Acta Metall Sin  1995, Vol. 31 Issue (7): 315-319    DOI:

Current Issue | Archive | Adv Search |

^MICROSTRUCTURE AND MECHANICAL PROPERTIES OF BORON-MODIFIED HAI 77-2 BRASS

WANG Jihui;JIANG Hiaoxia;LI Shizhuo(Institute of Metal Research;Chinese Academy of Sciences.Shenyang 110015)(Manuscript received 1994-12-20)

WANG Jihui;JIANG Hiaoxia;LI Shizhuo(Institute of Metal Research;Chinese Academy of Sciences.Shenyang 110015)(Manuscript received 1994-12-20). ^MICROSTRUCTURE AND MECHANICAL PROPERTIES OF BORON-MODIFIED HAI 77-2 BRASS. Acta Metall Sin, 1995, 31(7): 315-319.

Abstract References Related Articles Recommended Metrics Download:  PDF(410KB)  Export:  BibTeX | EndNote (RIS)       Abstract  The microstructure and mechanical properties of boron-modified HAl 77-2brass were investigated by XRD,SEM and tension test.The results show that with the increase of boron added to aluminium brass,the grain size of HAl 77-2 brass with and without arsenic decreases,the strength and hardness of boron-modified brass increase.On the basis of experimental results,the optimum amount of boron in HAl 77-2 brass was found.Correspondent:JIANG Hiaoxia,professor,(Institute of Metal Research,Chinese Academy of Sciences,Shen yang 110015) Key words:  boron      brass      microstructure.mechanical property      Received:  18 July 1995      Service E-mail this article Add to citation manager E-mail Alert RSS Collect articles（） Articles by authors URL:  https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1995/V31/I7/315 1青木清,和泉修．日本金属学会志,1979;43:11902郭建亭,孙超,谭明晖,赖万慧．金属学报,1990;26:A203 孙 理,姜晓霞．中国腐蚀与防护学报,1990;10:3714 周业蓉．腐蚀科学与防护技术1989;创刊号:285 窦照英,材料保护,1980;13(6):166 LangeneggerEE、Ronbison,FP．Corrosion,1969;25(3):1377 邱万川,汪的华,邹津耘．全国第五届正电子湮没谱学会议论文集,1993:84 [1] Kejian LI,Zhipeng CAI,Yao WU,Jiluan PAN. Research on Austenite Transformation of FB2 Heat-Resistant Steel During Welding Heating Process[J]. 金属学报, 2017, 53(7): 778-788. [2] XUE Yingyu, TANG Jiancheng, ZHUO Haiou, YE Nan, WU Tong, ZHOU Xusheng. MICROSTRUCTURES AND PROPERTIES OF LEAD-FREE FREE-CUTTING GRAPHITE-BRASS PREPARED BY GRAPHITIZATION OF CEMENTITE[J]. 金属学报, 2015, 51(2): 223-229. [3] MO Yongda, JIANG Yanbin, LIU Xinhua, XIE Jianxin. MECHANICAL PROPERTIES AND WORK HARDENING BEHAVIOR OF COLUMNAR-GRAINED HAl77-2 BRASS[J]. 金属学报, 2014, 50(11): 1367-1376. [4] KANG Mokuang ZHANG Mingxing LIU Feng ZHU Ming. OVERALL ACTIVATION ENERGY OF ISOTHERMAL TRANSFORMATION IN METAL ALLOY AND ITS MECHANISM II. Isothermal Transformation in β Brasses[J]. 金属学报, 2009, 45(1): 32-36. [5] ;. Effect of Solidification Condition on Structure and Properties of High Boron Iron-Base Alloy[J]. 金属学报, 2007, 43(5): 477-481 . [6] . Effect of boron on the microstructure and mechanical properties of as-cast TiAl alloy[J]. 金属学报, 2007, 43(5): 487-492 . [7] QIU Shengtao; XIAO Lijun; LIU Jiaqi; GAN Yong. Softening Mechanism of Boron—Bearing Low--Carbon Hot Strips Produced by TSCR Route[J]. 金属学报, 2006, 42(11): 1202-1206 . [8] TANG Bei; LIU Yongli; ZHENG Hong; LI Feng; CONG Hongtao; CHENG Huiming. MICROSCOPIC CHARACTERIZATION AND HRTEM IMAGES OF BORON NITRIDE NANOTUBES[J]. 金属学报, 2005, 41(9): 905-909 . [9] CHEN Guosheng; JIN Xin; ZHOU Dianhua; WANG Shipu; XIE Wei; WANG Lintao. Effects of Boron Content on Boundaries Precipitates in Ni Base Alloy GH4049 and Its High Temperature Properties[J]. 金属学报, 2005, 41(6): 622-626 . [10] LI Fan; ZHANG Dengjun; LI Baohou; LUO Shimin. Chemical Plating Nickel on the Surface of Hexagonal Boron Nitride Micro-Particles and Its Kinetic Model[J]. 金属学报, 2004, 40(2): 173-178 . [11] WANG Yu; LIN Dongliang(T. L. Lin)(Department of Materials Science; the Open Laboratory of Education Ministry for High-Temperature Materials and Test; Shanghai Jiao Tong University; Shanghai 200030)ZHOU Yuanxin; XIA Yuanming (Department of Morden Dynamics; University of Science and Technology of China; Hefei 230026)C. C. Law (Materials and Mechanics Engineering; United Technologies Company-Pratt & Whittney 400 Main Street; East Hartford; CT 06108; U. S. A.)Correspondent: LIN Dongliang; professon Tel: (021)62812544(O); (021)62835352(H);Fax: (021)62820892; E-mail: dllin@ mail. sjtu. edu. cn.. THE EFFECT OF MINOR BORON ADDITION ON DYNAMIC TENSILE PROPERTIES OF WROUGHT Ti-47Al-2Mn-2Nb ALLOY[J]. 金属学报, 1998, 34(9): 915-918. [12] WU Zhengan; GU Mingyuan; CHEN Yu; ZHANG Gooding (The State Key Laboratory of MMCs; Shanghai Jiaotong University; Shanghai 200030). THE INTERFACE MICROSTRUCTURE OF A B_4C_p +SiC_w/MB15 MAGNESIUM BASED COMPOSITE[J]. 金属学报, 1998, 34(4): 443-448. [13] LI Zhiqiang;REN Dagang;LI Douxing; GUO Jianting (Laboratory of Atom Imaging of Solids; Institute of Metal Research; The Chinese Academy of Sciences;Shenyang 110015). MICROSTRVCTURAL STUDY OF INTERMETALLIC COMPOUND Ni_3Al BY AP-FIM[J]. 金属学报, 1998, 34(3): 249-254. [14] SUI Zhitong;ZHANG Peixin(Northeastern University; Shenyang 110006). SELECTIVE PRECIPITATING BEHAVIOR OF THE BORON COMPONENTS FROM THE BORON SLAGS[J]. 金属学报, 1997, 33(9): 943-951. [15] ZHANG Tiancheng; CHU Wuyana (University of Science and Technology Beijing;Beijing 100083)SHI Xunqing; ZHU Wanxu; LIU Baochen (Tsinghua University;Bejing 100084). DISSOLUTION FACILITATING LOCAL PLASTIC DEFORMATION FOR BRASS IN AMMONIA SOLUTION[J]. 金属学报, 1997, 33(3): 309-314. No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed