研究论文

激光摆动对激光熔化沉积钛合金微观组织及力学性能的影响

  • 方远志 ,
  • 戴国庆 ,
  • 郭艳华 ,
  • 孙中刚 ,
  • 刘红兵 ,
  • 袁秦峰
展开
  • 1.南京工业大学 材料科学与工程学院 新材料研究院 南京 210009
    2.上海工程技术大学 材料工程学院 上海 201620
    3.浙江申吉钛业股份有限公司 湖州 313306
方远志,男,1997年生,硕士生

收稿日期: 2021-12-31

  修回日期: 2022-05-08

  网络出版日期: 2022-06-28

基金资助

国家自然科学基金项目(51875274);浙江省重点研发计划项目(2021C01085);江苏高校优势学科建设工程项目

Effect of Laser Oscillation on the Microstructure and Mechanical Properties of Laser Melting Deposition Titanium Alloys

  • Yuanzhi FANG ,
  • Guoqing DAI ,
  • Yanhua GUO ,
  • Zhonggang SUN ,
  • Hongbing LIU ,
  • Qinfeng YUAN
Expand
  • 1.Tech Institute for Advanced Materials, College of Materials Science and Engineering, Nanjing Tech University, Nanjing 210009, China
    2.School of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620, China
    3.Zhejiang Shenji Titanium Industry Co., Ltd., Huzhou 313306, China
SUN Zhonggang, professor, Tel: 15921177783, E-mail: sunzgg@njtech.edu.cn

Received date: 2021-12-31

  Revised date: 2022-05-08

  Online published: 2022-06-28

Supported by

National Natural Science Foundation of China(51875274);Key Research and Development Project of Zhejiang Province(2021C01085);Priority Academic Program Development of Jiangsu Higher Education Institutions

摘要

针对激光熔化沉积冶金组织与缺陷,借鉴激光摆动焊接技术,提出一种激光摆动送粉增材制造TC4钛合金工艺,借助激光原位摆动改变熔池运动轨迹进而影响温度梯度和凝固速率,改善增材制造钛合金的微观组织。利用OM、SEM、EBSD和Vickers硬度计研究了激光摆动送粉增材制造工艺对TC4钛合金微观组织演变及力学性能的影响。结果表明,无摆动激光熔化沉积实验的最佳工艺参数为:激光功率1000 W,扫描速率8 mm/s,送粉速率6.92 g/min;直线型激光摆动的最佳工艺参数为:摆动频率200 Hz,摆动幅度1.5 mm。直线型激光摆动对熔池形貌改善显著,气孔和裂纹等缺陷较少,柱状晶数量和尺寸均有所减小,并且晶粒出现了等轴化的现象。相比无摆动样品,激光摆动后Ti-6Al-4V合金单道区域平均晶粒尺寸从5.20 μm减小到4.37 μm;硬度从418.00 HV提升到428.75 HV。

本文引用格式

方远志 , 戴国庆 , 郭艳华 , 孙中刚 , 刘红兵 , 袁秦峰 . 激光摆动对激光熔化沉积钛合金微观组织及力学性能的影响[J]. 金属学报, 2023 , 59(1) : 136 -146 . DOI: 10.11900/0412.1961.2021.00600

