Acta Metall Sin  2020, Vol. 56 Issue (7): 937-948    DOI: 10.11900/0412.1961.2019.00291
Current Issue | Archive | Adv Search |
Low-Cycle Fatigue Behavior of 1100 MPa Grade High-Strength Steel
ZHOU Hongwei1,2, BAI Fengmei3,4(), YANG Lei1,2, CHEN Yan1,2, FANG Junfei1,2, ZHANG Liqiang3, YI Hailong4, HE Yizhu1,2
1. Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, Anhui University of Technology, Maanshan 243032, China
2. School of Materials Science and Engineering, Anhui University of Technology, Maanshan 243032, China
3. School of Metallurgical Engineering, Anhui University of Technology, Maanshan 243032, China
4. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China
Cite this article: 

ZHOU Hongwei, BAI Fengmei, YANG Lei, CHEN Yan, FANG Junfei, ZHANG Liqiang, YI Hailong, HE Yizhu. Low-Cycle Fatigue Behavior of 1100 MPa Grade High-Strength Steel. Acta Metall Sin, 2020, 56(7): 937-948.

Download:  HTML  PDF(3391KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  

The low-cycle fatigue (LCF) behavior of 1100 MPa grade tempered high strength steel under symmetrical strain control conditions was studied at the strain amplitude ranges of 0.4%~1.2% in this work. The LCF properties of quenching and tempering high strength steel were examined by means of OM, SEM and TEM. The microstructure changes, fracture morphology, crack propagation characteristics and inclusion morphology were studied in detail. The results show that the cyclic hardening and cyclic softening depend on strain amplitude. At the low strain amplitude of 0.4%, rapid cyclic hardening occurs in initial 10 cyc, and then the stress remains almost unchanged until the sample breaks. While at the strain amplitude ranges of 0.5%~1.2%, the cyclic hardening reaches a peak at the first few cycles, followed by the remarkable cyclic softening until the sample fails. The cyclic softening is mainly due to the recovery of some martensite lath under low-cycle fatigue loading and the decrease of dislocation density in the laths. 1100 MPa grade high-strength steel is found to obey LCF Manson-Coffin relationship. The high-strength steel has excellent LCF performance for two main reasons, which is related with the shape and size of inclusions. One is that the shape of the inclusion is nearly circular, and the diameter is 2~5 μm, which is lower than the critical dimension of the inclusions causing fatigue crack initiation. The crack is initiated on the surface of the sample. This increases fatigue crack initiation life. The other one is that the original austenite grain boundary, the martensite packet/block boundary and the inclusions or cavities can induce the crack deflection, reducing the crack propagation rate and increasing fatigue crack propagation life.

Key words:  high-strength steel      low-cycle fatigue      inclusion      fatigue fracture      crack propagation     
Received:  04 September 2019     
ZTFLH:  TG142.1,TG111.8  
Fund: Joint Fund of National Natural Science Foundation of China(U1760108);National Natural Science Foundation of China(51674079);National Natural Science Foundation of China(51874001);Natural Science Foundation of Anhui Provincial Education Department(KJ2018A0062);Natural Science Foundation of Anhui Provincial Education Department(KJ2019A0059)

URL: 

https://www.ams.org.cn/EN/10.11900/0412.1961.2019.00291     OR     https://www.ams.org.cn/EN/Y2020/V56/I7/937

Fig.1  Specimen geometry used in low-cycle fatigue (LCF) tests (unit: mm)
Fig.2  Cyclic stress response curves of high-strength steels under different strain amplitudes (Nf—the number of cycles to failure)
Fig.3  The low-cycle fatigue curves of high-strength steels
(a) Manson-Coffin equation fitting curve for 1100 MPa grade steel(b) comparison of the LCF curves of several high-strength steels
High-strength steelσ0.2 / MPaσb / MPaδ / %MicrostructureRef.
