INVESTIGATION OF PRECIPITATED PHASE IN LIQUID-PHASE-SINTERED W-Ni-Fe ALLOYS
LEI Bingqiang; ZHU Guisen (Central Iron and Steel Research Institute; Ministry of Metallurgical Industry; Beijing) (Manuscript received 3 July; 1985; revised manuscript 24 november; 1985)
Cite this article:
LEI Bingqiang; ZHU Guisen (Central Iron and Steel Research Institute; Ministry of Metallurgical Industry; Beijing) (Manuscript received 3 July; 1985; revised manuscript 24 november; 1985). INVESTIGATION OF PRECIPITATED PHASE IN LIQUID-PHASE-SINTERED W-Ni-Fe ALLOYS. Acta Metall Sin, 1987, 23(3): 182-187.
Abstract The microstructure of four liquid-phase-sintered W-Ni-Fe altoys with 90-95 wt-%W was investigated by means of optical and electron microscope and X-ray diffraction. It was found that there would be a precipitated phase formed in the 90W-Ni-Fe alloy in presence of a little carbon impurity and under the condition of slow-cooling after Iiquid-phase sintering. It was identified as a kind of A_6B_6C carbide of compiex face-centered cubic system with lattice constant of 1.0935 nm. Its morphology varies with the cooling speed and its empiric formula can be written as(Ni, Fe)_6W_6C approximateiy. After studying the heat treatment, the formation or elimination of this phase can be controlled.
1 Edmonds D V, Jones P N. Metall Trans, 1979; 10A: 289-295 2 Ariel E, Barta J, Brandon, D. Powder Metall Int, 1973; 5: 126-127 3 袁礼福,陈槐青,蒋民益,难熔金属文集,第四届难熔金属学术交流会,第四届难熔金属会议文集编辑组编,1983:52-55 4 Kang T K, Henig E-Th, Kaysser W A et al. In: Hausner H H et al. Eds., Modern Developments in Powder Metallurgy Vol. 14, Sponsored by the Metal Powder Industries Federation and American Powder Metallurgy Institute, Princeton: MPIF, 1981: 189-203 5 夏元洛,葛昌杶,钢铁研究总院学报,1984;4(1) :34-43 6 Muddle B C, Edmonds D V. Met Sci, 1983; 17(5) : 209-218 7 冶金部金属研究所.难熔金属文集,1976年,第三分册,上海科技情报所编,29-54 8 雷秉强,朱桂森,硕士学位论文,北京钢铁研究总院,1985年