Three--Dimensional Figure of Normal Stress and Shear Stress at One Point and Its Application in Analyzing Metal Forming Process

HE Zhubin; WANG Zhongren; YUAN Shijian

School of Materials Science and Engineering; Harbin Institute of Technology

HE Zhubin; WANG Zhongren; YUAN Shijian. Three--Dimensional Figure of Normal Stress and Shear Stress at One Point and Its Application in Analyzing Metal Forming Process. Acta Metall Sin, 2004, 40(3): 319-325 .

Abstract References Related Articles Recommended Metrics Download:  PDF(16785KB)  Export:  BibTeX | EndNote (RIS)       Abstract  A three--dimensional figure of normal stress and shear stress of one stress state was given, and the corresponding relationship of the figure with deformation type was analyzed.The figures can be divided into three main types, which refer to compression, plain strain, and tension, respectively. In addition, the stress--strain of typical points in simple tension, drawing, and extrusion was successfully analyzed by the figures. Key words:  normal stress      shear stress      Lode parameter       Received:  03 March 2003      ZTFLH:  TB12   Service E-mail this article Add to citation manager E-mail Alert RSS （） Articles by authors HE Zhubin WANG Zhongren YUAN Shijian URL:  https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y2004/V40/I3/319 [1] Hagen H, Ebert A, van Lengen R H, Scheuermann G. International Conference on Informatics-10 Years Back, 10 Years Ahead, Dagstuhl, Germany, 2000 [2] Wang Z R, Dai K. Acta Metall Sin, 2000; 36:46(王仲仁,戴昆.金属学报,2000;36:46) [3] Kun Dai, Wang Z R. J Mater Proc Technol, 2000; 102:174 [4] Wang Z R. Fundamental of Plastic Working Mechanics. Beijing: National Defence Industry Press, 1989:127(王仲仁.塑性加工力学基础.北京:国防工业出版社,1989:127)U [1] LIU Jiangtao;WANG Zhongguang;SHANG Jianku. DEFORMATION BEHAVIORS OF [110] AND [112]　ORIENTED β-Sn SINGLE CRYSTALS[J]. 金属学报, 2008, 44(12): 1409-1414. [2] WU Donghai;HU Gengxiang (Department of Materials Science; Shanghai Jiaotong University; Shanghai 200030)INUI Haruyuki; YAMAGUCHI Masaharu (Kyoto University; Kyoto 606-01; Japan). DEFORMATION BEHAVIOR OF γ-TiAl SINGLE CRYSTALS AT DIFFERENT TEMPERATURES[J]. 金属学报, 1998, 34(1): 39-44. [3] YUE Zhufeng;ZHENG Changqing(Northwestern Polytechnical University;Xi'an)(Manuscript received 2 April;1993;in revised form 24 September;1993). MICRO-MECHANICAL ANALYSIS OF THERMAL MISFIT OF SINGLE CRYSTAL Ni-BASE SUPERALLOY[J]. 金属学报, 1994, 30(3): 124-132. No Suggested Reading articles found! Viewed Full text Abstract Cited   Shared      Discussed