Abstract

Laser melting deposition (LMD) combines the laser cladding and rapid prototyping manufacturing technologies, and can be used for swift prototyping of complex parts with excellent comprehensive properties. However, due to its unique metallurgical conditions, it is easy to develop penetrating columnar crystals and coarse primary grains along the building direction. This remarkably reduces the mechanical properties of the alloy. The root cause of this issue can be traced back to the thermodynamic and dynamic metallurgical processes. Thus, this study proposes an oscillating laser melting deposition (OLMD) based on laser oscillating welding technology, and aims to elucidate the metallurgical structure and defects of laser melt deposition. OLMD modifies the motion trajectory of the molten pool using a laser in situ oscillation, and directly impacts the temperature gradient and solidification rate, thus improving the microstructure of titanium alloy by LMD. Furthermore, the microstructure evolution and mechanical properties of TC4 titanium alloy produced using OLMD were studied using OM, SEM, EBSD, and a Vickers hardness tester. The results indicate that the optimum process parameters of laser melting deposition without oscillation are as follows: the laser power is 1000 W, scanning rate is 8 mm/s, and powder feeding rate is 6.92 g/min. The optimum technological parameters of linear oscillation are as follows: the frequency is 200 Hz and the oscillation amplitude is 1.5 mm. Addition of linear laser oscillation considerably improved the morphology of the molten pool, and defects such as porosity and cracks were not observed. The overall number and size of columnar crystals reduced, and the grains were equiaxed. When compared to the sample without oscillation, the average grain size of Ti-6Al-4V alloy with linear oscillation decreased from 5.20 μm to 4.37 μm, while hardness increased from 418.00 HV to 428.75 HV.

