A NiCr--Based High Temperature Self Lubricating Coating PM304 Prepared by Powder Metallurgy
DING Chunhua1); WANG Yaping2);ZHOU Jing'en1)
1) State Key Laboratory for Mechanical Behavior of Materials; Xi'an Jiaotong University; Xi'an 710049
Cite this article: 

DING Chunhua; WANG Yaping; ZHOU Jing'en. A NiCr--Based High Temperature Self Lubricating Coating PM304 Prepared by Powder Metallurgy. Acta Metall Sin, 2006, 42(11): 1212-1216 .

Download:  PDF(871KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  PM304 composite comprised of NiCr (80/20) matrix (60 wt%) combined with Cr2O3 (20 wt%), Ag (10 wt%) and eutectic BaF2/CaF2 (10 wt%) as solid self-lubricants additives has been prepared by high-energy ball milling and powder metallurgy. Experimental results showed that the sintering temperature had great influence on relative density and tensile strength of the PM304 composite. The relative density and tensile strength of PM304 increased rapidly with the increase of sintering temperature from 800°C to 1100°C. The size of Cr2O3 and BaF2/CaF2 of PM304 composite sintered at 1100°C was less than 1 μm, and that of Ag particles was below 5 μm, the relative density was 94%, and the mean tensile strength 47 MPa, 33% greater than that of PS304.
Key words:  PM304      self lubricating      NiCr alloy      
Received:  17 April 2006     
ZTFLH:  TF123  

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y2006/V42/I11/1212

[1] Dellacorte C, Edmonds B J. NASA TM-107056, 1995
[2] Dellacorte C, Laskowski J A. NASA TM-107163, 1996
[3] Dellacorte C, Tribol Trans, 2003; 46: 361
[4] Dellacorte C, Edmonds B J. Tribol Trans, 2002; 45: 499
[5] Stanford M K, Eylon D. Ceram Eng Sci Proc, 2003; 24: 577
[6] Wang W C. Surf Coat Technol, 2004; 177: 12
[7] Li J F, Ding C X. Wear, 2000; 240: 180
[8] Radii K C, Dellacorte C. Tribol Trans, 2002; 45: 199
[9] Matejicek J, Sampath S. Ada Mater, 2003; 51: 863
[10] Fernandez J E, Rodriguez R, Wang Y. Wear, 1995; 181-183: 417
[11] He J. Nanostruct Mater, 1999; 10: 1271
[12] Gleiter H. Acta Mater, 2001; 48: 1
[13] DellaCorte C, Lukaszewicz V, Valco M J, Radii K C, Heshmat H. NASA; TM-209187, 2000
[15] Meredith B, Milner D R. Powder Metall, 1976, 19: 38
[16] Engel U, Hubner H. J Mater Sci, 1978; 13: 2003
[17] Dellacorte C. NASA TM-208660, 1998T
[1] XIN Li; LI Tiefan; LI Meishuan; JIN Huiming; SHI Changxu (State Key Laboratory for Corrosion and Protection; Institute ofCorrosion and Protection of Metals; Chinese Academy ofSciences; Shenyang 110015) (Manuscript received 1996- l0-24; in revised form 1997-01 -09). INFLUENCES OF Y~+-IMPLANATION ON INTERFACIAL DEFECTS AND SPALLING MECHANISM OF Cr_2O_3 SCALE FORMED ON Ni30Cr DIRECT1ONAL SOLIDIFICATION ALLOY[J]. 金属学报, 1997, 33(8): 851-862.
No Suggested Reading articles found!