EFFECT OF Fe-RICH PHASE PARTICLES WITH DIFFER-ENT CONCENTRATIONS ON THE BENDABILITYOF Al-Mg-Si-Cu SERIES ALLOYS
Received date: 2015-04-14
Online published: 2016-03-17
Supported by
Supported by National High Technology Research and Development Program of China (No.2013-AA032403), National Natural Science Foundation of China (Nos.51571023 and 51301016), Fundamental Research Funds for the Central Universities (NoFRF-TP-15-051A3) and Constructed Project for Key Laboratory of Beijing (No FRF-SD-B-005B)
通过弯边变形, 拉伸实验, OM, SEM和TEM观察等手段研究了不同浓度富Fe相粒子对Al-Mg-Si-Cu系合金板材弯边性能的影响规律. 结果表明, 随着富Fe相浓度增加, 合金板材沿纵横向的弯边性能存在较大差异, 不含富Fe相粒子的合金板材沿2个方向弯边变形180°后外表面粗糙度增加, 处于中等浓度(含0.2%Fe)时沿2个方向弯边变形后均具有优异的外表面质量, 但是随着富Fe相浓度的进一步增加(至0.5%Fe), 合金板材沿横向弯边变形后在外表面出现微裂纹. 虽然富Fe相粒子浓度增加对合金板材纵横向延伸率影响不大, 但是拉伸断口,弯边和拉伸断裂后的侧表面组织均表明, 不含富Fe相的合金板材弯边变形后外表面粗糙度增加与剪切带组织密切相关, 而含有较高浓度富Fe相粒子的合金板材弯边变形后外表面出现的微裂纹与粗大富Fe相粒子的尺寸,形态以及分布状态密切相关. 此外, 根据不同浓度富Fe相粒子与合金弯边性能间的定量关系, 提出了合金弯边变形后外表面粗糙度增加和微裂纹形成的模型示意图.
关键词： Al-Mg-Si-Cu合金; 富Fe相; 弯边性能; 剪切带; 模型
邢辉 , 郭明星 , 汪小锋 , 张艳 , 张济山 , 庄林忠 . 不同浓度富Fe相粒子对Al-Mg-Si-Cu系合金弯边性能的影响*[J]. 金属学报, 2016 , 52(3) : 271 -280 . DOI: 10.11900/0412.1961.2015.00220
The influence of Fe-rich phase particle with different contents on the bendability of the Al-Mg-Si-Cu alloys was investigated by means of bending and tensile tests, OM, SEM and TEM characterization. The results reveal that, with the increase of Fe-rich phase particle content, the bendability of the alloy sheets in the longitudinal and transverse directions was quite different, and the outer surface of the alloy sheets after bending of 180° along the two directions became much rough, especially along the transverse direction. When the Fe-rich phase concentration increased to the medium level (0.2%Fe), the quality of outer surface after bending was very good. With further increasing Fe-rich phase to the high level (0.5%Fe), micro cracks were produced after bending along the transverse direction. Although increasing Fe-rich phase concentration did not give a great effect on the elongation of the alloys in the two directions, according to the tensile fracture and microstructure in the slid surface of the specimen after bending or tension test, the roughening of outer surface of the alloy sheet without Fe-rich phase was closely related with the formation of shear bands, while for the alloy sheet with high concentration of Fe-rich phases, the formation of micro cracks after bending was mainly related with the size, morphology and distribution of coarse Fe-rich phases. In addition, based on the quantitative relationship between Fe-rich phase concentration and bendability of the alloy sheets, the models of outer surface roughening and micro cracks forming during bendingare proposed.
