THE ISOTHERMAL SECTIONS AT 1200℃ OF THE EQUILIBRIUM DIAGRAMS OF THE SYSTEMS Mo-Ti-Zr AND Mo-Nb-Zr
CHUANG Y-CHIH; T'ANG CH'AN-HONG; CHUANG HSIANG-LIN
Cite this article: 

CHUANG Y-CHIH; T'ANG CH'AN-HONG; CHUANG HSIANG-LIN. THE ISOTHERMAL SECTIONS AT 1200℃ OF THE EQUILIBRIUM DIAGRAMS OF THE SYSTEMS Mo-Ti-Zr AND Mo-Nb-Zr. Acta Metall Sin, 1966, 9(1): 63-124.

Download:  PDF(3301KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The isothermal sections at 1200℃ of the systems Mo-Ti-Zr and Mo-Nb-Zr have been determined by metallographic and X-ray diffraction methods supplemented by hardness measurements. The constitutions of these two systems are strikingly similar; besides a b.c.c, ternary terminal solid solution and a ternary Laves phase isomorphous with MgCu_2 structure, no new intermediate phase has been found.In the Mo-Ti-Zr system the lattice parameter of the ternary solid solution increases with the increase of Ti or Zr in solid solution, and the ternary Laves phase is (Ti, Zr) Mo_2. In the Mo-Nb-Zr system, the lattice parameter of the ternary solid solution also increases with the increase in the Nb- or Zr-content, and the ternary phase in this case is Zr(Mo, Nb)_2.The iso-hardness contours of the Mo-Ti-Zr system tend to expand towards the titanium corner as the Ti-content is increased, whereas those of the Mo-Nb-Zr system expand towards the niobium corner with the increase in Nb-content in a like manner.
Received:  18 January 1966     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1966/V9/I1/63

[1] Hansen, M., Kamen, E. L., Kessler, H. D., et al.: Trans. AIME, 1951, 191, 881.
[2] De Boer, J. H., Clausing, P.: Physica, 1930, 10, 267.
[3] Domagala, R. F., Mcpherson, D. J., Hansen, M.: Trans. AIME, 1953, 197, 73.
[4] Semchyshen, M., Barr, R. Q.: Refractory Metals and Alloys, (Interscience, 1961) , vol. 11, p. 300.
[5] Buckle, H.: Z. Metallk., 1946, 37, 53.
[6] Rogers, B. A., Atkins, D. F.: Trans. AIME, 1956, 206, 619.
[7] Rogers, B. A., Atkins, D F.: Trans. AIME, 1955, 203, 1034.
[8] #12
[9] Chuang Yu-chih (庄育智), Chuang Tsiang-lin (庄祥麟), Wu Cheung-hang (吴昌衡): Sci. Sinica, 1963, 15, 1851.
[10] Taylor, A., Sinclair, H.: Proc. Phys. Soc., 1945, 57, 108.
[11] Taylor, A., Sinclair, H.: Proc. Phys. Soc., 1945, 57, 126.
[12] Hansen, M., Anderko, K.: Constitution of Binary Alloys, 2nd ed., (McGraw-Hill, 1958) , p. 981.
[13] Hansen, M., Anderko, K.: Constitution of Binary Alloys, 2nd ed., (McGraw-Hill, I958) , p. 1022.
No related articles found!
No Suggested Reading articles found!