Effect of Adding Ag on the Nanoindentation Behavior of Cu-Zr-Al-Based Metallic Glass
Received date: 2021-01-06
Revised date: 2021-03-08
Online published: 2021-03-23
Supported by
National Natural Science Foundation of China(51925103)
采用铜模吸铸法制备得到不同Ag含量的Cu45Zr45Al10-xAgx (x = 1、2、3、5,原子分数,%)金属玻璃。利用纳米压痕技术系统地探讨了Ag元素添加对Cu-Zr-Al基金属玻璃纳米塑性变形行为的影响。借助经验方程拟合纳米压痕蠕变曲线求得应变速率敏感指数(m),进而计算出蠕变过程中的剪切转变区体积(Ω)。通过Kohlrausch-Williams-Watts方程拟合蠕变深度曲线,分析蠕变过程中的弛豫行为。结果表明,Ag含量增加导致KWW方程的扩展指数(β)增加。与此同时,Cu-Zr-Al基金属玻璃的硬度随微量Ag元素含量的增加而提高,并且在维持高硬度的基础上提高了塑性。本工作为理解金属玻璃热稳定性与力学性能的相关性奠定了基础。
张倪侦 , 马昕迪 , 耿川 , 穆永坤 , 孙康 , 贾延东 , 黄波 , 王刚 . Ag元素添加对Cu-Zr-Al基金属玻璃纳米压痕行为的影响[J]. 金属学报, 2021 , 57(4) : 567 -574 . DOI: 10.11900/0412.1961.2021.00009
Metallic glasses (MGs) with a long-range disordered structure and without crystallographic defects have attracted great research attention. Owing to the disordered structure, MGs usually exhibit excellent physical and chemical properties, comprehensive mechanical performances, and high thermal stability. Minor doping of elements can effectively enhance the glass-forming ability of MGs and then seriously affect the yielding strength and plasticity. In this study, a family of Cu45Zr45Al10-xAgx (x = 1, 2, 3, and 5, atomic fraction, %) MG with minor Ag-addition was prepared by suction casting. A nanoindentation test was used to investigate the influence of Ag content on the nanoplastic deformation behavior of the Cu-Zr-Al-based MG. In terms of the empirical equation, the strain rate sensitivity index (m) was acquired to calculate the shear transformation zone volume during the nanoindentation creep process. Based on the Kohlrausch-Williams-Watts equation, the relaxation evolution was obtained. As Ag content approaches 5%, m attains its minimum, indicating that the creep resistance of the Cu-Zr-Al-based MG is the largest. The creep behavior of the system depends on the loading rate, i.e., the faster the loading rate, the lower the creep resistance. With an increase in the Ag content, the exponent stretch is increased, and the hardness of the Cu-Zr-Al-based MG was enhanced combined with an increased plasticity. This study presents the fundamental information of the relationship between the thermal dynamic and mechanical properties of the Cu-Zr-Al-based MG.
Key words: metallic glass; creep depth; shear transition zone volume; relaxation
| 1 | Ashby M F, Greer A L. Metallic glasses as structural materials [J]. Scr. Mater., 2006, 54: 321 |
| 2 | Bhowmick R, Raghavan R, Chattopadhyay K, et al. Plastic flow softening in a bulk metallic glass [J]. Acta Mater., 2006, 54: 4221 |
| 3 | Wang W H. Roles of minor additions in formation and properties of bulk metallic glasses [J]. Prog. Mater. Sci., 2007, 52: 540 |
| 4 | Klement W, Willens R H, Duwez P. Non-crystalline structure in solidified gold-silicon alloys [J]. Nature, 1960, 187: 869 |
| 5 | Drehman A J, Greer A L, Turnbull D. Bulk formation of a metallic glass: Pd40Ni40P20 [J]. Appl. Phys. Lett., 1982, 41: 716 |
| 6 | Zhang Y, Zhou M, Zhao X Y, et al. Co substituted Zr-Cu-Al-Ni metallic glasses with enhanced glass-forming ability and high plasticity [J]. J. Non-Cryst. Solids, 2017, 473: 120 |
| 7 | Zhang Y, Chen J, Chen G L, et al. Glass formation mechanism of minor yttrium addition in CuZrAl alloys [J]. Appl. Phys. Lett., 2006, 89: 131904 |
| 8 | Park E S, Kim D H. Phase separation and enhancement of plasticity in Cu-Zr-Al-Y bulk metallic glasses [J]. Acta Mater., 2006, 54: 2597 |
| 9 | Liu Y H, Wang G, Pan M X, et al. Deformation behaviors and mechanism of Ni-Co-Nb-Ta bulk metallic glasses with high strength and plasticity [J]. J. Mater. Res., 2007, 22: 869 |