1100 MPa grade1160135517.8Tempered lath martensite-
ASTM A7231170126213.0Tempered lath martensite[25]
34CrNiMo6967103518.0Martensite, lower bainite[7]
HSLA89391415.3Lath bainite[24]
10CrNiMo83092519.0Tempered lath martensite[5]
Table 1  Mechanical properties for several high-strength steels
Fig.4  TEM images of high-strength steel (The dotted circle indicates triangular grain boundaries and the boxes highlight the position of precipitates)
(a) martensitic lath and nanoscale precipitate
(b) prior austenite grain boundary (PAGB) and nanoscale precipitate (c, d) bright (c) and dark (d) field TEM images of precipitates, respectively
Fig.5  TEM images, SAED pattern and EDS analyses of high-strength steel
(a) spherical precipitate (Inset is the SAED pattern of the carbide)
(b) short rod-shaped precipitate (c, d) EDS of precipitates denoted by cycles in Figs.5a (c) and b (d), respectively
Fig.6  TEM images of fatigue fracture specimens
(a, b) lath structure under the strain amplitude of 0.4% at low (a) and high (b) magnifications
(c) low dislocation density, precipitate, PAGB, lath under the strain amplitude of 1.0%
(d) crack propagation path indicated by arrows under the strain amplitude of 1.0%
Fig.7  Fatigue cracks initiated from the surface of specimens under the strain amplitudes of 0.4% (a), 0.6% (b), 0.8% (c) and 1.2% (d)
Fig.8  Main crack fracture morphology and secondary crack under strain amplitude of 1.0%
(a) whole view of fracture including crack initiation stage I, crack propagation stage II and stage III (b~d) locally magnified images indicated by boxes in Fig.8a, showing striation (b), secondary crack and striation (c) and dimple fracture (d)
Fig.9  Inclusions in the fractured specimens
(a) inclusion and EDS during stage II
(b) inclusion and striation during stage II
(c) tyre pattern and striation during stage II
(d) inclusion during stage III
Fig.10  Fatigue crack propagation morphology (a) and local magnifications (b, c) of high-strength steel at 1.0% strain amplitude (The inserted EDS indicates the composition of the inclusion, and arrows in Figs.10b and c show crack propagation directions)
[1] An T B, Tian Z L, Shan J G, et al. Effect of the temperature of post weld heat treatment on microstructure and performance of weld metal for 1000 MPa grade high strength steel [J]. J. Mech. Eng., 2015, 51(4): 40
(安同邦, 田志凌, 单际国等. 后热温度对1000 MPa级高强钢焊缝组织与性能的影响 [J]. 机械工程学报, 2015, 51(4): 40)
[2] Zhu B, Liu Z, Wang Y A, et al. Application of a model for quenching and partitioning in hot stamping of high-strength steel [J]. Metall. Mater. Trans., 2018, 49A: 1304
[3] Xie Z J, Fang Y P, Han G, et al. Structure-property relationship in a 960 MPa grade ultrahigh strength low carbon niobium-vanadium microalloyed steel: The significance of high frequency induction tempering [J]. Mater. Sci. Eng., 2014, A618: 112
[4] Fang J F, Xu Z L, Si S H, et al. Microstructure transformation characteristic of CGHAZ of Q1100 high-strength steel at different cooling rates [J]. Mater. Mech. Eng., 2017, 41(1): 107
(方俊飞, 徐震霖, 斯松华等. 不同冷速下Q1100高强钢焊接热影响区粗晶区的组织转变特征 [J]. 机械工程材料, 2017, 41(1): 107)
[5] Zhang Y J. Low cycle fatigue characteristic of 10CrNiMo high-strength steel [J]. J. Univ. Sci. Technol. Beijing, 2011, 33(1): 22
(张亚军. 10CrNiMo高强钢的低周疲劳特性 [J]. 北京科技大学学报, 2011, 33(1): 22)
[6] Sowards J W, Pfeif E A, Connolly M J, et al. Low-cycle fatigue behavior of fiber-laser welded, corrosion-resistant, high-strength low alloy sheet steel [J]. Mater. Des., 2017, 121: 393
[7] Branco R, Costa J D, Antunes F V. Low-cycle fatigue behaviour of 34CrNiMo6 high strength steel [J]. Theor. Appl. Fract. Mec., 2012, 58: 28
[8] Jiang Q M, Zhang X Q, Chen L Q, et al. SH-CCT Diagram, microstructures and properties of heat-affected zone in a 1000 MPa grade extra high-strength steel [J]. J. Iron Steel. Res., 2014, 26(1):47
(蒋庆梅, 张小强, 陈礼清等. 1000 MPa级超高强钢的SH-CCT曲线及其热影响区的组织和性能 [J]. 钢铁研究学报, 2014, 26(1):47)
[9] Pang J C, Li S X, Wang Z G, et al. General relation between tensile strength and fatigue strength of metallic materials [J]. Mater. Sci. Eng., 2013, A564: 331
[10] Wang X S, Liang F, Zeng Y P, et al. SEM in situ observations to the effects of inclusions on initiation and propagation of the low cyclic fatigue crack in super strength steel [J]. Acta Metall. Sin., 2005, 41: 1272
(王习术, 梁 锋, 曾燕屏等. 夹杂物对超高强度钢低周疲劳裂纹萌生及扩展影响的原位观测 [J]. 金属学报, 2005, 41: 1272)
[11] Li S X. Effects of inclusions on very high cycle fatigue properties of high strength steels [J]. Int. Mater. Rev., 2012, 57: 92
[12] Song S W, Lee J H, Lee H J, et al. Enhancing high-cycle fatigue properties of cold-drawn Fe-Mn-C TWIP steels [J]. Int. J. Fatigue, 2016, 85: 57
[13] Zhou H W, He Y Z, Zhang H, et al. Influence of dynamic strain aging pre-treatment on the low-cycle fatigue behavior of modified 9Cr-1Mo steel [J]. Int. J. Fatigue, 2013, 47: 83
[14] Ye D Y, Matsuoka S, Nagashima N, et al. The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel [J]. Mater. Sci. Eng., 2006, A415: 104
[15] Bai F M, Zhou H W, Liu X H, et al. Masing behavior and microstructural change of quenched and tempered high-strength steel under low cycle fatigue [J]. Acta. Metall. Sin. (Engl. Lett.), 2019, 32: 1346
[16] Chakraborti P C, Mitra M K. Room temperature low cycle fatigue behaviour of two high strength lamellar duplex ferrite-martensite (DFM) steels [J]. Int. J. Fatigue, 2005, 27: 511
[17] Verma P, Srinivas N C S, Singh S R, et al. Low cycle fatigue behavior of modified 9Cr-1Mo steel at room temperature [J]. Mater. Sci. Eng., 2016, A652: 30
[18] Chauhan A, Hoffmann J, Litvinov D, et al. High-temperature low-cycle fatigue behavior of a 9Cr-ODS steel: Part 1-Pure fatigue, microstructure evolution and damage characteristics [J]. Mater. Sci. Eng., 2017, A707: 207
[19] Chauhan A, Litvinov D, Aktaa J. Deformation and damage mechanisms of a bimodal 12Cr-ODS steel under high-temperature cyclic loading [J]. Int. J. Fatigue, 2016, 93: 1
[20] Marinelli M C, Alvarez-Armas I, Krupp U. Cyclic deformation mechanisms and microcracks behavior in high-strength bainitic steel [J]. Mater. Sci. Eng., 2017, A684: 254
[21] Kang J, Zhang F C, Long X Y, et al. Low cycle fatigue behavior in a medium-carbon carbide-free bainitic steel [J]. Mater. Sci. Eng., 2016, A66: 88
[22] François D, Pineau A, Zaoui A. Mechanical Behaviour of Materials: Volume II: Fracture Mechanics and Damage [M]. 2nd Ed., London: Springer Dordrecht Heidelberg, 2013: 340
[23] Glodež S, Knez M, Jezernik N, et al. Fatigue and fracture behaviour of high strength steel S1100Q [J]. Eng. Fail. Anal., 2009, 16: 2348
