ISOTHERMAL SECTION AT 1000 AND 1100℃ OF Fe-Mn-AI SYSTEM PHASE DIAGRAM
LIU Xingjun; HAO Shiming; SUN Rongyao; (Northeast University of Technology; Shenyang)
Cite this article: 

LIU Xingjun; HAO Shiming; SUN Rongyao; (Northeast University of Technology; Shenyang). ISOTHERMAL SECTION AT 1000 AND 1100℃ OF Fe-Mn-AI SYSTEM PHASE DIAGRAM. Acta Metall Sin, 1992, 28(7): 50-54.

Download:  PDF(949KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Phase equilibria at Fe-Mn side of isothermal section at 1000 and 1100℃ in Fe-Mn-Al system have been determined using the diffusion couple, technique and metallography. A three-phase, α+γ+β, region was found at 1000℃. The method of solid/gas diffusion couple used to determine equilibrium phase composition is believed to be feasible for the system containing volatile component.
Key words:  Fe-Mn-Al system      phase equilibrium      diffusion couple     
Received:  18 July 1992     

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1992/V28/I7/50

1 Banerji S. Adv Met Prog, 1987; 4: 59
2 Charles J, Berghezan A, Lutts A, Dancoisne P L. Met Prog, 1981; 119(6) : 71
3 张彦生.金属学报,1986;22:A470
4 Schmatz D J. Trans AIME, 1959; 215: 112
5 Chakrabarti D J. Metall Trans, 1977; 8B: 121
6 郝士明,刘兴军.中国物理学会第五届全国相图会议文集,武汉,1988)
[1] Chengsong LIU,Fei YE. Mechanism on Modification of MnO-SiO2-Type Oxide by Interfacial Solid-State Reaction During Heat Treatment[J]. 金属学报, 2017, 53(1): 10-18.
[2] Yu GONG, Yongchong CHEN, Dandan LIU, Yanping ZHANG, Csaba CSERHáTI, Attila CSIK. INVESTIGATION OF PERIODIC-LAYERED STRUCTURE DURING SOLID STATE REACTIONS OF Zn/CuxTiy SYSTEMS[J]. 金属学报, 2016, 52(3): 349-354.
[3] WU Changjun, ZHU Chenlu, SU Xuping, LIU Ya, PENG Haoping, WANG Jianhua. THERMODYNAMICAL AND KINETIC INVESTIGA-TION OF FORMATION OF PERIODIC LAYERED STRUCTURE IN TiCu/Zn INTERFACE REACTION[J]. 金属学报, 2014, 50(8): 930-936.
[4] LI Hongxiao REN Yuping MA Qianqian JIANG Min QIN Gaowu. PHASE EQUILIBRIUM IN THE LOW-Ca SIDE OF Mg-Zn-Ca SYSTEM AT 400 ℃[J]. 金属学报, 2012, 48(1): 70-75.
[5] LI Hongxiao MA Qianqian REN Yuping JIANG Min QIN Gaowu. TERNARY COMPOUNDS AND RELATIVE PHASE EQUILIBRIA IN THE Mg-RICH SIDE OF THE Mg-Zn-Ca SYSTEM[J]. 金属学报, 2011, 47(4): 385-390.
[6] XIE Yu ZHANG Yan CHEN Rongshi HAN Enhou. RELATIONSHIP OF COMPOSITIONS, PHASE CONSTITUENTS AND SOLIDIFICATION PATHS OF CASTING Mg-Al-Zn ALLOYS[J]. 金属学报, 2009, 45(11): 1396-1401.
[7] ;. Research on the ternary compound T1 with low Nd content in the Mg-Zn-Nd alloys[J]. 金属学报, 2008, 44(4): 385-390 .
[8] . Diffusion-induced Stresses[J]. 金属学报, 2006, 42(3): 225-233 .
[9] FU Xiaoliang; LI Changrong; LI Mei; ZHANG Weijing. Determination of the Phase Equilibrium of the Ag-Ti Binary System at 980, 1100 and 1200℃[J]. 金属学报, 2005, 41(7): 691-694 .
[10] LI Juntao; HAO Shiming; WAN Qingfeng (Department of Materials Science and Engineering; Northeastern University; Shenyang 110006)Correspondent: HAO Shiming; professor; Tel: (024)23893000-7737; E-mail: smhao@mail. neu. eds. cn. STUDY ON α/γ PHASE EQUILIBRIUM IN Ti-Al-Cr-Fe QUARTERNARY SYSTEM[J]. 金属学报, 1998, 34(9): 897-902.
[11] DING Jinjun;ZHAO Gang;HAO Shiming (Department of Materials Science and Engineering; School of Materials and Metallurgy; Northeastern University;Shenyang 110006). PHASE EQUILIBRIUM RELATIONSHIPS OF α_2(α)/γ IN THE Ti-Al-Cr TERNARY SYSTEM[J]. 金属学报, 1998, 34(2): 171-175.
[12] LI Juntao; HAO Shiming (Northeastern University; Shenyang 110006). ^^α(α_2)/ PHASE EQUILIBRIA IN Ti-Al-Si SYSTEM[J]. 金属学报, 1996, 32(11): 1171-1176.
[13] QIN Gaowu;HAO Shiming;ZENG Ninghua (Northeastern University;Shenyang 110006)(Manuscript received 1994-11-04;in revised form 1995-05-04). α(α_2)/γ PHASE EQUILIBRIA IN Ti-Al-Ga AND Ti-Al-Nb-Cr SYSTEMS[J]. 金属学报, 1995, 31(23): 484-488.
[14] HAO Shiming; JIANG Min (Northeast University of Technology; Shenyang). TWO-PHASE EQUILIBRIUM CALCULATION BY THE GRAND POTENTIAL METHOD FOR BINARY ALLOYS[J]. 金属学报, 1992, 28(11): 54-58.
[15] QIU Cai'an;JIN Zhanpeng;HUANG Peiyun Central South University of Technology; Changsha. ISOTHERMAL SECTION OF THE W-Ni-Cu SYSTEM AT 1017℃[J]. 金属学报, 1988, 24(5): 403-406.
No Suggested Reading articles found!