钢包出钢末期漩涡抑制机理探究及防漩设计 |
王强1,2( ), 王连钰1,3, 李宏侠1, 蒋佳伟1, 朱晓伟1,3, 郭占成2, 赫冀成1 |
1 东北大学材料电磁过程研究教育部重点实验室 沈阳 1108192 2 北京科技大学钢铁冶金新技术国家重点实验室 北京 1000833 3 东北大学冶金学院 沈阳 110819 |
|
Suppression Mechanism and Method of Vortex During Steel Teeming Process in Ladle |
Qiang WANG1,2( ), Lianyu WANG1,3, Hongxia LI1, Jiawei JIANG1, Xiaowei ZHU1,3, Zhancheng GUO2, Jicheng HE1 |
1 Key Laboratory of Electromagnetic Processing of Materials (Ministry of Education), Northeastern University, Shenyang 110819, China 2 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China 3 School of Metallurgy, Northeastern University, Shenyang 110819, China |
引用本文:
王强, 王连钰, 李宏侠, 蒋佳伟, 朱晓伟, 郭占成, 赫冀成. 钢包出钢末期漩涡抑制机理探究及防漩设计[J]. 金属学报, 2018, 54(7): 959-968.
Qiang WANG,
Lianyu WANG,
Hongxia LI,
Jiawei JIANG,
Xiaowei ZHU,
Zhancheng GUO,
Jicheng HE.
Suppression Mechanism and Method of Vortex During Steel Teeming Process in Ladle[J]. Acta Metall Sin, 2018, 54(7): 959-968.
[1] | Niclas A, Andrey K, Par G J.The effect of different non-metallic inclusions on the machinability of steels[J]. Materials, 2015, 8: 751 | [2] | Holappa L E K, Helle A S. Inclusion control in high-performance steels[J]. J. Mater. Process. Technol., 1995, 53: 177 | [3] | Zhang L F, Thomas B G.State of the art in the control of inclusions during steel ingot casting[J]. Metall. Mater. Trans., 2006, 37B: 733 | [4] | Tripathi N N, Nzotta M, Sandberg A, et al.Effect of ladle age on formation of non-metallic inclusions in ladle treatment[J]. Ironmak. Steelmak., 2004, 31: 235 | [5] | Beskow K, Tripathi N N, Nzotta M, et al.Impact of slag-refractory lining reactions on the formation of inclusions in steel[J]. Ironmak. Steelmak., 2004, 31: 514 | [6] | Zhang S J, Zhu M Y, Zhang Y L, et al.Study on mechanism of entrapment in slab continuous casting mould with high casting speed and argon blowing[J]. Acta Metall. Sin., 2006, 42: 1087(张胜军, 朱苗勇, 张永亮等. 高拉速吹氩板坯连铸结晶器内的卷渣机理研究[J]. 金属学报, 2006, 42: 1087) | [7] | Riaz S, Mills K C, Bain K.Experimental examination of slag/refractory interface[J]. Ironmak. Steelmak., 2002, 29: 107 | [8] | Hassall G J, Bain K G, Jones N, et al.Modelling of ladle glaze interactions[J]. Ironmak. Steelmak., 2002, 29: 383 | [9] | Lei H, Zhu M Y, He J C.Mathematical modeling of slag entrapment in continuous casting mould[J]. Acta Metall. Sin., 2000, 36: 1113(雷洪, 朱苗勇, 赫冀成. 连铸结晶器内卷渣过程的数学模型[J]. 金属学报, 2000, 36: 1113) | [10] | Piva M, Iglesias M, Bissio P, et al.Experiments on vortex funnel formation during drainage[J]. Physica, 2003, 329A: 1 | [11] | Sankaranarayanan R, Guthrie R I L. Slag entraining vortexing funnel formation during ladle teeming: Similarity criteria and scale-up relationships[J]. Ironmak. Steelmak., 2002, 29: 147 | [12] | Kuwana K, Hassan M I, Signh P K, et al.Scale-model experiment and numerical simulation of a steel teeming process[J]. Mater. Manuf. Process., 2008, 23: 407 | [13] | Hammerschmid P, Tacke K H, Popper H, et al.Vortex formation during drainage of metallurgical vessels[J]. Ironmak. Steelmak., 1984, 11: 332 | [14] | Sucker D, Reinecke J, Hage-Jewainski H.Flow investigations for melting metallurgical processes[J]. Stahl Eisen, 1985, 105: 765 | [15] | Lin R, Yan Z G, Liu T, et al.Modeling formation mechanism of vortex during steel casting in a 60 t LADLE[J]. Chin. J. Process. Eng., 2010, 10: 655(蔺瑞, 颜正国, 刘涛等. 60 t钢包浇注过程中汇流旋涡形成机理[J]. 过程工程学报, 2010, 10: 655) | [16] | Pierre V.Récipient métallurgique de coulee [P]. France Pat, No2443892, 1978 | [17] | Dardick I I, Kapusta A K, Mikhailovich B M, et al.Methods and facilities for suppressing vortices arising in tundishes or ladles during their respective discharge [P]. Eur Pat, EP1791665, 2007 | [18] | Suh J W, Park J, Kim H, et al.Suppression of the vortex in ladle by static magnetic field[J]. ISIJ Int., 2001, 41: 689 | [19] | Ono-Nakazato H, Taguchi K, Usui T, et al.Prevention method of swirling flow generation in discharging liquid in the reactor vessel[J]. J. Jpn. Soc. Exp. Mech., 2007, 8: S147 | [20] | Mazzaferro G M, Piva M, Ferro S P, et al.Experimental and numerical analysis of ladle teeming process[J]. Ironmak. Steelmak., 2004, 31: 503 | [21] | Lin R, Yan Z G, Liu T, et al. Water modelling on the effect of trapezoidal nozzle on vortex during teeming in ladle [J]. Adv. Mater. Res., 2011, 295-297: 716 | [22] | Labate M D.Slag retaining device with vortex inhibitor [P]. US Pat, 4799650, 1989 | [23] | Huang Y, Ye S F, Su T S, et al.Technology of preventing slag down in casting process[J]. Jiangxi Metall, 1999, 19(6): 1(黄晔, 叶树峰, 苏天森等. 浇注过程的防下渣技术[J]. 江西冶金, 1999, 19(6): 1) | [24] | Li H X, Wang Q, Lei H, et al.Mechanism analysis of free-surface vortex formation during steel teeming[J]. ISIJ Int., 2014, 54: 1592 | [25] | Li H X, Wang Q, Jiang J W, et al.Analysis of factors affecting free surface vortex formation during steel teeming[J]. ISIJ Int., 2016, 56: 94 | [26] | Centerra Resource park 10 Cavendish court Lebanon. User's Guide for Fluent version 6. 3, 2006 | [27] | Sankaranarayanan R, Guthrie R I L. Slag entraining vortexing funnel formation during ladle teeming: Similarity criteria and scale-up relationships[J]. Ironmak. Steelmak., 2002, 29: 147 | [28] | Jain A K, Ranga R, Kittur G, et al.Vortex formation at vertical pipe intake[J]. J. Hydraulics Division, 1978, 104: 1429 | [29] | Aubert J, Brito D, Nataf H C, et al.A systematic experimental study of rapidly rotating spherical convection in water and liquid gallium[J]. Phys. Earth Planet. Int., 2001, 128: 51 |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|