[24] Wang J G, Yang S L, Wang H Y, et al. Low-cycle fatigue properties of 800 MPa-grade ultrafine-grained steel [J]. J. Univ. Sci. Technol. Beijing, 2005, 27(1): 75
(王建国, 杨胜利, 王红缨等. 800 MPa级低合金高强度钢低周疲劳性能 [J]. 北京科技大学学报, 2005, 27(1): 75)
[25] Koh S K, Stephens R I. Mean stress effects on low cycle fatigue for a high strength steel [J]. Fatigue Fract. Eng. Mater. Struct., 1991, 14: 413
[26] Fang Y P, Xie Z J, Shang C J. Effect of induction tempering on carbide precipitation behavior and toughness of a 1000 MPa grade high strength low alloy steel [J]. Acta Metall. Sin., 2014, 50: 1413
(房玉佩, 谢振家, 尚成嘉. 感应回火对1000 MPa级高强度低合金钢碳化物析出行为及韧性的影响 [J]. 金属学报, 2014, 50: 1413)
[27] Zhou H W, He Y Z, Cui M, et al. Dependence of dynamic strain ageing on strain amplitudes during the low-cycle fatigue of TP347H austenitic stainless steel at 550 ℃ [J]. Int. J. Fatigue, 2013, 56: 1
[28] Kruml T, Polák J. Fatigue cracks in Eurofer 97 steel: Part I. Nucleation and small crack growth kinetics [J]. J Nucl. Mater., 2011, 412: 2
[29] Man J, Vystavěl T, Weidner A, et al. Study of cyclic strain localization and fatigue crack initiation using FIB technique [J]. Int. J. Fatigue, 2012, 39: 44
[30] Man J, Klapetek P, Man O, et al. Extrusions and intrusions in fatigued metals. Part 2. AFM and EBSD study of the early growth of extrusions and intrusions in 316L steel fatigued at room temperature [J]. Philos. Mag., 2009, 89: 1337
[31] Chan K S. Roles of microstructure in fatigue crack initiation [J]. Int. J. Fatigue, 2010, 32: 1428
[32] Pan Q S, Zhou H F, Lu Q H, et al. History-independent cyclic response of nanotwinned metals [J]. Nature, 2017, 551: 214
pmid: 29088707
[33] Koyama M, Zhang Z, Wang M M, et al. Bone-like crack resistance in hierarchical metastable nanolaminate steels [J]. Science, 2017, 355: 1055
pmid: 28280201
[34] Abareshi M, Emadoddin E. Effect of retained austenite characteristics on fatigue behavior and tensile properties of transformation induced plasticity steel [J]. Mater. Des., 2011, 32: 5099
[35] Gui X L, Zhang B X, Gao G H, et al. Fatigue behavior of bainite/martensite multiphase high strength steel treated by quenching-partitioning-tempering process [J]. Acta Metall. Sin., 2016, 52: 1036
(桂晓露, 张宝祥, 高古辉等. Q-P-T处理贝氏体/马氏体复相高强钢疲劳断裂特性研究 [J]. 金属学报, 2016, 52: 1036)
[36] Zhang Z, Hu Z F, Fan L K, et al. Low cycle fatigue behavior and cyclic softening of P92 ferritic-martensitic steel [J]. J. Iron Steel Res. Int., 2015, 22: 534
[37] Huang Z W, Yuan F H, Wang Z G, et al. Low cycle fatigue properties and fracture mechanisms of M38 nickel base superalloy at high temperature [J]. Acta Metall. Sin., 2007, 43: 1025
(黄志伟, 袁福河, 王中光等. M38镍基高温合金高温低周疲劳性能及断裂机制 [J]. 金属学报, 2007, 43: 1025)
[38] Wei D Y, Gu J L, Fang H S, et al. Fatigue behavior on a 1500 MPa grade bainite/martensite duplex-phase high strength steel [J]. Acta Metall. Sin., 2003, 39: 734
(韦东远, 顾家琳, 方鸿生等. 1500 MPa级贝氏体/马氏体复相高强钢的疲劳断裂特性 [J]. 金属学报, 2003, 39: 734)
[39] Hu D Y, Wang T, Ma Q H, et al. Effect of inclusions on low cycle fatigue lifetime in a powder metallurgy nickel-based superalloy FGH96 [J]. Int. J. Fatigue, 2019, 118: 237
[1] JIANG He, NAI Qiliang, XU Chao, ZHAO Xiao, YAO Zhihao, DONG Jianxin. Sensitive Temperature and Reason of Rapid Fatigue Crack Propagation in Nickel-Based Superalloy[J]. 金属学报, 2023, 59(9): 1190-1200.
