CYCLIC DEFORMATION OF COARSE GRAINED POLYCRYSTALLINE PURE Al Ⅰ. SLIP CHARACTERISTICS
XIA Yuebo;WANG Zhongguang State Key Laboratory for Fatigue and Failure of Materials; Institute of Metal Research; Academia Sinica; Shenyang
Cite this article: 

XIA Yuebo;WANG Zhongguang State Key Laboratory for Fatigue and Failure of Materials; Institute of Metal Research; Academia Sinica; Shenyang. CYCLIC DEFORMATION OF COARSE GRAINED POLYCRYSTALLINE PURE Al Ⅰ. SLIP CHARACTERISTICS. Acta Metall Sin, 1992, 28(2): 3-8.

Download:  PDF(2250KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  

Comparing with ordinary ploycrystalline materials sized to μm grade, the slip morphology of the coarse grained polycrystalline pure Al is characterized by: (1) several slip domains occur in a grain, and in same domain, several slip systems operate at same time or one after another intensely, a beautiful and neat slip pattern is forming on the specimen surface; (2)for high-∑value coincident and random grain boundaries , the grain boundary affecting zone (GBAZ), about 50--120 μm wide, is favourable site to form intergranular crack at early fatigue life easily, and migration or slide of the boundaries were often observed. While low ∑--value near-coincident grain boundaries show a higher degree of slip continuity and strain compatibili-ty than high ∑--value ones. Intergranular crack is not easily nucleated at low ∑--value near--coincident boundaries; and (3) due to suppression of grain boundary slip at triple grain boundary node, the high ∑--value and random grain boundary among the three boundaries of tricrystal crack easily during cyclic deformation.

Key words:  coincident grain boundary      random grain boundary      intergranular crack      boundary slide      serrated grain boundary     
Received:  18 February 1992     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1992/V28/I2/3

1 Lim L C, Raj R. Acta Metall, 1985; 33: 2205
2 Lim L C, Raj R. Acta Metall, 1984; 32: 1177
3 Okada T, Onaka S, Hashimoto S, Miura S. Scr Metall, 1989; 23: 49
4 Basinski Z S, Basinski S J. Acta Metall, 1985; 33: 1307
5 Jin N Y. Acta Metall, 1989; 37: 2055
6 Wang Zhongguang, Hu Tianbao, Xia Yuebo, Yang Qibin. Chin J Met Sci Technol, 1986; 2: 367
7 Liu Wei, Wang Zhongguang, Xia Yuebo. Chin J Met Sci Technol, 1989; 5: 123
8 Liu Wei, Wang Zhongguang, Xia Yuebo. Phys Status Solidi(a), 1989; 114: 177
9 林栋梁,吴建生.金属学报,1988;24:A76

[1] Zilong ZHANG, Shuang XIA, Wei CAO, Hui LI, Bangxin ZHOU, Qin BAI. EFFECTS OF GRAIN BOUNDARY CHARACTER ON INTERGRANULAR STRESS CORROSION CRACKING INITIATION IN 316 STAINLESS STEEL[J]. 金属学报, 2016, 52(3): 313-319.
[2] ZENG Qiang, YAN Ping, SHAO Chong, ZHAO Jingchen, HAN Fengkui,ZHANG Longfei. INVESTIGATION ON COARSENING BEHAVIORS OF SERRATED GRAIN BOUNDARIES IN K480 NICKEL BASE SUPERALLOY DURING LONG TERM AGING AT 900 ℃[J]. 金属学报, 2013, 49(1): 63-70.
[3] HAN Guangwei(Central Iron and Steel Research institute Ministry of Metallurgical Industry); SONG Yujiu; (Xi′an Jiaotong University)(Manuscript received 9 November; 1993; in revised form 3 June; 1994). EFFECTS OF HYDROGEN ATOMS OF INITIATION AND PROPAGATION OF CRACKS UNDER SLOW LOADING[J]. 金属学报, 1994, 30(10): 448-452.
No Suggested Reading articles found!