Key words： Al-Mg-Si-Cu alloy; Fe-rich phase; bendability; shear band; modelling
| [1] | Miller W S, Zhuang L, Bottema J, Wittebrood A J, De Smet P, Haszler A, Vieregge A.Mater Sci Eng, 2000; A280: 37 |
| [2] | Wang D.Shanghai Nonferrous Met, 2013; 34(3): 130 |
| [2] | (王丹. 上海有色金属, 2013; 34(3): 130) |
| [3] | Wang M J, Huang D Y, Jiang H T.Heat Treatment Met, 2006; (09): 34 |
| [3] | (王孟君, 黄电源, 姜海涛. 金属热处理, 2006; (09): 34) |
| [4] | Sun J.Tech Educ, 2010; (02): 26 |
| [4] | (孙静. 技术与教育, 2010; (02): 26) |
| [5] | Liu Y W, Wang S W.Auto Engineer, 2011; (02): 50 |
| [5] | (刘伟燕, 王书伟. 汽车工程师, 2011; (02): 50) |
| [6] | Zhang Q X, Guo M X, Hu X Q, Cao L Y, Zhuang L Z, Zhang J S.Acta Metall Sin, 2013; 49: 1604 |
| [6] | (张巧霞, 郭明星, 胡晓倩, 曹零勇, 庄林忠, 张济山. 金属学报, 2013; 49: 1604) |
| [7] | Cui L, Guo M X, Peng X Y, Zhang Y, Zhang J S, Zhuang L Z.Acta Metall Sin, 2015; 51: 289 |
| [7] | (崔莉, 郭明星, 彭祥阳, 张艳, 张济山, 庄林忠. 金属学报, 2015; 51: 289) |
| [8] | Wang A D. Master Thesis, Dalian University of Technology, 2011 |
| [8] | (王安东. 大连理工大学硕士学位论文, 2011) |
| [9] | Wang X F, Guo M X, Cao L Y, Luo J R, Zhang J S, Zhuang L Z.Mater Sci Eng, 2015; A621: 8 |
| [10] | Sarkar J, Kutty T R G, Wilkinson D S, Embury J D, Lloyd D J.Mater Sci Eng, 2004; A369: 258 |
| [11] | Itoh G, Suzuki T, Horikawa K. Mater Sci Forum, 2002; 396-402: 1193 |
| [12] | Hirth S M, Marshall G J, Court S A, Lloyd D J. Mater Sci Eng, 2001; A319-321: 452 |
| [13] | Datsko J, Yang C T.J Eng Ind, 1960; 82: 309 |
| [14] | Davidkov A, Petrov R H, Smet P D, Schepers B, Kestens L A I.Mater Sci Eng, 2011; A528: 7068 |
| [15] | Castany P, Diologent F, Rossoll A, Despois J F, Bezen?on C, Mortensen A.Mater Sci Eng, 2013; A559: 558 |
| [16] | Mulazimoglu M, Zaluska A, Gruzleski J, Paray F.Metall Mater Trans, 1996; 27A: 929 |
| [17] | Allen C M, O'Reilly K A Q, Cantor B, Evans P V.Prog Mater Sci, 1998; 43: 89 |
| [18] | Tanihata H, Sugawara T, Matsuda K, Ikeno S.J Mater Sci, 1999; 34: 1205 |
| [19] | Couper M J, Rinderer B, Yao J Y. Mater Sci Forum, 2006; 519-521: 303 |
| [20] | Peng X Y, Guo M X, Wang X F, Cui L, Zhang J S, Zhuang L Z.Acta Metall Sin, 2015; 51: 169 |
| [20] | (彭祥阳, 郭明星, 汪小锋, 崔莉, 张济山, 庄林忠. 金属学报, 2015; 51: 169) |
| [21] | Wang X F, Guo M X, Chapuis A, Luo J R, Zhang J S, Zhuang L Z.Mater Sci Eng, 2015; A644: 137 |
| [22] | Lievers W B, Pilkey A K, Worswick M J.Mech Mater, 2003; 35: 661 |
| [23] | Lloyd D J, Weatherly G C, Perovic D D.In: Subodh K Das ed., Proceedings of Symposium: Automotive Alloys 1999, San Diego: TMS, 2000: 211 |
| [24] | Lv D. Master Thesis, Lanzhou University of Technology, 2009 |
| [24] | (吕丹. 兰州理工大学硕士学位论文, 2009) |
| [25] | Fan X G.PhD Dissertation, Harbin Institute of Technology, 2007 |
| [25] | (樊喜刚. 哈尔滨工业大学博士学位论文, 2007) |
/
| 〈 |
|
〉 |