Acta Metall Sin  1986, Vol. 22 Issue (6): 73-78    DOI:
Current Issue | Archive | Adv Search |
STRESS CORROSION CRACKING IN HIGH STRENGTH STEEL UNDER MODE Ⅲ LOADING
by CHU Wuyang; XIAO Jimei (Chi-Mei Hsiao); ZHU Shuyan; XU Baiqi (Beijing University of Iron and Steel Technology)
Cite this article: 

by CHU Wuyang; XIAO Jimei (Chi-Mei Hsiao); ZHU Shuyan; XU Baiqi (Beijing University of Iron and Steel Technology). STRESS CORROSION CRACKING IN HIGH STRENGTH STEEL UNDER MODE Ⅲ LOADING. Acta Metall Sin, 1986, 22(6): 73-78.

Download:  PDF(961KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Stress corrosion cracking (SCC) of high-strength steel in aqueous medium in comparison to hydrogen induced cracking (HIC) during dynamic charging under mode Ⅲ loading was investigated. The threshold stress intensities for SCC and HIC under mode Ⅲ and Ⅰ were measured and compared. It was found that both SCC and HIC under mode Ⅲ loading initiated and propagated on the planes inclined at 45°to the notch plane, differing from that under mode Ⅰ loading. The fracture surfaces, however, revealed intergranular facets, similar to that under mode Ⅰ loading. The addition of thiourea decreases the threshold value for SCC under mode Ⅲ and Ⅰ loading, which was still higher than that for dynamic charging. The threshold values of both SCC and HIC under mode Ⅲ are larger than that under mode Ⅰ, i. e., K_(ⅢH)K_(ⅠH), K_(ⅢSCC)K_(ⅠSCC). Based upon the fracture mechanics analysis, this difference is attributed to the different equilibrium hydrogen concentration between mode Ⅲ and Ⅰ loading. These results give enough evidence that the SCC mechanism in high strength steel under mode Ⅲ loading is also related to hydrogen induced cracking.
Received:  18 June 1986     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1986/V22/I6/73

1 Hayden, H.W.; Floreen, S., Corrosion, 27 (1971) , 429.
2 Pickens, J. R.; Gordon, J.R.; Green, J.A.S., Metall Trans. A, 14A(1983) , 925.
3 Chu W.Y. (褚武扬); Hsiao C.M. (肖纪美); Ju S.Y. (朱淑彦); Wang C. (王枨), Corrosion 38(1982) , 446.
4 Chu W.Y. (褚武扬); Zhang T.Y. (张统一); Hsiao C.M.(肖纪美), Corrosion, 40(1984) , 197.
5 Chu W.Y. (褚武扬); Hsiao C.M. (肖纪美), Li S.Q.(李世琼), Corrosion, 37(1981) , 320.
6 Chu W.Y. (褚武扬); Hsiao C.M. (肖纪美) , Li W.X. (李文学); Zhang Y.G. (张彦国), Metall Trans. A, 15A(1984) , 2087.
7 褚武扬编著,断裂力学基础,科学出版社,1979.
8 Zhang T.Y.(张统一); Chu W.Y.(褚武扬); Hsiao C.M.(肖纪美), Metall. Trans. A,16A(1985) ,1649.
9 张统一;褚武扬;肖纪美,中国科学,1986,№3,316.
No related articles found!
No Suggested Reading articles found!