| MORPHOLOGY OF SUB-CRITICAL GROWTH ON STRESS CORROSION CRACKING AND PLASTIC ZONE AT CRACK TIP |
| Lin Dongliang(T. L. Lin); Wu Jiansheng; Yang Zhengrui and Yah Benda (Shanghai Jiaotong University) |
|
Cite this article:
Lin Dongliang(T. L. Lin); Wu Jiansheng; Yang Zhengrui and Yah Benda (Shanghai Jiaotong University). MORPHOLOGY OF SUB-CRITICAL GROWTH ON STRESS CORROSION CRACKING AND PLASTIC ZONE AT CRACK TIP. Acta Metall Sin, 1981, 17(6): 617-704.
|
|
|
Abstract Using polished cantilever specimens made of two high strength steels 40CrNiMoA and AISI4330M, the nucleation and propagation on stress corrosion cracking in distilled water have been traced by metallographie shadowing technique. The morphology of sub-critical crack growth has also been observed. It was indicated that the shadow zone, i.e. a plastic deformation area in the front of crack tip, reveals. its different morphologies in various steels. In 40CrNiMoA, the shadow zone grows and joins one another with the crack propagation. In 4330M, it does not join together, but develop along two parallel paths. The catlike shadow zone immediately appeared at the crack tip after loading can be considered as the plastic zone at the crack tip. However, the shadow zone hereafter observed during whole process of the crack propagation seems not to present the plastic zone at the crack, but to represent the deformation induced by. the formation of shear lip and can be related closely to the pop-in. This should be distinguished from the plastic zone at the crack tip in the linear elastic fracture mechanics.
|
|
Received: 18 June 1981
|
[1] Tien, J. K., Buck, O., Batec, R. C. and Nair, S., Scr. Metall., 14 (1980) , 583．
[2] 褚武扬,肖纪美,李世琼,金属学报,17(1981) ,10．
[3] 褚武扬,李世琼,肖纪美,王枨,金属学报,16(1980) ,179．
[4] 褚武扬,李世琼,肖纪美,刘天化,北京钢铁学院学报,2(1979) ,126．
[5] 张百伟,杜家驹,金属学报,17(1981) ,18．
[6] Green, G., Smith, R. F. and Knott, J. F., Mechanics and Mechanism of Crack Growth, Proceedings of Conference Organised by the Physical Metallurgy Centre of the British Steel Corporation Held at Churchill College, Cambrige, 1973, p.58．
[7] Corcos, J., Nomine, A. M. and Miannay, D., Advances in Research on the Strength and Fracture of Materials, Vol. 2A, Ed. by D. M. R. Taplin, Pergamon Press, New York, 1978, p. 261．
[8] Boyd, G. M., Brittle Fracture in Steel Structures, Butterworths, London, 1970, p. 35．
[9] Beachem, C. D., Metall. Trans., 3 (1972) , 437．
[10] Knott, J. F., Advances in Research on the Strength and Fracture of Materials, Vol. 1, Ed. by D. M. R. Taplin, Pergamon Press, New York, 1978, p. 61．
[11] Knott, J. F., Fundamentals of Fracture Mechanics, Butterworths, London, 1973, p. 75．h |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|