Acta Metall Sin  1989, Vol. 25 Issue (2): 116-120    DOI:

Current Issue | Archive | Adv Search |

PHASE DIAGRAM OF Nd-Fe-B TERNARY SYSTEM I. ISOTHERMAL SECTION AT ROOM TEMPERATURE

ZHANG Ning;LUO Yang Central Iron and Steel Research Institute; Ministry of Metallurgical Industry Beijing

ZHANG Ning;LUO Yang Central Iron and Steel Research Institute; Ministry of Metallurgical Industry Beijing. PHASE DIAGRAM OF Nd-Fe-B TERNARY SYSTEM I. ISOTHERMAL SECTION AT ROOM TEMPERATURE. Acta Metall Sin, 1989, 25(2): 116-120.

Abstract References Related Articles Recommended Metrics Download:  PDF(1309KB)  Export:  BibTeX | EndNote (RIS)       Abstract  The microstructures of both as-cast and annealed Nd-Fe-B alloys havebeen studied. The stable phase regions existing in Nd-Fe-B ternary system at room-temperature have been established by the microzone composition analysis and thephase identification. Based on the obtained results, an isothermal section of Nd-Fe-Bternary system at room-temperature was drawn. Key words:  phase diagram      Nd-Fe-B isothermal section      Received:  18 February 1989      Service E-mail this article Add to citation manager E-mail Alert RSS （） Articles by authors URL:  https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1989/V25/I2/116 1 Chaban N F, Kuzma YU B, Bilonizhko N S, Kachmar O O, Petrov N V. Dopov Akad Nauk Ukr RSR, Ser. A, 1979; (10) : 873 2 Herbst J F, Croat J J. Pinkerton F E, Yelon W B. Phys Rev, B, 1984; 29: 4176 3 Rezinge A, Brawn H F, Muller J. Yvon K. Solid State Commun, 1985; 55: 131 4 Stadelmaier H H, El-Masry N A. In: Strnat K J ed, Proc 4th Int Symp on Magn. Anisotropy and Coerivity in Rare Eare-Transition Metal Alloys, Dayton. OH, 1985: 613 5 Matsuura Y, Hirosawa S, Yamamoto H, Fujimura S, Sagawa M, Osamura K. Jpn J Appl Phys, 1985; 24 (8) : L635 6 Chin T S, Tsai D S, Chang Y H, Hsu S E, Hung M P. In: Strnat K J ed, Proc 9th Int Workshop on Rare-Earth Magnets, Bad Soden, FRG, Sept. 1987: 403 7 Sohneider G, Henig E T, Stadelmaier H H, Petzow G. In: Strnat K J ed, Proc 9th Int Workshop on Rare-Earth Magnets, Bad Soden, FRG, Sept. 1987: 347 8 Moffatt W G. The Handbook of Binary Phase Diagrams, General Electric Company, USA, 1978 9 Kubaschewski O. Iron-Binary Phase Diagrams, Berlin: Springer-Verlag, 1982: 15 10 #12 11 Cannon J F. Robertson D L. Hall H T. Mater Res Bull, 1972; 7: 5 12 Schneider G, Henig E T, Petzow G, Stadelmaier H H. Z Metallk, 1986; 77: 755 [1] GAO Xiang, ZHANG Guikai, XIANG Xin, LUO Lizhu, WANG Xiaolin. Effects of Alloying Elements on the Adsorption of Oxygen on V(110) Surfaces: A First-Principles Study[J]. 金属学报, 2020, 56(6): 919-928. [2] ZHANG Weibin SHA Chunsheng DU Yong WEN Guanghua XIE Wen WANG Shequan. COMPUTER SIMULATIONS AND VERIFICATION OF GRADIENT ZONE FORMATION IN CEMENTED CARBIDES[J]. 金属学报, 2011, 47(10): 1307-1314. [3] ZHANG Huawei; LI Yanxiang; LIU Yuan. Study of Metal--Hydrogen Binary Phase Diagram in Gasar Process[J]. 