CARBON DIFFUSION AND ITS EFFECT ON HIGH TEMPERATURE CREEP LIFE OF Cr5Mo/A302 DISSIMILAR WELDED JOINT |
JIANG Yong( ), ZHANG Zuo, GONG Jianming |
College of Mechanical and Power Engineering, Nanjing TECH University, Nanjing 211816 |
|
Cite this article:
JIANG Yong, ZHANG Zuo, GONG Jianming. CARBON DIFFUSION AND ITS EFFECT ON HIGH TEMPERATURE CREEP LIFE OF Cr5Mo/A302 DISSIMILAR WELDED JOINT. Acta Metall Sin, 2015, 51(4): 393-399.
|
Abstract Based on the consideration of economy and being easy to construct on site, Cr5Mo/A302 dissimilar welded joints are widely used in elevated temperature applications such as coal-fired power station, nuclear plant and petrochemical industry. Because of the difference in carbide forming elements on both sides of welded joint fusion line, carbon diffusion will happen in service progress and induce premature invalidation. The calculation methods of carbon diffusion and its harm to creep life of dissimilar welded joints have been investigated in the past decades. Theoretically, at a certain temperature, creep damage mechanism changes according to stress levels. However, the previous works paid little attention on the effect of carbon diffusion to creep life at different stress levels and few studies have been done focusing on relationships among carbon diffusion degree, stress level and creep life. In this work, carbon diffusion behavior of Cr5Mo/A302 dissimilar welded joint was first studied by employing aging treatment test, micro-hardness measurement and Fick's second law. Subsequently, creep tests were performed to investigate the effect of 200 mm wide decarburized zone on the joint creep life at different stress levels. The results showed that carbon diffusion in Cr5Mo/A302 dissimilar welded joints became serious with the increase of aging treatment time. The widths of carbon rich zone and decarburized zone were both consistent with the parabola distribution law and could be simulated by Fick's second law. The decarburised zone, which formed in the process of aging, reduced the creep life of the joint greatly at high stress levels. However, with the decline of testing load, its effect became much smaller. When the stress level dropped to about 36% of the yield stress, its effect was negligible. Meanwhile, the relationship of stress and carbon diffusion impact factor S was established to determine the critical value of the stress below which the decarburised zone would not affect the high-temperature creep life of the dissimilar joint.
|
|
|
Fund: Supported by National Natural Science Foundation of China (No.10172046) |
[1] |
Lundin C D. Weld J, 1982; 61: 58
|
[2] |
Bhaduri A K,Venkadesan S. Int J Pressure Vessel Piping, 1994; 58: 251
|
[3] |
Viswanathan R,Nutting J. Advanced Heat Resistant Steel for Power Generation. London: The University Press, Cambridge, 1999: 84
|
[4] |
Jiang Y,Gong J M,Tu S T. Pressure Vessel Technol, 2004; 21(7): 13
|
|
(姜 勇, 巩建鸣, 涂善东. 压力容器, 2004; 21(7): 13)
|
[5] |
Gong J M, Jiang Y, Tu S T. Acta Metall Sin (Engl Lett), 2004; 17: 560
|
[6] |
Murti K G K, Sunderesan S. Weld J, 1985; 64: 327
|
[7] |
Klueh R L, King J F. Weld J, 1980; 61: 302
|
[8] |
Lundin C D, Khan K K, Yang D. WRC Bull, 1995; 407: 1
|
[9] |
Hillert M,translated by Lai H Y,Liu G X. Alloy Diffusion and Thermodynamics. Beijing: Metallurgical Industry Press, 1984: 58
|
|
(Hillert M著,赖和怡,刘国勋 译. 合金扩散和热力学. 北京: 冶金工业出版社, 1984: 58)
|
[10] |
Li Y J, Zou Z D, Zhou B. Mater Sci Technol, 2001; 17: 338
|
[11] |
Huang M L, Wang L. Metall Mater Trans, 1998; 29A: 3037
|
[12] |
Huang M L, Wang L, Ya S J, Wang F G, Yu C Z. Acta Metall Sin, 2000; 36: 902
|
|
(黄明亮, 王 来, 亚生江, 王富岗, 于承志. 金属学报, 2000; 36: 902)
|
[13] |
Chen B L. Base of Metal Weldability. Beijing: China Machine Press, 1982: 106
|
|
(陈伯蠡. 金属焊接性基础. 北京: 机械工业出版社, 1982: 106)
|
[14] |
Pan C, Zhang Z. Mater Charact, 1994; 33: 87
|
[15] |
Pan C, Zhang Z. Mater Charact, 1996; 36: 5
|
[16] |
Pan C X. Dissimilar Metal Welding—Microstructure Characteristic and Transformation Mechanism. Beijing: China Communications Press, 2000: 55
|
|
(潘春旭. 异种金属焊接—显微结构特征及其转变机理. 北京: 人民交通出版社, 2000: 55)
|
[17] |
Li M S. Pressure Vessel Technol, 1998; 15(4): 11
|
|
(李萌盛. 压力容器, 1998; 15(4): 11)
|
[18] |
Fu J S, Wang Z N. J Ningxia Univ (Nat Sci), 2004; 25(2): 317
|
|
(付景山, 王治宁. 宁夏大学学报(自然科学版), 2004; 25(2): 317)
|
[19] |
Li D Y, Lou J X, Wang X Y, Zhang J, Xie T N. J Shenyang Univ Technol, 2012; 34(5): 491
|
|
(李德元, 娄建新, 王晓宇, 张 晶, 谢天男. 沈阳工业大学学报, 2012; 34(5): 491)
|
[20] |
Shi C Y, Xue J R, Yu Q Z, Li Q, Yu F, Guo Y. Trans China Weld Inst, 1999; 20(4): 258
|
|
(史春元, 薛继仁, 于启湛, 李 亓, 于 凤, 郭 勇. 焊接学报, 1999; 20(4): 258)
|
[21] |
Yang H J, Shi G, Zhang Y L, Lu W G, Cao S. Trans China Weld Inst, 2001; 22(4): 77
|
|
(杨厚君, 石 岗, 章应霖, 吕文广, 曹 晟. 焊接学报, 2001; 22(4): 77)
|
[22] |
Lundin C D, Khan K K. WRC Bull, 1995; 405: 62
|
[23] |
Ni R C, Zhu F W. Acta Metall Sin, 1978; 14: 97
|
|
(倪瑞澄, 朱逢吾. 金属学报, 1978; 14: 97)
|
[24] |
Parker J D,Parsons A W J. Int J Pressure Vessel Piping, 1995; 63: 45
|
[25] |
Parker J D. Int J Pressure Vessel Piping, 1995; 63: 55
|
[26] |
Tu S D. High Temperature Structural Integrity. Beijing: Science Press, 2003: 56
|
|
(涂善东. 高温结构完整性原理. 北京: 科学出版社, 2003: 56)
|
[27] |
Dobrzanski J. J Mater Process Technol, 2004; 157: 297
|
[28] |
Dobrzanski J, Zielinski A, Sroka M. J Achive Mater Manuf Eng, 2009; 32: 142
|
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|