不同酸溶液中制备纳米结构MnO2单晶
收稿日期: 2010-02-11
修回日期: 2010-04-28
网络出版日期: 2010-07-11
基金资助
国家自然科学基金项目50762003和海南省自然科学基金项目807009资助
PREPARATION OF NANOSTRUCTURE MnO$_{\bf 2}$ SINGLE CRYSTAL IN VARIOUS ACID SOLUTION
Received date: 2010-02-11
Revised date: 2010-04-28
Online published: 2010-07-11
Supported by
Supported by National Natural Science Foundation of China (No.50762003) and Natural Science Foundation of Hainan Province (No.807009)
陈永 , 洪玉珍 , 马艳平 , 杨昊 , 李健保 . 不同酸溶液中制备纳米结构MnO2单晶[J]. 金属学报, 2010 , 46(7) : 857 -861 . DOI: 10.3724/SP.J.1037.2010.00088
Nanostructure MnO2 single crystal was prepared through redox reactions of potassium permanganate in different inorganic acid (hydrochloric acid, sulfuric acid and nitric acid) and organic acid (acetate). The products were characterized by TEM and XRD. It indicated that the crystal structure and morphology of the synthesized MnO2 can be tailored by adjusting the pH value in solution and reaction temperature. It was also found that layer folded δ-MnO2 microspheres were obtained at low reaction temperature and low hydrochloric acid concentration, whereas α-MnO2 single-crystal nanorods were fabricated with increased reaction temperature and hydrochloric acid concentration. The possible formation mechanism of δ-MnO2 microspheres and α-MnO2 nanorods is also discussed.
Key words： MnO2; nanostructures; redox reaction
[1] Liao M Y, Lin J M, Wang J H, Yang C T, Chou T L, Mok B H. Electrochem Commun, 2003; 5: 312
[2] Reddy R N, Reddy R G. J Power Sources, 2004; 132: 315
[3] Ataherian F, Zolfaghari A, Jafari S M, Ghaemi M. Electrochim Acta, 2008; 53: 4607
[4] Park M S, Yoon W Y. J Power Sources, 2003; 114: 237
[5] Manickam M, Singh P, Issa T B, Thurgate S, Marco R D. J Power Sources, 2004; 130: 254
[6] Sugantha M, Ramakrishnan P A, Hermann A M, Warmsingh C P, Ginley D S. Int J Hydrogen Energy, 2003; 28: 597
[7] Ghaemi M, Gholami A, Moghaddam R B. Electrochim Acta, 2008; 53: 3250
[8] Reddy A L M, Shaijumon M M, Gowda S R, Ajayan P M. Nano Lett, 2009; 9: 1002
[9] Devaraj S, Munichandraiah N. J Phys Chem, 2008; 112C: 4406
[10] Wang X, Li Y D. J Am Chem Soc, 2002; 124: 2880
[11] Wang X, Li Y D. Chem Eur J, 2003; 9: 300
[12] Xiao T D, Bokhimi X, Benaissa M, Perez R, Strutt P R, Yacaman M J. Acta Mater, 1997; 45: 1685
[13] Yuan Z Y, Zhang Z, Du G, Ren T Z, Su B L. Chem Phys Lett, 2003; 378: 349
[14] Wang X, Li Y. J Am Chem Soc, 2002; 124: 2880
[15] Zhang Y, Chen L, Zheng Z, Yang F. Solid State Sci, 2009; 11: 1265
[16] Huang X, Lv D, Yue H, Attia A, Yang Y. Nanotechnology, 2008; 19: 225606
[17] Wei M, Konishi Y, Zhou H, Sugihara H, Aiakawa H. Nanotechnology, 2005; 16: 245
[18] Chen Y, Liu C, Li F, Cheng H M. J Alloys Compd, 2005; 397: 282
[19] Chen Y, Hong Y, Ma Y, Li J. J Alloys Compd, 2010; 490: 331
[20] Kijima N, Yasuda H, Sato T, Yoshimura Y. J Solid State Chem, 2001; 159: 94
[21] Muraoka Y, Chiba H, Atou T, Kikuchi M, Hiraga K, Syono Y. J Solid State Chem, 1999; 144: 136
/
| 〈 |
|
〉 |