HYDROGEN DAMAGE IN HIGH PURITY IRON

WU Yichu;CHANG Xiangrong;TIAN Zhongzhuo;XIAO Jimei University of Science and Technology Beijing

Cite this article:

WU Yichu;CHANG Xiangrong;TIAN Zhongzhuo;XIAO Jimei University of Science and Technology Beijing. HYDROGEN DAMAGE IN HIGH PURITY IRON. Acta Metall Sin, 1992, 28(2): 43-46.

Download:

PDF(588KB)
Export: BibTeX | EndNote (RIS)

Abstract Hydrogen damage in Fe of 99.99% purity has been investigated by Doppler broadening measurement. Experimental results show that when the iron is charged with hydrogen in 0.5 mol / L H_2SO_4 so-lution, the critical current density to cause hydrogen damage is 20 mA / cm~2. While a little As_2O_3, saying 250 mg / L, added to H_2SO_4 solution, even rather small current density, <0.2 mA / cm~2, would cause hydrogen damage. With the help of slow tensile test, it revealed that the hydrogen damage occurred in the specimen may be influential to the subsequent process of deformation and fracture.

Key words: hydrogen damage critical current density positron annihilation technique hydrogen-induced defect

Received: 18 February 1992

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y1992/V28/I2/43

1 Hirth J P. Metall Trans, 1980; 11A: 861
2 羽木秀树,林安德,大谷南海男.日本金属学会志,1978;42:124
3 West R N. In: Hautojarvi P ed., Positrons in solids, Berlin: Springer-Verlag, 1979: 89
4 Alam A. J Phys F: Met Phys, 1981; 11(10) : L259
5 Nieminen R M, Laakkonen J, Hautojarvi P, Vehanen A. Phys Rev, 1979; 19B: 1397
6 Pressouyre G M, Bernstein I M. Metall Trans, 1981; 12A: 835
7 Tian Zhongzhuo, Chang Xiangrong, Lu Rongbang, Hsiao Chimei (Xiao Jimei), Xue Jiayu, Ji Guokun. Scr Metall, 1982; 16: 1383
8 王燕斌.北京科技大学博士学位论文,1985v

[1]	AN Xudong, ZHU Te, WANG Qianqian, SONG Yamin, LIU Jinyang, ZHANG Peng, ZHANG Zhaokuan, WAN Mingpan, CAO Xingzhong. Interaction Mechanism of Dislocation and Hydrogen in Austenitic 316 Stainless Steel[J]. 金属学报, 2021, 57(7): 913-920.
[2]	YU Guanghua; CHENG Yihuan; CHEN Hongxing; NIU Xuejun; QIAO Lijie; CHU Wuyang (University of Science and Technology Beijing; Beijing 100083)(Baoshan Corporation of Iron and Steel; Shanghai 201900). HYDROGEN-INDUCED FAILURE OF OIL-WELL TUBULAR STEEL C90[J]. 金属学报, 1996, 32(6): 617-623.
[3]	QIU Zliuxian;YAO Guangchun;YU Yaxin;ZHANG Zhonglin(Northeastern University; Shenyang). WETTABILITY AND CRITICAL CURRENT DENSITY OF LITHIUM SALT-CONTAINING CARBON ANODE[J]. 金属学报, 1994, 30(22): 439-443.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed