Re对一种定向凝固镍基高温合金微观组织的影响*
收稿日期: 2015-11-19
网络出版日期: 2016-03-21
基金资助
* 国家自然科学基金项目51101160和51501117, 国家重大科学仪器设备开发专项项目2012YQ22023304, 以及辽宁省教育厅项目L2014050资助
INFLUENCE OF Re ON MICROSTRUCTURESOF A DIRECTIONALLY SOLIDIFIEDNi-BASED SUPERALLOY
Received date: 2015-11-19
Online published: 2016-03-21
Supported by
Supported by National Natural Science Foundation of China (Nos.51101160 and 51501117), National Key Foundation for Exploring Scientific Instrument (No.2012YQ22023304) and Liaoning Provincial Department of Education Project (No.L2014050)
采用SEM, EPMA和TEM等技术对不含Re (0Re)和含2%Re (2Re)的定向柱晶高温合金铸态和热处理态组织进行了系统的研究. 结果表明: Re促进了铸态共晶外围和晶界上μ相的析出; 合金热处理后, Re明显促进了MC碳化物周围和晶界上相的析出, 0Re合金MC碳化物周围只有少量的M6C相析出, 晶界上有细小的M23(C, B)6硼碳化物析出, 而2Re合金MC碳化物周围和晶界上都有大量块状μ相析出, μ相的析出促进了γ′包层的形成. 0Re合金中B元素明显偏聚于晶界, 而2Re合金中B元素分布相对比较均匀. 并对热处理过程中μ相的析出机制进行了深入分析.
张思倩 , 王栋 , 王迪 , 彭建强 . Re对一种定向凝固镍基高温合金微观组织的影响*[J]. 金属学报, 2016 , 52(7) : 851 -858 . DOI: 10.11900/0412.1961.2015.00600
Up to now, considerable effort has been expended in attempts to investigate the influences of Re on Ni-based single crystal superalloys. However, few study had elucidated the influences of Re on carbide, boride and grain boundary. Therefore, the influence of a 2%Re (mass fraction) addition on the as-cast and heat-treated microstructures of a Ni-based directionally solidified superalloy was investigated by comparison with Re-free alloy using SEM, EPMA and TEM. The results show that Re accelerates the precipitation of μ phase in the periphery of eutectic and at grain boundary for as-cast microstructure. After heat treatment, Re also accelerates the precipitation of phase in the vicinity of primary MC carbide and at grain boundary. For 0Re alloy, there are small number of M6C carbide in the vicinity of primary MC carbide and M23(C, B)6 boro-carbide at grain boundary. For 2Re alloy, a large amount of blocky μ phase enveloped by thick γ′-film is found in the vicinity of primary MC carbide and at grain boundary. Enrichment of B along the grain boundary is observed in 0Re alloy. On the contrary, relatively uniform distribution of B is found in 2Re alloy. The precipitation mechanism of μ phase during the process of heat treatment is also analyzed.
Key words： Ni-based superalloy; directional solidification; Re; μ phase; grain boundary; carbide
| [1] | Koizumi Y, Kobayashi T, Yokokawa T, Zhang J X, Osawa M, Harada H, Aoki Y, Arai M.In: Green K A, Pollock T M, Harada H, Howson T E, Reed R C, Schirra J J, Walston S eds., Superalloys 2004, Warrendale, PA: The Minerals, Materials and Metals Society, 2004: 35 |
| [2] | Harris K, Erickson G L, Sikkenga S L, Brentnall W D, Aurrecoechea J M, Kubarych K G.J Mater Eng Perform, 1993; 2: 481 |
| [3] | Ross E W, O'Hara K S. In: Antolovich S D, Stusrud R W, MacKay R A, Anton D L, Khan T, Kissinger R D, Klarstrom D L eds., Superalloys 1992, Warrendale, PA: The Minerals, Materials and Metals Society, 1992: 257 |
| [4] | Cetel A D, Duhl D N.In: Antolovich S D, Stusrud R W, MacKay R A, Anton D L, Khan T, Kissinger R D, Klarstrom D L eds., Superalloys 1992, Warrendale, PA: The Minerals, Materials and Metals Society, 1992: 287 |
| [5] | Bürgel R, Grossmann J, Lüseberink O, Mughrabi H, Pyczak F, Singer R F, Volek A.In: Green K A, Pollock T M, Harada H, Howson T E, Reed R C, Schirra J J, Walston S eds., Superalloys 2004, Warrendale, PA: The Minerals, Materials and Metals Society, 2004: 25 |
| [6] | Harris K, Erickson G L, Schwer R E.In: Gell M, Kortovich C S, Bricknell R H, Kent W B, Radovich J F eds., Superalloys 1984, Warrendale, PA: The Minerals, Materials and Metals Society, 1984: 221 |
| [7] | Harris K, Erickon G L, Sikkenga S L, Kubarych K G.In: Antolovich S D, Stusrud R W, MacKay R A, Anton D L, Khan T, Kissinger R D, Klarstrom D L eds., Superalloys 1992, Warrendale, PA: The Minerals, Materials and Metals Society, 1992: 297 |
| [8] | Chen R Z. J Aero Mater, 1993; (1): 47 |
| [8] | (陈荣章. 航空材料学报, 1993; (1): 47) |
| [9] | Blavette D, Caron P, Khan T.Scr Mater, 1986; 20: 1395 |
| [10] | Warren P J, Cerezo A, Smith G D W.Mater Sci Eng, 1998; A250: 88 |
| [11] | Mottura A, Warnken N, Miller M K, Finnis M W, Reed R C.Acta Mater, 2010; 58: 931 |
| [12] | Wanderka N, Glatzel U.Mater Sci Eng, 1995; A203: 69 |
| [13] | Rüsing J, Wanderka N, Czubayko U, Naundorf V, Mukherji D, R?sler J.Scr Mater, 2002; 46: 235 |
| [14] | Epishin A, Bruckner U, Portella P D, Link T.Scr Mater, 2003; 48: 455 |
| [15] | Fu C L, Reed R, Janotti A, Krcmar M.In: Green K A, Pollock T M, Harada H, Howson T E, Reed R C, Schirra J J, Walston S eds., Superalloys 2004, Warrendale, PA: The Minerals, Materials and Metals Society, 2004: 867 |
| [16] | Luo Y S, Li J R, Liu S Z, Sun F L, Han X M, Cao C X.Chin J Nonferrous Met, 2005; 15: 1655 |
| [16] | (骆宇时, 李嘉荣, 刘世忠, 孙凤礼, 韩秀梅, 曹春晓. 中国有色金属学报, 2005; 15: 1655) |
| [17] | Li P, Li Q Q, Jin T, Zhou Y Z, Li J G, Sun X F, Zhang Z F.Mater Sci Eng, 2014; A603: 84 |
| [18] | Zhang Y D, Yang Z G, Zhang C, Lan H.Chin J Aero, 2010; 23: 370 |
| [19] | Wang M G, Tian S G, Yu H C, Yu X F, Qian B J.J Aero Mater, 2009; 29(4): 98 |
| [19] | (王明罡, 田素贵, 于慧臣, 于兴福, 钱本江. 航空材料学报, 2009; 29(4): 98) |
| [20] | Li J R, Tang D Z, Chen R Z.J Mater Eng, 1997; (8): 3 |
| [20] | (李嘉荣, 唐定中, 陈荣章. 材料工程, 1997; (8): 3) |
| [21] | Darolia R, Lahrman D F, Field R D.In: Reichman S, Duhl D N, Maurer S, Antolovich S, Lund C eds., Superalloys 1988, Warrendale, PA: The Minerals, Materials and Metals Society, 1988: 255 |
| [22] | Walston W S, Schaeffer J C, Murphy W H.In: Kissinger R D, Deye D J, Anton D L, Cetel A D, Nathal M V, Pollock T M, Woodford D A eds., Superalloys 1996, Warrendale, PA: The Minerals, Materials and Metals Society, 1996: 9 |
| [23] | Walston W S, O'Hara K S, Ross E W, Pollock T M, Murphy W H. In: Kissinger R D, Deye D J, Anton D L, Cetel A D, Nathal M V, Pollock T M, Woodford D A eds., Superalloys 1996, Warrendale, PA: The Minerals, Materials and Metals Society, 1996: 27 |
| [24] | Pollock T M, Murphy W H, Goldman E H, Uram D L, Tu J S.In: Antolovich S D, Stusrud R W, MacKay R A, Anton D L, Khan T, Kissinger R D, Klarstrom D L eds., Superalloys 1992, Warrendale, PA: The Minerals, Materials and Metals Society, 1992: 125 |
| [25] | Kong Y H, Chen Q Z.Mater Sci Eng, 2004; A366: 135 |
/
| 〈 |
|
〉 |