论文

定向凝固NiAl-Cr(Mo)-Hf(Ho)共晶合金的组织与性能

  • 肖旋 ,
  • 郭建亭 ,
  • 谢亿
展开
  • 1. 沈阳理工大学材料科学与工程学院; 沈阳 110168
    2. 湖南省电力公司试验研究院; 长沙 410007
    3. 中国科学院金属研究所; 沈阳 110016
肖璇, 女, 1966年生, 副教授

收稿日期: 2009-10-10

  修回日期: 2010-03-19

  网络出版日期: 2010-06-11

MICROSTRUCTURES AND MECHANICAL PROPERTIES OF DIRECTIONALLY SOLIDIFIED NiAl–Cr(Mo)–Hf(Ho) EUTECTIC ALLOY

  • XIAO Xuan ,
  • GUO Jian-Ting ,
  • XIE Yi
Expand
  • 1. School of Materials Science and Engineering; Shenyang Ligong University; Shenyang 110168
    2. Hunan Electric Power Test and Research Institute; Changsha 410007
    3. Institute of Metal Research; Chinese Academy of Sciences; Shenyang 110016

Received date: 2009-10-10

  Revised date: 2010-03-19

  Online published: 2010-06-11

摘要

通过液态金属冷却技术制备了名义成分为Ni-30.4Al-34Cr-4.3Mo-0.1Hf-0.05Ho(原子分数, \%)的定向合金. 定向凝固工艺消除了普通铸造合金中的初生Cr(Mo)相, 获得了共晶组织. 随抽拉速率从8 mm/min提高到15 mm/min, 合金中的共晶胞尺寸从115 μm减小到85 μm, 共晶胞间距变窄, 胞间混乱区减少. 与普通铸造相比,定向凝固工艺能提高该共晶合金的室温、高温拉伸强度, 高温拉伸塑性以及室温断裂韧度,并且定向合金的上述力学性能随抽拉速率增大而增大.

本文引用格式

肖旋 , 郭建亭 , 谢亿 . 定向凝固NiAl-Cr(Mo)-Hf(Ho)共晶合金的组织与性能[J]. 金属学报, 2010 , 46(6) : 701 -707 . DOI: 10.3724/SP.J.1037.2009.00668

Abstract

The alloy with nominal composition of Ni-30.4Al-34Cr-4.3Mo-0.1Hf-0.05Ho (atomic fraction, %) has been directionally solidified at two withdrawal rates by liquid metal (Sn) cooling (LMC) process. Compared to the as-cast alloy, directional solidification process eliminates primary Cr(Mo) phase. With increasing withdrawal rate from 8 to 15 mm/min, the diameter of NiAl/Cr(Mo) eutectic cell decreases from 115 to 85 μm. In addition, the intercellular spaces and disordered regions become less. In virtue of the disappearance of primary Cr(Mo) phase, the mechanical properties of directionally solidified alloys are better than those of as--cast alloy and are further improved with increasing withdrawal rate.

参考文献

[1] Noebe R D, Bowman R R, Nathal N V. Int Mater Rev, 1993; 38: 193
[2] Miracle D B. Acta Metall Mater, 1993; 41: 649
[3] Johnson D R, Oliver B F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3: 493
[4] Yang J M, Jeng S M, Bain K, Amato R A. Acta Metall Mater, 1997; 45: 295
[5] Johnson D R, Chen X F, Oliver B F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3: 99
[6] Walter J L, Cline H E. Metall Trans, 1970; 1: 1221
[7] Cline H E, Walter J L. Metall Trans, 1970; 1: 2907
[8] Cline H E, Walter J L, Lifshine E, Russell R R. Metall Trans, 1971; 2: 189
[9] Chen X F, Johnson D R, Noebe R D, Oliver B F. J Mater Res, 1995; 10: 1159
[10] Raj S V, Locci I E. Intermetallics, 2001; 9: 217
[11] Whittenberger J D, Raj S V, Locci I E, Salem J A. Intermetallics, 1999; 7: 1159
[12] Raj S V, Locci I E, Salem J A, Pawlik R J. Metall Mater Trans, 2002; 33A: 597
[13] Jachson K H, Hunt J D. Trans Metall Soc AIME, 1966; 236: 1129
[14] Whittenberger J D, Locci I E, Darolia R, Bowman R R. Mater Sci Eng, 1999; A268: 165
[15] Takeyama M, Liu C T. J Mater Res, 1990; 5: 1189
[16] Guo J T, Cui C Y, Qi Y H, Ye H Q. J Alloys Compd, 2002; 343: 142
[17] Guo J T, Huai K W, Gao Q, Ren W L, Li G S. Intermetallics , 2007; 15: 727
[18] Ren W L, Guo J T, Li G S, Zhou J. Mater Lett, 2003; 57: 1374

文章导航

/