经新型Q－P－T工艺处理后Q235钢的组织与性能

贾晓帅; 左训伟; 陈乃录; 黄坚; 唐新华; 戎咏华

doi:10.3724/SP.J.1037.2012.00351

金属学报 >

2013 , Vol. 49 >Issue 1: 35 - 42

DOI: https://doi.org/10.3724/SP.J.1037.2012.00351

论文

经新型Q－P－T工艺处理后Q235钢的组织与性能

贾晓帅 ,
左训伟 ,
陈乃录 ,
黄坚 ,
唐新华 ,
戎咏华

展开

1.上海交通大学材料科学与工程学院, 上海 200240
2.上海交通大学机械与动力工程学院, 上海 200240

贾晓帅, 男, 1985年生, 博士生

收稿日期: 2012-06-13

修回日期: 2012-10-25

网络出版日期: 2013-01-11

基金资助

国家自然科学基金重点资助项目51031001

收起

MICROSTRUCTURE AND PROPERTIES OF Q235 STEEL TREATED BY NOVEL Q-P-T PROCESS

JIA Xiaoshuai ,
ZUO Xunwei ,
CHEN Nailu ,
HUANG Jian ,
TANG Xinhua ,
RONG Yonghua

Expand

1. School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240
2. School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai 200240

Received date: 2012-06-13

Revised date: 2012-10-25

Online published: 2013-01-11

Fold

摘要

研究了最低屈服强度为235 MPa的Q235钢经新型淬火－分配－回火(Q－P－T)工艺处理后的力学性能和焊接性能. 结果表明, 经Q－P－T处理后的Q235钢(QPT235钢)强度得到了大幅度的提升: 屈服强度和抗拉强度分别达到435和 615 MPa. 采用相同焊料和焊接工艺, QPT235钢焊接接头的力学性能比Q235钢显著提高, 前者的抗拉强度约为532 MPa, 延伸率约为16.7%, 而后者的抗拉强度约为414 MPa,延伸率约为12.4%. 显微组织观察揭示了QPT235钢性能改善的原因: QPT235钢焊接热影响区中铁素体晶粒和珠光体层片显著细化, 并避免了魏氏组织的大量出现; 在QPT235钢的母材和热影响区中均存在硬相马氏体、贝氏体和软相残留奥氏体的复合组织, 取代了Q235钢中部分的铁素体和珠光体.

关键词： 淬火－分配－回火(Q－P－T)工艺; 力学性能; 焊接接头; 微观组织; 组织细化

本文引用格式

贾晓帅 , 左训伟 , 陈乃录 , 黄坚 , 唐新华 , 戎咏华 . 经新型Q－P－T工艺处理后Q235钢的组织与性能[J]. 金属学报, 2013 , 49(1) : 35 -42 . DOI: 10.3724/SP.J.1037.2012.00351

Abstract

This paper presents the mechanical properties and welding properties of Q235 steel with minimum yield strength of 235 MPa treated by a novel quenching－partitioning－tempering (Q-P-T) process.The experiments indicate that the strengths of Q-P-T treated Q235 steel (briefly called QPT235 steel) markedly raise compared with Q235 steel, and its yield strength and tensile strength are 435 and 615 MPa, respectively. In addition, the mechanical properties of the welding joint of QPT235 steel are markedly improved compared with Q235 steel when the same welding solder and process are performed for the steel with the two treatments, and the tensile strength and elongation of the former are about 532 MPa and 16.71%, respectively, while those of the latter are about 414 MPa and 12.4%. The microstructural characterization reveals two main factors resulting in the mechanical properties of QPT235 steel superior to those of Q235 steel: the grains of ferrite and interlamellar spacing of pearlite are both refined in the welding heat affected zone (HAZ), and a lot of widmanstatten structures in the welding joint of Q235 steel is avoided for QPT235 steel; there is a mixed microstructure of hard phases of martensite and bainite as well as remained austenite as soft phase in both base metal and HAZ, which replace parts of ferrite and pearlite in Q235 steel.

