定向凝固多孔铜热沉传热性能的理论分析
收稿日期: 2012-05-14
修回日期: 2012-07-19
网络出版日期: 2012-11-11
基金资助
国家自然科学基金项目U0837603和51101092资助
THEORETICAL STUDY ON HEAT TRANSFER PERFORMANCE OF DIRECTIOANLLY SOLIDIFIED POROUS COPPER HEAT SINK
Received date: 2012-05-14
Revised date: 2012-07-19
Online published: 2012-11-11
Supported by
Supported by National Natural Science Foundation of China (Nos.u0837603 and 51101092)
对定向凝固多孔Cu热沉的传热性能进行理论分析和预测, 并将定向凝固多孔Cu热沉传热性能的理论预测结果与实验结果进行了比较. 结果表明, 将定向凝固多孔Cu热沉单元进行肋片等效, 由于实际热沉所用多孔Cu结构与其理想结构存在偏差, 理论预测结果远高于实验结果; 引入通孔率和通孔孔径对理论预测结果进行修正后, 理论预测结果与实验结果吻合. 定向凝固多孔Cu的结构是影响热沉传热性能的根本因素, 根据理论分析, 沿孔长方向长度为20 mm时, 具有优异传热性能的热沉的定向多孔Cu部分应具有如下结构: 孔径0.1-0.6 mm; 气孔率30%-70%; 高度≧4 mm.
陈刘涛 张华伟 刘源 李言祥 . 定向凝固多孔铜热沉传热性能的理论分析[J]. 金属学报, 2012 , 48(11) : 1374 -1380 . DOI: 10.3724/SP.J.1037.2012.00271
Porous copper with long cylindrical pores fabricated by unidirectional solidification of metal-gas eutectic system can be used to manufacture a special kind of micro-channel heat sink. In order to simplify the heat transfer analysis, a fin model was introduced into the theoretical study on heat transfer performance of directionally solidified porous copper heat sink. The heat transfer performance of porous copper heat sink was also tested by experiments, and it was found that experimental values are far less than theoretical predicted ones. That is because the structure of porous copper might deviate from its ideal structure, such as, some pores are not penetrated, and the distribution of pore size and pore location is not uniform. After the model was modified by introducing area ratio of penetrating pores and mean diameter of penetrating pores, the theoretical results were consistent with the experimental results. Thus the analytical method based on the fin model in this paper can be used to predict the heat transfer performance of directionally solidified porous copper heat sink. According to the theoretical analysis, porous copper used for heat sink with excellent heat transfer performance should have the following porous structure: the pore diameter is 0.1-0.6 mm, the porosity is 30%-70%, the height of porous copper is more than 4 mm when its length along the direction of pore axis is 20 mm.
[1] Mahajan R, Nair R, Wakharkar V, Swan J, Tang J, Vandentop G. Int Technol J Semicond Technol Manuf, 2002; 6: 61
[2] Tuckerman D B, Pease R F W. IEEE Electron Dev Lett, 1981; 2: 126
[3] Rosa P, Karayiannis T G, Collins M W. Appl Therm Eng, 2009; 29: 3447
[4] Wei X J. J Electron Packag, 2004; 126: 60
[5] Ogushi T, Chiba H, Nakajima H, Ikeda T. J Appl Phys, 2004; 95: 5843
[6] Chiba H, Ogushi T, Nakajima H, Torji K, Tomimura T, Ono F. J Appl Phys, 2008; 103: 013515
[7] Liu Y, Li Y X, Zhang H W, Wang J. Acta Metall Sin, 2005; 41: 886
(刘源, 李言祥, 张华伟, 万疆. 金属学报, 2005; 41: 886)
[8] Liu Y, Li Y X, Wan J, Zhang H W. Mater Sci Eng, 2005; A402: 47
[9] Zhang H W, Li Y X, Liu Y. Acta Metall Sin, 2006; 42: 1165
(张华伟, 李言祥, 刘源. 金属学报, 2006; 42: 1165)
[10] Li Y X, Liu Y, Zhang H W, Wang X. In: Nakajima H, Kanetake N eds., Proc Met Foam 2005, Sendai: The Japan Institute of Metals, 2006: 237
[11] Zhang H W, Li Y X, Liu Y. Acta Metall Sin, 2006; 42: 1171
(张华伟, 李言祥, 刘 源. 金属学报, 2006; 42: 1171)
[12] Wang X, Li Y X, Liu Y. Acta Metall Sin, 2006; 42: 1075
(王雪, 李言祥, 刘源. 金属学报, 2006; 42: 1075)
[13] Ogushi T, Chiba H, Nakajima H. In: Nakajima H, Kanetake N eds., Proc Met Foam 2005, Sendai: The Japan Institute of Metals, 2006: 27
[14] Chiba H, Ogushi T, Nakajima H. In: Nakajima H, KanetakeN eds., Proc Met Foam 2005, Sendai: The Japan Institute of Metals, 2006: 35
[15] Chen L T, Zhang H W, Liu Y, Li Y X. Acta Metall Sin, 2012: 48: 329
(陈刘涛, 张华伟, 刘源, 李言祥. 金属学报, 2012: 48: 329)
[16] Yang S M, Tao W Q. Heat Transfer. 4th Ed, Beijing: Higher Education Press, 2006: 57
(杨世铭, 陶文铨. 传热学. 第4版, 北京: 高等教育出版社, 2006: 57)
[17] Shah R K, London A L. Laminar Flow Forced Convection In Ducts. New York: Academic Press, 1978: 148
[18] Li X Q, Li Y, Ding T. Engineering Fluid Mechanics. Beijing: China Water Power Press, 2009: 120
(李小芹, 李 岩, 丁 涛. 工程流体力学. 北京: 中国水利水电出版社, 2009: 120)
/
| 〈 |
|
〉 |