金属学报  2005, Vol. 41 Issue (3): 245-250

论文 本期目录 | 过刊浏览 |

DD8单晶镍基高温合金热机械疲劳后γ/γ’界面位错网产生内应力的计算

周丽;李守新;王跃臣;王中光

中国科学院金属研究所沈阳材料科学国家(联合)实验室;沈阳 110016；沈阳理工大学机械工程系; 沈阳 110168

Calculation of the internal stresses at the γ/γ’ interface of DD8 single crystal nickel base superalloy after thermo-mechanical fatigue

ZHOU Li; LI Shouxin; WANG Yuechen; WANG Zhongguang

Shenyang National Laboratory for Materials Science; Institute of Metal Research;The Chinese Academy of Sciences; Shenyang 110016；Department of Mechanical Engineering; Shenyang Institute of Technology; Shenyang 110168

周丽; 李守新; 王跃臣; 王中光 . DD8单晶镍基高温合金热机械疲劳后γ/γ’界面位错网产生内应力的计算[J]. 金属学报, 2005, 41(3): 245-250 .
, , , . Calculation of the internal stresses at the γ/γ’ interface of DD8 single crystal nickel base superalloy after thermo-mechanical fatigue[J]. Acta Metall Sin, 2005, 41(3): 245-250 .

摘要 参考文献 相关文章 Metrics 全文: PDF(493 KB)   摘要: 计算了DD8单晶镍基高温合金在同相(IP)和反相(OP)热机械疲劳(TMF)后γ/γ’相界面上产生的位错网的内应力. 结果表明: IP TMF条件下，γ/γ’相界面上产生的位错网可以释放掉大部分错配应力，同时因位错网的存在导致了γ’沉淀相发生了明显的筏化现象. OP条件下产生的层错未造成基体内应力分布的不同，因此未发生γ’沉淀相的筏化. 关键词 ： 单晶镍基高温合金,  热机械疲劳,  位错网     Abstract：The internal stresses produced by dislocation networks at the γ/γ’ interfaces in a single crystal nickel-base superalloy DD8 has been studied after in phase (IP) and out of phase (OP) thermo-mechanical fatigue (TMF) testing. The results indicate that one of the roles of the dislocation networks at the γ/γ’ interfaces is to relax most of the misfit stress under IP TMF, on the other hand, the existence of the dislocation networks results in the directional coarsening of the γ’ precipitates. While under the OP TMF, the internal stress in the matrix induced by stacking faults does not vary significantly, the γ’ precipitates do not show direction coarsening in OP test. Key words： single crystal nickel base superalloy    thermo-mechanical fatigue    dislocation network 收稿日期: 2004-04-29      ZTFLH:  TG132.3   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 周丽 李守新 王跃臣 王中光 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2005/V41/I3/245 [1] Weatherly G C, Nicheolson R B. Philos Mag, 1968; 17: 801 [2] Lesalmonie A, Strudel J L. Philos Mag, 1975; 32: 937 [3] Zhang J H, Hu Z Q, Xu Y B, Wang Z G. Metall Trans, 1992; 23A: 1253 [4] Zhang J X, Murakumo T, Koizumi Y, Koizumi T, Kobayashi T, Harada H, Masaki S J R. Metall Mater Trans, 2002; 33A: 3741 [5] Gabrisch H, Mukherji D, Wahi R P. Philos Mag, 1996; 74A: 229 [6] Gabb T P, Draper S L, Hull D R, MacKay R A, Nathal M V. Mater Sci Eng, 1989; 118A: 59 [7] Wang Y C, Li S H, Ai S H, Liu F, Zhou L, Zhang H. Acta Metall Sin, 2003; 39: 237 (王跃臣,李守新,艾素华,刘峰,周丽,张辉.