金属学报, 2005, 41(1): 55-. [4] ZHANG Jian(Metallurgical Engineering School; University of Science and Technology Beijing; Beijing 100083). CONSISTENCY(OR SIMILARITY) OF THERMODYNAMIC PROPERTIES OF METALLURGICAL MELTS WITH THEIR PHASE DIAGRAMS[J]. 金属学报, 1998, 34(7): 742-752. [5] Zhang Jian (Institute of Metallurgy; University of Science and Technology Beijing; Beijing 100083). CLASSIFICATION OF THERMODYNAMIC PROPERTIES OF BINARY METALLIC MELTS ACCORDING TO THEIR PHASE DIAGRAMS[J]. 金属学报, 1998, 34(1): 75-85. [6] ZHOU Hong; WANG Jinguo; JIA Shusheng (Jilin University of Technology; Chanerhun 130025) OGIKeisaku(Kyushu Universily; Japan) (Manuscript received 1996-03-22; in revised form 1997-04- 13). SOLIDIFIED MICROSTRUCTURES AND PHASES OF HIGH SPEED STEELS CONTA1NING DIFFERENT V AND C CONTENT[J]. 金属学报, 1997, 33(8): 838-843. [7] FANG Jianhui; TANG Yun; LI Yu; YAN Licheng; CHEN Nianyi (Shanghai University;Shanghai 201800); WANG Jiyang (Shandong University; Jinan 250012)(Manuscript received 1996-04-08; in revised form 1996-09-10). KPO_3-M0O_3 PHASE DIAGRAM[J]. 金属学报, 1997, 33(4): 395-397. [8] ZHOU Guozhi(Kuo-Chih Chou) (University of Science and Technology Beijing;Beiing 100083). NEW GENERATION SOLUTION GEOMETRICAL MODEL AND ITS FURTHER DEVELOPMENT[J]. 金属学报, 1997, 33(2): 126-132. [9] DING Jinjun;ZHAO Gang;HAO Shiming (Northeastern University; Shenyang 110006). PHASE EQUILIBRIUM RELATIONSHIPS AND INTERDIFFUSION COEFFICIENTS OF β,α ANDγIN THE Ti-Al BINARY SYSTEM[J]. 金属学报, 1997, 33(10): 1105-1109. [10] YUAN Wenxia; MA Shulan; QIAO Hin; ZHUANG Weidong; XING Xianran;QIAO Zhiyu (University of Science and Technology Beijing; Beijing 100083)(General Institute for Non-Ferrous Metals; Beijing 100088)(Manuscript received 1995-04-28; in revised form 1995-11-05). A STUDY ON THE YCl_3-AECl_2(AE=Mg, Ca, Sr, Ba)BINARY PHASE DIAGRAMS[J]. 金属学报, 1996, 32(2): 139-143. [11] HAO Shiming; ZENG Ninghua (Northeastern University; Shenyang 110006)(Manuscript received 1994-11-16). ISOTHERMAL SECTION OF PHASE DIAGRAM IN Ti-Al-Cr TERNARY SYSTEM AT 1000℃[J]. 金属学报, 1995, 31(16): 152-158. [12] YAN Licheng;FANG Jianhui;XU Jingyan;YANG Jinxiu(Shanghai University of Science and Technology). PHASE DIAGRAM OF KF-LiCl-CaCl_2 SYSTEM[J]. 金属学报, 1994, 30(19): 301-303. [13] WAN Jinglong(Anhui Institute of Technology; Hefei); BI Qinghua(Shanghai University of Science and Technology). Gd-CoAl VERTICAL SECTION OF Gd-Co-Al PHASE DIAGRAM[J]. 金属学报, 1994, 30(17): 204-207. [14] XU Qian;YU Yaxin;QIU Zhuxian(Northeastern University;Shenyang)(Manuscript received 25 June;1993). THERMODYNAMIC PROPERTIES AND PHASE DIAGRAMS OF Li-CaF_2,NaF-CaF_2 AND KF-CaF_2[J]. 金属学报, 1994, 30(16): 150-155. [15] SHEN Jianyun(General Research Institute for Non-Ferrous Metals;Beijing);CHATILLON C(Laboratoire de Thermodynamique et Physico-chimie Metallurgiques;Fracne)(Manuscript received 16 June;1993). THERMODYNAMICS OF Ga-In-As SYSTEM UNDER LATTICE DEFORMATION[J]. 金属学报, 1994, 30(16): 145-149. No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed