| EFFECT OF ZIGZAG GRAIN BOUNDARY ON CREEP RUPTURE OF A 10Cr-15Co-Ni-BASE WROUGHT SUPERALLOY |
| YE Ruizeng; GE Zhangying (Beijing University of Iron and Steel Technology); WANG Yueyi; DU Baoquan; LIAO Zhongyt; LI Lijia (Xindu Machine Works; Chengdu) (Manuscript received 23 December; 1982; revised manuscript 30 May; 1983) |
|
Cite this article:
YE Ruizeng; GE Zhangying (Beijing University of Iron and Steel Technology); WANG Yueyi; DU Baoquan; LIAO Zhongyt; LI Lijia (Xindu Machine Works; Chengdu) (Manuscript received 23 December; 1982; revised manuscript 30 May; 1983). EFFECT OF ZIGZAG GRAIN BOUNDARY ON CREEP RUPTURE OF A 10Cr-15Co-Ni-BASE WROUGHT SUPERALLOY. Acta Metall Sin, 1984, 20(1): 34-144.
|
|
|
Abstract Investigation was made of the effect of the zigzag or straight grain boundary, which may be obtained by two different schemes of heat treatment, on the creep rupture of a 10Cr-15Co-Ni-base wrought superalloy, especially, on the reason whyits strength and plasticity at elevated temperature can be improved by the zigzaggrain boundary. It is shown that the zigzag grain boundary may delay the initiation, growth and propagation of crack, as well as may also influence the crack morphology and the fracture mode markedly. Furthermore, the zigzag grain boundary may intensively inhibit the grain boundary sliding and retard the crack joining, thus, force the bulk-grains to take part in more deformation. It displays an important role in the tertiary stage of creep. The creep life to failure of the alloy tested with zigzag grain boundary was increased by a factor of 1/4, and the plasticity was also improved slightly.
|
|
Received: 18 January 1984
|
1 王迪;叶锐曾;徐志超;苏永安;高良;俞同丰;张润岗;李力加,北京钢铁学院学报(1982) ,№2,47．
2 徐志超;叶锐曾;王迪;张润岗;俞同丰,金属热处理,(1982) ,№6,36．
3 苏永安;高良;叶锐曾,GH 220合金弯曲晶界的研究,北京钢铁学院硕士研究生论文.
4 #12
5 #12
6 Larson, J.M., Metall. Trans., 7A (1976) , 1497．
7 Larson, J.M.; Floreen, S., Metall. Trans., 8A (1977) , 51．
8 Merrick, H.F.; Floreen, S., Metall. Trans., 9A (1978) , 231．
9 Miyagawa, O.; Yamamoto, M.; Kobayashi, M., Superalloys: Metallurgy and Manufacture, Proc. 3rd Int. Symp. on Superalloys, Eds. Kear, B.H.; Muzyka, D.R.; Tien, J.K., et al., Claitor's Pub., Baton Rouge, Louisiana, 1976, p. 245．
10 嵯峨卓朗;宫川大海;小林光征;藤代大,鈇銅,56(1970) ,55．
11 小林光征,山本 优;宫川大海,嵯峨卓朗,藤代大,鉄鋼,58(1972) ,859．
12 山本 优;持木良美;宫川大海;藤代 大,鉄鋼,60(1974) ,584．
13 山崎道夫;日本金属学会誌,30(1966) ,1032．
14 褚幼义;贺信莱;张兴钤,蠕变断裂机构,北京钢铁学院资料,1964．
15 余宗森;王敬智;葛占英;张兴钤,212镍基耐热合金的蠕变与断裂,北京钢铁学院资料,1965．
16 田家凯教授来华讲学笔记,1980．
17 Furillo, F, T.; Davidson, J.M.; Tien, J. K.; Jackman, L.A., Mater. Sci. Eng., 39 (1979) , 267．
18 穆志平;高良;叶锐曾;田树森,GH 37合金的弯曲晶界及其对蠕变断裂性能的影响,北京钢铁学院硕士研究生论文,1982,待发表. |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|