参考文献

1 DebRoy T, Wei H L, Zuback J S, et al. Additive manufacturing of metallic components-process, structure and properties [J]. Prog. Mater. Sci., 2018, 92: 112
2 Oliveira J P, Santos T G, Miranda R M. Revisiting fundamental welding concepts to improve additive manufacturing: From theory to practice [J]. Prog. Mater. Sci., 2020, 107: 100590
3 Akbari M, Kovacevic R. An investigation on mechanical and microstructural properties of 316LSi parts fabricated by a robotized laser/wire direct metal deposition system [J]. Addit. Manufactur., 2018, 23: 487
4 Murray A K, Isik T, Ortalan V, et al. Two-component additive manufacturing of nanothermite structures via reactive inkjet printing [J]. J. Appl. Phys., 2017, 122: 184901
5 Gu?nther J, Krewerth D, Lippmann T, et al. Fatigue life of additively manufactured Ti-6Al-4V in the very high cycle fatigue regime [J]. Int. J. Fatigue, 2017, 94: 236
6 Kusuma C. The effect of laser power and scan speed on melt pool characteristics of pure titanium and Ti-6Al-4V alloy for selective laser melting [D]. Dayton: Wright State University, 2016
7 Zhang D Y, Qiu D, Gibson M A, et al. Additive manufacturing of ultrafine-grained high-strength titanium alloys [J]. Nature, 2019, 576: 91
8 Wang J, Lin X, Li J Q, et al. A study on obtaining equiaxed prior-β grains of wire and arc additive manufactured Ti-6Al-4V [J]. Mater. Sci. Eng., 2020, A772: 138703
9 Zhirnov I V, Podrabinnik P A, Okunkova A A, et al. Laser beam profiling: Experimental study of its influence on single-track formation by selective laser melting [J]. Mech. Ind., 2015, 16: 709
10 Liu S Y, Shin Y C. Additive manufacturing of Ti6Al4V alloy: A review [J]. Mater. Des., 2019, 164: 107552
11 Fayazfar H, Salarian M, Rogalsky A, et al. A critical review of powder-based additive manufacturing of ferrous alloys: Process parameters, microstructure and mechanical properties [J]. Mater. Des., 2018, 144: 98
12 Ngo T D, Kashani A, Imbalzano G, et al. Additive manufacturing (3D printing): A review of materials, methods, applications and challenges [J]. Composites, 2018, 143B: 172
13 Martin A A, Calta N P, Khairallah S A, et al. Dynamics of pore formation during laser powder bed fusion additive manufacturing [J]. Nat. Commun., 2019, 10: 1987
14 Yu H Q, Zhu M Y. Effect of electromagnetic stirring in mold on the macroscopic quality of high carbon steel billet [J]. Acta Metall. Sin. (Engl. Lett.), 2009, 22: 461
15 Jiang Z G, Chen X, Li H, et al. Grain refinement and laser energy distribution during laser oscillating welding of Invar alloy [J]. Mater. Des., 2020, 186: 108195
16 Qiu C L, Ravi G A, Dance C, et al. Fabrication of large Ti-6Al-4V structures by direct laser deposition [J]. J. Alloys Compd., 2015, 629: 351
17 Xu W, Lui E W, Pateras A, et al. In situ tailoring microstructure in additively manufactured Ti-6Al-4V for superior mechanical performance [J]. Acta Mater., 2017, 125: 390
18 Xu W, Brandt M, Sun S, et al. Additive manufacturing of strong and ductile Ti-6Al-4V by selective laser melting via in situ martensite decomposition [J]. Acta Mater., 2015, 85: 74
19 Carroll B E, Palmer T A, Beese A M. Anisotropic tensile behavior of Ti-6Al-4V components fabricated with directed energy deposition additive manufacturing [J]. Acta Mater., 2015, 87: 309
20 Yuan D, Shao S Q, Guo C H, et al. Grain refining of Ti-6Al-4V alloy fabricated by laser and wire additive manufacturing assisted with ultrasonic vibration [J]. Ultrason. Sonochem., 2021, 73: 105472
21 Huang W C, Chuang C S, Lin C C, et al. Microstructure-controllable laser additive manufacturing process for metal products [J]. Phys. Proced., 2014, 56: 58
22 Meng X, Min J, Sun Z G, et al. Columnar to equiaxed grain transition of laser deposited Ti6Al4V using nano-sized B4C particles [J]. Composites, 2021, 212B: 108667
23 Choi K D, Ahn Y N, Kim C. Weld strength improvement for Al alloy by using laser weaving method [J]. J Laser Appl., 2010, 22(3): 116
24 Cai C, Li L Q, Chen X Y, et al. Study on laser-MAG hybrid weaving welding characteristics for high-strength steel [J]. J. Laser App., 2016, 28: 022401
25 Zhang X, Chen W, Bao G, et al. Suppression of porosity in beam weaving laser welding [J]. Sci. Technol. Weld. Join., 2004, 9: 374
26 Gong M C, Meng Y F, Zhang S, et al. Laser-arc hybrid additive manufacturing of stainless steel with beam oscillation [J]. Addit. Manuf., 2020, 33: 101180
27 Gusarov A V, Malakhova-Ziablova I S, Pavlov M D. Thermoelastic residual stresses and deformations at laser treatment [J]. Phys. Procedia., 2013, 41: 896
28 Tan X P, Kok Y, Tan Y J, et al. Graded microstructure and mechanical properties of additive manufactured Ti-6Al-4V via electron beam melting [J]. Acta Mater., 2015, 97: 1
29 Pantleon W. Resolving the geometrically necessary dislocation content by conventional electron backscattering diffraction [J]. Scr. Mater., 2008, 58: 994
30 Zhang C, Li X W, Gao M. Effects of circular oscillating beam on heat transfer and melt flow of laser melting pool [J]. J. Mater. Res. Technol., 2020, 9: 9271
31 Wang T, Zhu Y Y, Zhang S Q, et al. Grain morphology evolution behavior of titanium alloy components during laser melting deposition additive manufacturing [J]. J. Alloys Compd., 2015, 632: 505
32 Xia Y L, Chen H N, Liang X D, et al. Circular oscillating laser melting deposition of nickel-based superalloy reinforced by WC: Microstructure, wear resistance and electrochemical properties [J]. J. Manuf. Processes, 2021, 68: 1694
33 Liang Z L, Sun Z G, Zhang W S, et al. The effect of heat treatment on microstructure evolution and tensile properties of selective laser melted Ti6Al4V alloy [J]. J. Alloys Compd., 2019, 782: 1041
34 Xiao H, Cheng M P, Song L J. Direct fabrication of single-crystal-like structure using quasi-continuous-wave laser additive manufacturing [J]. J. Mater. Sci. Technol., 2021, 60: 216
文章导航

/