金属学 报,2003;39:237) [8] Wang Y C, Li S H, Ai S H, Liu F, Zhou L, Zhang H. Acta Metall Sin, 2003; 39: 150 (王跃臣,李守新,艾素华,刘峰,周丽,张辉.金属学 报,2003;39:150) [9] Carry C, Dermarker S, Strudel J L, Wonsiewicz B C. Metall Trans, 1979; 10A: 855 [10] Scheunemann-Frerker G, Muller L, Feller-Kniepmeier M. Philos Mag, 1993; 68A: 193 [11] Probst-Hein M, Dlouhy A, Eggeler G. Acta Mater, 1999; 47: 2497 [12] Zhou L, Li S X, Chen C R, Wang Y C, Zang Q S, Lu K. Z Metallkd, 2002; 4: 315 [13] Zhou L, Li S X, Chen C R, Wang Y C, Zang Q S, Lu K. Mater Sci Eng, 2003; A352: 300 [14] Kraft S, Altenberger I, Mughrabi H. Scr Metall Mater, 1995; 32: 411 [15] Mardhand N, Esperance G L, Pelloux M. ASTM STP 942, 1988: 638 [16] Carry C, Srudel J L. Acta Metall, 1977; 25: 767 [17] Buffiere J Y, Chegnet M C, Ignat M. Scr Metall Mater, 1996; 34: 349 [1] 赵鹏, 谢光, 段慧超, 张健, 杜奎. 两种高代次镍基单晶高温合金热机械疲劳中的再结晶行为[J]. 金属学报, 2023, 59(9): 1221-1229. [2] 张禄, 余志伟, 张磊成, 江荣, 宋迎东. GH4169高温合金热机械疲劳循环损伤机理及数值模拟[J]. 金属学报, 2023, 59(7): 871-883. [3] 谢君,田素贵,刘姣,周晓明,苏勇. FGH95粉末镍基合金蠕变期间位错网的形成与分析[J]. 金属学报, 2013, 49(7): 838-844. [4] 陈竹兵 黄志伟 王中光 朱世杰. 涂覆Ni--Cr--Al--Y涂层的镍基高温合金热机械疲劳行为[J]. 金属学报, 2009, 45(7): 820-825. [5] 王跃臣; 李守新; 艾素华 . DD8单晶镍基高温合金的热机械疲劳[J]. 金属学报, 2003, 39(9): 903-907 . [6] 王跃臣; 李守新; 艾素华; 刘峰; 周丽; 张辉 . DD8单晶镍基高温合金热机械疲劳后的微观结构[J]. 金属学报, 2003, 39(4): 337-341 . [7] 王跃臣; 李守新; 艾素华 . 同位相热机械疲劳形变后r/r’相界面上的位错网分析[J]. 金属学报, 2003, 39(3): 237-241 . [8] 王跃臣; 李守新; 艾素华; 刘峰; 周丽; 张辉 . 单晶镍基高温合金DD8反位相热机械疲劳后的层错[J]. 金属学报, 2003, 39(2): 150-154 . [9] 刘峰; 艾素华; 王跃臣; 张辉; 王中光 . K417铸造镍基高温合金热机械疲劳行为的研究[J]. 金属学报, 2001, 37(3): 267-271 . [10] 钱立和; 王中光; 户田裕之; 小林俊郎 . SiC晶须增强6061Al基复合材料的热机械疲劳性能Ⅱ.疲劳寿命与损伤机制[J]. 金属学报, 2001, 37(11): 1203-1207 . [11] 张济山;崔华;胡壮麒;村田纯教;森永正彦;汤川夏夫. 应用d-电子合金设计理论发展新型抗热腐蚀单晶镍基高温合金──Ⅲ.性能评价[J]. 金属学报, 1994, 30(2): 70-78. [12] 张济山;崔华;胡壮麒;村田纯教;森永正彦;汤川夏夫. 应用d—电子合金设计理论发展新型抗热腐蚀单晶镍基高温合金 Ⅰ.相稳定性临界条件的确定[J]. 金属学报, 1993, 29(7): 5-12. [13] 张济山;崔华;胡壮麒;村田纯教;森永正彦;汤川夏夫. 应用d—电子合金设计理论发展新型抗热腐蚀单晶镍基高温合金——Ⅱ合金元素对显微组织和性能的影响[J]. 金属学报, 1993, 29(7): 13-22. [14] 艾素华;V.LUPINC;M.MALDINI. 单晶镍基高温合金的蠕变断裂[J]. 金属学报, 1992, 28(3): 32-37. [15] 王华明;唐亚俊;张静华;张志亚;胡壮麒. 单晶高温合金定向凝固过程中初生碳化物的上浮现象[J]. 金属学报, 1991, 27(4): 71-72. Viewed Full text Abstract Cited   Shared      Discussed