金属学报  1998, Vol. 34 Issue (5): 552-560

论文 本期目录 | 过刊浏览 |

[011]多滑移取向铜单晶体的循环形变行为──Ⅱ.表面滑移特征及形变带

李小武;王中光;孙守光;吴世丁;李守新;李广义

中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015;中国北方交通大学力学工程系;北京;100044;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015

CYCLIC DEFORMATION BEHAVIOR OF [011]MULTIPLE-SLIP-ORIENTED COPPER SINGLE CRYSTALS Ⅱ. Surface Slip Features and Deformation Bands

(LI Xiaowu; WANG Zhongguang; SUN Shouguang; WU Shiding; LI Shouxin;LI Guangyi (State Key Laboratory for Fatigue and Fracture of Materials; Institute of Metal Research; The Chinese Academy of Sciences; Shenyang 110015)(Department of Mechanical Engineering; Northern Jiaotong University; Beijing 100044)

李小武;王中光;孙守光;吴世丁;李守新;李广义. [011]多滑移取向铜单晶体的循环形变行为──Ⅱ.表面滑移特征及形变带[J]. 金属学报, 1998, 34(5): 552-560.
, , , , , . CYCLIC DEFORMATION BEHAVIOR OF [011]MULTIPLE-SLIP-ORIENTED COPPER SINGLE CRYSTALS Ⅱ. Surface Slip Features and Deformation Bands[J]. Acta Metall Sin, 1998, 34(5): 552-560.