[2] CHEN Runnong, LI Zhaodong, CAO Yanguang, ZHANG Qifu, LI Xiaogang. Initial Corrosion Behavior and Local Corrosion Origin of 9%Cr Alloy Steel in ClContaining Environment[J]. 金属学报, 2023, 59(7): 926-938.
[3] ZHANG Yuexin, WANG Jujin, YANG Wen, ZHANG Lifeng. Effect of Cooling Rate on the Evolution of Nonmetallic Inclusions in a Pipeline Steel[J]. 金属学报, 2023, 59(12): 1603-1612.
[4] ZHOU Hongwei, GAO Jianbing, SHEN Jiaming, ZHAO Wei, BAI Fengmei, HE Yizhu. Twin Boundary Evolution Under Low-Cycle Fatigue of C-HRA-5 Austenitic Heat-Resistant Steel at High Temperature[J]. 金属学报, 2022, 58(8): 1013-1023.
[5] SUN Yangting, LI Yiwei, WU Wenbo, JIANG Yiming, LI Jin. Effect of Inclusions on Pitting Corrosion of C70S6 Non-Quenched and Tempered Steel Doped with Ca and Mg[J]. 金属学报, 2022, 58(7): 895-904.
[6] LIU Jie, XU Le, SHI Chao, YANG Shaopeng, HE Xiaofei, WANG Maoqiu, SHI Jie. Effect of Rare Earth Ce on Sulfide Characteristics and Microstructure in Non-Quenched and Tempered Steel[J]. 金属学报, 2022, 58(3): 365-374.
[7] ZHU Miaoyong, DENG Zhiyin. Evolution and Control of Non-Metallic Inclusions in Steel During Secondary Refining Process[J]. 金属学报, 2022, 58(1): 28-44.
[8] TANG Haiyan, LIU Jinwen, WANG Kaimin, XIAO Hong, LI Aiwu, ZHANG Jiaquan. Progress and Perspective of Functioned Continuous Casting Tundish Through Heating and Temperature Control[J]. 金属学报, 2021, 57(10): 1229-1245.
[9] SUN Feilong, GENG Ke, YU Feng, LUO Haiwen. Relationship of Inclusions and Rolling Contact Fatigue Life for Ultra-Clean Bearing Steel[J]. 金属学报, 2020, 56(5): 693-703.
[10] ZHANG Zhefeng,SHAO Chenwei,WANG Bin,YANG Haokun,DONG Fuyuan,LIU Rui,ZHANG Zhenjun,ZHANG Peng. Tensile and Fatigue Properties and Deformation Mechanisms of Twinning-Induced Plasticity Steels[J]. 金属学报, 2020, 56(4): 476-486.
[11] ZHANG Xinfang, YAN Longge. Regulating the Non-Metallic Inclusions by Pulsed Electric Current in Molten Metal[J]. 金属学报, 2020, 56(3): 257-277.
[12] Tongbang AN,Jinshan WEI,Jiguo SHAN,Zhiling TIAN. Influence of Shielding Gas Composition on Microstructure Characteristics of 1000 MPa Grade Deposited Metals[J]. 金属学报, 2019, 55(5): 575-584.
[13] FENG Yefei,ZHOU Xiaoming,ZOU Jinwen,WANG Chaoyuan,TIAN Gaofeng,SONG Xiaojun,ZENG Weihu. Interface Reaction Mechanism Between SiO2 and Matrix and Its Effect on the Deformation Behavior of Inclusionsin Powder Metallurgy Superalloy[J]. 金属学报, 2019, 55(11): 1437-1447.
[14] ZHANG Xiaochen, MENG Weiying, ZOU Defang, ZHOU Peng, SHI Huaitao. Effect of Pre-Cyclic Stress on Fatigue Crack Propagation Behavior of Key Structural Al Alloy Materials Used in High Speed Trains[J]. 金属学报, 2019, 55(10): 1243-1250.
[15] Yu HUANG, Guoguang CHENG, You XIE. Modification Mechanism of Cerium on the Inclusions in Drill Steel[J]. 金属学报, 2018, 54(9): 1253-1261.
No Suggested Reading articles found!