| 10 | Cheng Y Q, Ma E, Sheng H W. Alloying strongly influences the structure, dynamics, and glass forming ability of metallic supercooled liquids [J]. Appl. Phys. Lett., 2008, 93: 111913 |
| 11 | Li F, Zhang H J, Liu X J, et al. Effects of Al addition on atomic structure of Cu-Zr metallic glass [J]. J. Appl. Phys., 2018, 123: 055101 |
| 12 | Cheng Y Q, Cao A J, Sheng H W, et al. Local order influences initiation of plastic flow in metallic glass: Effects of alloy composition and sample cooling history [J]. Acta Mater., 2008, 56: 5263 |
| 13 | Xu D H, Lohwongwatana B, Duan G, et al. Bulk metallic glass formation in binary Cu-rich alloy series——Cu100-xZrx (x = 34, 36, 38.2, 40 at.%) and mechanical properties of bulk Cu64Zr36 glass [J]. Acta Mater., 2004, 52: 2621 |
| 14 | Zhang W, Inoue A. High glass-forming ability and good mechanical properties of new bulk glassy alloys in Cu-Zr-Ag ternary system [J]. J. Mater., 2006, 21: 234 |
| 15 | Jiang Q K, Wang X D, Nie X P, et al. Zr-(Cu, Ag)-Al bulk metallic glasses [J]. Acta Mater., 2008, 56: 1785 |
| 16 | Wang X, Cao Q P, Chen Y M, et al. A plastic Zr-Cu-Ag-Al bulk metallic glass [J]. Acta Mater., 2011, 59: 1037 |
| 17 | Li M C, Jiang M Q, Jiang F, et al. Testing effects on hardness of a Zr-based metallic glass under nanoindentation [J]. Scr. Mater., 2017, 138: 120 |
| 18 | Fornell J, Concustell A, Greer A L, et al. Effects of shot peening on the nanoindentation response of Cu47.5Zr47.5Al5 metallic glass [J]. J. Alloys Compd., 2014, 586: S36 |
| 19 | Liu F X, Gao Y F, Liaw P K. Rate-dependent deformation behavior of Zr-based metallic-glass coatings examined by nanoindentation [J]. Metall. Mater. Trans., 2008, 39A: 1862 |
| 20 | Yang Y, Zeng J F, Ye J C, et al. Structural inhomogeneity and anelastic deformation in metallic glasses revealed by spherical nanoindentation [J]. Appl. Phys. Lett., 2010, 97: 261905 |
| 21 | Yoo B G, Oh J H, Kim Y J, et al. Nanoindentation analysis of time-dependent deformation in as-cast and annealed Cu-Zr bulk metallic glass [J]. Intermetallics, 2010, 18: 1898 |
| 22 | Burgess T, Laws K J, Ferry M. Effect of loading rate on the serrated flow of a bulk metallic glass during nanoindentation [J]. Acta Mater., 2008, 56: 4829 |
| 23 | Bian X L, Wang G, Chen H C, et al. Manipulation of free volumes in a metallic glass through Xe-ion irradiation [J]. Acta Mater., 2016, 106: 66 |
| 24 | Bian X L, Zhao D, Kim J T, et al. Controlling the distribution of structural heterogeneities in severely deformed metallic glass [J]. Mater. Sci. Eng., 2019, A752: 36 |
| 25 | Johnson W L, Samwer K. A universal criterion for plastic yielding of metallic glasses with a (T/Tg)2/3 temperature dependence [J]. Phys. Rev. Lett., 2005, 95: 195501 |
| 26 | Pan D, Inoue A, Sakurai T, et al. Experimental characterization of shear transformation zones for plastic flow of bulk metallic glasses [J]. Proc. Natl. Acad. Sci. USA, 2008, 105: 14769 |
| 27 | Argon A S. Plastic deformation in metallic glasses [J]. Acta Metall., 1979, 27: 47 |
| 28 | Ma X D, Li P Y, Wang G. Nano-indentation creep behavior of a Co56Ta35B9 metallic glass film [J]. Shanghai Met., 2019, 41(6): 39 |
| 28 | 马昕迪, 李培友, 王 刚. Co56Ta35B9非晶合金薄膜纳米压痕蠕变行为研究 [J]. 上海金属, 2019, 41(6): 39 |
| 29 | Yang B, Riester L, Nieh T G. Strain hardening and recovery in a bulk metallic glass under nanoindentation [J]. Scr. Mater., 2006, 54: 1277 |
| 30 | Tong X, Wang G, Yi J, et al. Shear avalanches in plastic deformation of a metallic glass composite [J]. Int. J. Plast., 2016, 77: 141 |
| 31 | Li J, Ke C H, Tong X, et al. Impact of free volume on shear band multiplication and bending plasticity [J]. Mater. Sci. Eng., 2019, A747: 136 |
| 32 | Zhang M, Chen Y, Li W. On the origin of softening in the plastic deformation of metallic glasses [J]. Int. J. Plast., 2019, 116: 24 |
/
| 〈 |
|
〉 |