摘要 参考文献 相关文章 Metrics 全文: PDF(4041 KB)   摘要: 本文系统研究了[011]多滑移取向铜单晶体在不同塑性应变幅下循环饱和后的表面滑移特征.结果表明，[011]多滑移取向铜单晶体的疲劳极限低于[001]多滑移取向铜单晶体.当应变幅γpl≥2.5×10－3时，表面出现两种宏观形变带（DBI和DBII）；它们呈严格的正交关系，其形成可能与循环加载中产生的不可逆晶体旋转密切相关.当应变幅γpl≥5.0×10－3时，表面还出现DBIII形变带，其惯习面为（001）；此类形变带的出现是［011］单晶体在高应变幅下循环达到峰值应力后出现明显循环软化现象的根本原因 关键词 ： [011]多滑移取向铜单晶体,  循环形变,  形变带,  晶体旋转     Abstract：Surface deformation features were investigated on [011] multiple-slip-oriented copper single crystals under different strain amplitudes. It is shown that the fatigue limit of [011]multiple-slip-oriented copper single crystal is lower than that of [001] multiple-slip-oriented copper single crystal. For γpl≥2.5×10-3, two types of deformation bands (DBI and DBII)formed on the specimen surface and their habit planes are perpendicular to each other strictly.This may be caused by the occurrence of irreversible rotation of crystal under cyclic loading. For γpl ≥5.0×10-3, another type of deformation band (DBIII) forms on the specimen surface and its habit plane is (001). The occurrence of the obvious cyclic softening processes, in cyclically deformed [011] copper single crystals with high strain amplitudes, was largely attributed to the Key words： [011] multiple-slip-oriented copper single crystal    cyclic deformation    deformation band    rotation of crystal 收稿日期: 1998-05-18      基金资助:国家自然科学基金!19392300－4和19402001 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 李小武 王中光 孙守光 吴世丁 李守新 李广义 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1998/V34/I5/552 1 Saletore M,Taggart R.Mater Sci Eng,1978;36:259 2 李小武,王中光,孙守光,吴世丁,李守新,李广义.金属学报,1998; 34:545(Li Xiaowu,Wang Zhangguang,Sun Shouguang,Wu Shiding,Li Shouxin .Li Guangyi.Acta Metall Sin,1998; 34:545) 3 Mughrabi H. Mater Sci Eng, 1978 33: 207 4 Gong B, Wang Z R, Wang Z G. Acta Mater, 1997 45: 1365 5 Barrett C S,Levenson L H.Trans Metall Soc AIME,1939;135:327 6 Barrett C S,Levenson L H.Trans Metall Soc AIME,1939;137:112 7 Honeycombe R K W. J Inst Met, 1951-1952 80: 45 8 Calnan E A.Acta Crystallogr,1952 ;5:557 9 Gostelow C R. Met Sci J, 1971;5: 177 10 Gong B, Wang Z G, Zhang Y W Mater Sci Eng, 1995; A194: 171 11 Li S X, Gong B, Wang Z G Scr Metall Mater, 1994 31: 1729 12 宫波,王中光,张轶伟,李广义,张天宜.金属学报,1994;30:439(Gong Bo, Wang Zhongguang, Zhang Yiwei, Li Guangyi, Zhang Tanyi. Acta Metall Sin, 1994 30: 439) 13 Vorren O, Ryum N Acta Metall, 1988; 36: 1443 14 Crocker A G, Abell J S、 Philos Mag, 1976 33: 305 15 Zhai T, Martin J W, Briggs G A D. Acta Metall Mater. 1995: 43: 3813 16 Zhai T, Martin J W, Briggs G A D, Wilkinson A J Acta Mater, 1996: 44: 3477 17 Suresh S.Fatigue of Materials London:Cambridge University Press,1991 18 Li X W, Hu Y M, Wang Z G Mater Sci Eng, 1998; in press 19 Reid C N. Deformation Geometry for Materials Scientists. Oxford: Pergamon Press, 1973 20 Villechaise P,Mendez J,Violan P. Acta Metall Mater,1991; 39:1683 [1] 郭廷彪, 李琦, 王晨, 张锋, 贾智. 单晶Cu等通道转角挤压A路径形变特征及力学性能[J]. 金属学报, 2017, 53(8): 991-1000. [2] 杨军 贺志荣 王芳 王永善. Cr掺杂对Ti-Ni形状记忆合金相变和循环形变特性的影响[J]. 金属学报, 2011, 47(2): 157-162. [3] 杨瑞青; 李守新; 李广义; 张哲峰 . 不同取向疲劳态铜单晶高速冲击下的绝热剪切带[J]. 金属学报, 2006, 42(3): 245-250 . [4] 陈常强; 李守新; 李广义; 艾素华 . 低氢含量工业纯钛循环变形的微观结构 I．[J]. 金属学报, 2004, 40(3): 235-240 . [5] 陈常强; 李守新; 李广义; 艾素华 . 低氢含量工业纯钛循环变形的微观结构II.[J]. 金属学报, 2004, 40(3): 241-244 . [6] 黄崇湘; 吴世丁; 李广义; 刘腾; 姜传斌; 李守新 . 循环形变对超细晶铜室温拉伸行为的影响[J]. 金属学报, 2004, 40(11): 1165-1169 . [7] 李勇; 李守新; 李广义 . 晶粒组元沿晶界旋转的铜双晶在循环变形中的滑移形貌与位错组态[J]. 金属学报, 2002, 38(8): 819-824 . [8] 陆永浩; 乔利杰; 褚武扬 . Cu-Ni-Al形状记忆合金形变、相变以及裂纹形核的相互关系[J]. 金属学报, 2001, 37(7): 686-690 . [9] 吴世丁; 王中光; 李广义 . 亚微米铜循环形变特征研究[J]. 金属学报, 1999, 35(9): 960-963 . [10] 吴细毛; 王中光; 李广义 . [112]-Cu-7Al单晶体循环形变行为Ⅰ.应变突发行为[J]. 金属学报, 1999, 35(8): 789-792 . [11] 吴细毛; 王中光; 李广义 . [112]Cu-7Al单晶体循环形变行为 Ⅱ.循环形变特征[J]. 金属学报, 1999, 35(8): 793-795 . [12] 张萌; 杨平生; 刘炎; 谈育煦 . 冲击疲劳循环形变阶段的晶界行为[J]. 金属学报, 1999, 35(7): 703-706 . [13] 吴细毛; 王中光; 李广义 . [123]Cu-16Al单晶循环形变的不稳定性 II.循环形变行为[J]. 金属学报, 1999, 35(7): 711-714 . [14] 吴细毛; 王中光 . [123]Cu-16Al单晶循环形变的不稳定性 I.应变突发行为[J]. 金属学报, 1999, 35(7): 707-710 . [15] 李小武; 王中光; 李守新 . 循环变形铜单晶体的滞后回线形状变化与驻留滑移带的萌生[J]. 金属学报, 1999, 35(6): 594-599 . Viewed Full text Abstract Cited   Shared      Discussed