Microstructure Evolution of AZ91D Magnesium Alloy During Semi-Solid Isothermal Heat Treatment Under Direct Current
ZHOU Quan; YANG Yuansheng; TANG Junli; HU Zhuangqi
Institute of Metal Research; The Chinese Academy of Sciences; Shenyang 110016
Cite this article:
ZHOU Quan; YANG Yuansheng; TANG Junli; HU Zhuangqi. Microstructure Evolution of AZ91D Magnesium Alloy During Semi-Solid Isothermal Heat Treatment Under Direct Current. Acta Metall Sin, 2006, 42(1): 28-34 .
[1]Mordike B L,Elbert T.Mater Sci Eng,2001;A302:37 [2]Kojima Y.Mater Trans,2001;42:1154 [3]Aghion E,Bronfin B.Mater Sci Forum,2000;350-351:19 [4]Eliezer D,Aghion E,Fores F H.Adv Perfor Mater,1998;5:201 [5]Harutoshi M,Toshio S.Material,1999;38:317 [6]Zhu M F,Su H Q.Foundry,1996;(4):1(朱鸣芳,苏华钦.铸造,1996;(4):1) [7]Li Y D,Hao Y,Yan F Y,Fang M.Chin Nonferrous Met,2001;11:571(李元东,郝远,闫峰云,方铭.中国有色金属学报,2001;11:571) [8]Li Y D,Hao Y,Chen T J,Ma Y.Chin Nonferrous Met,2004;14:366(李元东,郝远,陈体军,马颖.中国有色金属学报,2004;14:366) [9]Kim J M,Kim K T,Jung W J.Mater Sci Technol,2002;18:688 [10]Misra A K.Metall Trans,1985;16A:1354 [11]The Chinese Foundry Association.Casting Manuals.Vol.3.Beijing:China Machine Press,1995:171(中国铸造专业学会.铸造手册.第3卷.北京:机械工业出版社,1995:171) [12]Massalski T B,Okamoto H,Subramanian P R,Kacprzak L.Binary Alloy Phase Diagrams,2nd ed,Mepals Park,Olt:ASM International,1990:170 [13]Kukushkin S A.Acta Metal,1994;42:715 [14]Li W F,Yang Y S,Yu L,Zhang Y,Hu Z Q.Mater Eng,2001;(9):8(李万峰,杨院生,于力,张匀,胡壮麒.材料工程,2001;(9):8) [15]Lakshmanan T S,Olson D L,Rigney D A.Scr Metall,1971;5:1099 [16]Coriell S R,McFadden G B,Wheeler A A,Hurle D T.J Cryst Growth,1989;94:334 [17]Dabo Y,Nguyen T H,Coriell S R,McFadden G B,Li Q,Billia B.J Cryst Growth,2000;216:483