; Shenyang. KINETICS OF CARBON COMBUSTION IN PLASMA AIR[J]. 金属学报, 1989, 25(2): 85-88.
[5]	. [J]. 金属学报, 2001, 37(1): 42-46 .
[6]	. [J]. 金属学报, 1999, 35(3): 320-324 .
[7]	. [J]. 金属学报, 2000, 36(1): 72-76 .
[8]	. [J]. 金属学报, 1999, 35(3): 330-333 .
[9]	. [J]. 金属学报, 1999, 35(3): 334-336 .
[10]	. [J]. 金属学报, 2000, 36(6): 647-650 .
[11]	. [J]. 金属学报, 2000, 36(6): 655-658 .
[12]	No Author. ACTA METALLURGLCA SLNLCA Volume 28 Series A 1992 SUBJECT INDEX[J]. 金属学报, 1992, 28(12): 63-90.
[13]	. [J]. 金属学报, 2000, 36(7): 780-784 .
[14]	No Author. ACTA METALLURGICA SINICA(JINSHU XUEBAO) Volume 28 1992 AUTHOR INDEX[J]. 金属学报, 1992, 28(12): 71-94.
[15]	Хань Яо-вэнь Инсмцмум мемаддов АН КНР;Г.н.Ойкс Московскц цнсмцмум смадц. НЗУЧЕНИЕ ПРОЦЕССОВ ДЕСУЛЬФУРАЦИИ ХНДКОΓО МЕТАЛЛА В ВАКУУМЕ[J]. 金属学报, 1963, 6(2): 98-110.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed