| A STUDY OF SIDE-BLOWN BASIC BESSEMER STEEL |
| WU CHAO-WANG;PAI CHAO-KUNG Institute of Ferrous Metallurgy Tang-Shan Steel Plant |
|
Cite this article:
WU CHAO-WANG;PAI CHAO-KUNG Institute of Ferrous Metallurgy Tang-Shan Steel Plant. A STUDY OF SIDE-BLOWN BASIC BESSEMER STEEL. Acta Metall Sin, 1957, 2(3): 237-247.
|
|
|
Abstract A total of more than 150 experimental heats was tested, and the results pointout that in order to improve the properties of side-blown Bessemer steel, thefollowing facts should be considered: 1) Normal temperature mechanical test results of side-blown basic Bessemersteel are higher than the lower limits enumerated for group A, steels in the Stan-dard Specifications of the Ministry of Metallurgy. However, due to the highernitrogen content, averaging about 0.008%, such steel is obviously nonfavorable ascompared with acid Bessemer as well as basic open-hearth steels with respect tosuch properties as strain-aging, blue-brittleness and sub-zero behaviors. The pre-vious usage of chemical specifications of open-hearth steel to side-blown basicbessemer steel is evidently impractical, as the influence of nitrogen content in thelatter is unduly neglected. In the present paper, a suggestion is made for modi-fying the chemical specification of basic Bessemer steel. 2) Nitrogen and non-metallic inclusions noticeably affect the properties of steel.When the depth of blowing is kept unchanged, content of nitrogen and non-metallic inclusion depend, to a large extend, upon the amount of residuel carbonat the end point of blowing. The present paper further suggests that in the future,the practice of blowing to too low a carbon content with subsequent recarburizingin the laddle should be avoided.
|
|
Received: 18 March 1957
|
[1] W. W. Webb, R. R. Webster, H. H. George Operation of the Experimental Converter.
[2] C. E. Sims, F. L. Toy, Experimental Operation of a Basiclined Surface Blown Hearth for Steel Production.
[3] Physical Chemistry of Steelmaking Committee. Basic Open Hearth Steel Making.
[4] 松岛喜市郎编,制钢法.
[5] Journal of Metals, December, 1953, Relationship of Spectrochemical Al to Mcquaid-Ehn grainsize.
[6] Samuel L. Case, Aluminum in lron & Steel.
[7] A. S. M. Grain-Size Symposium.
[8] C. A. Edwards, The Structure & Properties of Mild Steel.
[9] Hollomon Taffe, Ferrous Metallurgical Design.
[10] A. S. M. Age hardening of Metals.
[11] J. M. Camp, The Making, Shaping & Treating of Steel.
[12] Б.А.Андреев
[13] И.Р.Крунин
[14] Metal Progress October, 1951． Bessemer Steel Low in N & P.
[15] Transactions of the A. S. M. Mechsnical Properties of Metals at Low Temperature. |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|