Key words：

quenching-partitioning-tempering (Q-P-T) process

; mechanical property; welding joint; microstructure; refinement

参考文献

[1] Xu Z Y. In: Xue Q J ed., The Perspective of Chemical Industry, Metallurgy and Materials,Beijing: Chemical Industry Publishing House, 2007: 403

(徐祖耀. 见: 薛群基主编, 中国工程院化工、冶金与材料工程学部第六届学术会议特邀报告会议论文集,北京: 化学与工业出版社, 2007: 403)

[2] Xu Z Y. Heat Treat, 2008; 23(2): 1

(徐祖耀. 热处理, 2008; 23(2): 1)

[3] Shang C J, Hu L J, Yang S W, Wang X M, Zhao Y T, He X L. Acta Metall Sin, 2005; 41: 471

(尚成嘉, 胡良均, 杨善武, 王学敏, 赵运堂, 贺信莱. 金属学报, 2005; 41: 471)

[4] Liu D S, Cheng B G, Chen Y Y. Acta Metall Sin, 2012; 48: 334

(刘东升, 程丙贵, 陈圆圆. 金属学报, 2012; 48: 334)

[5] Qi J J, Yang W Y, Sun Z Q. Acta Metall Sin, 2002; 38: 629

(齐俊杰, 杨王玥, 孙祖庆. 金属学报, 2002; 38: 629)

[6] Matlock D K, Speer J G. In: Lee H C ed., The 3rd Int Conf on Advanced Structural Steels,

Korea: The Korean Institute of Metals and Materials, 2006: 774

[7] Mileiko S T, Speer J G. J Mater Sci, 1969; 4: 974

[8] Speer J G, Matlock D K, Cooman B C, Schroth J G. Acta Mater, 2003; 51: 2661

[9] Sakuma Y. In: Baker M A ed., Proc Int Conf on Advanced High Strength Sheet Steels for Automotive

Applications, Warrendale: Association for Iron－Steel Technology, 2004: 11

[10] Sugimoto K, Kobayshi M, Hashimoto S Y. Metall Trans, 1992; 23: 2085

[11] Speer J G, Assuncao F C R, Matlock D K, Edmonds D V. Mater Res, 2005; 8: 417

[12] Hsu T Y. Mater Sci Forum, 2007; 561: 2283

[13] Wang X D, Zhong N, Rong Y H, Xu Z Y. J Mater Res, 2009; 24: 261

[14] Zhang K, Xu W Z, Guo Z H, Rong Y H, Wang M Q, Dong H. Acta Metall Sin, 2011; 47: 489

(张柯, 许为宗, 郭正洪, 戎咏华, 王毛球, 董瀚. 金属学报, 2011; 47: 489)

[15] Zhong N, Wang X D, Wang L, Rong Y H. Mater Sci Eng, 2009; A506: 111

[16] Chen N L, Rong Y H. Chin Pat, 10562008.9, 2010

(陈乃录, 戎咏华. 中国专利, 10562008.9, 2010)

[17] Zhou S, Zhang L, Chen N L, Gu J F, Rong Y H. ISIJ Int, 2011; 51: 1688

[18] Liu H P, Lu X W, Jin X J. Mater Des, 2011; 32: 2269

[19] Wang C L. Metal Fracture Analysis. Harbin: Harbin University Press, 1998: 4

(王长利. 金属断口分析. 哈尔滨: 哈尔滨工业大学出版社, 1998: 4)

[20] Peng Y, Wang A H, Xiao H J, Tian Z L. Acta Metall Sin, 2012; 48: 1281

(彭云, 王爱华, 肖红军, 田志凌. 金属学报, 2012; 48: 1281)

[21] Zhao L, Zhang X D, Chen W Z. Acta Metall Sin, 2005; 41: 392

(赵琳, 张旭东, 陈武柱. 金属学报, 2005; 41: 392)

Options

文章导航

模态框（Modal）标题

摘要

本文引用格式

Abstract

参考文献