钨-钼-锆三元系平衡图中1200℃恒溫截面的研究
庄育智;倪国年
A STUDY OF THE ISOTHERMAL SECTION AT 1200℃ OF THE TERNARY SYSTEM W-Mo-Zr
CHUANG Y-CHIH; NI KUO-NIEN
引用本文:

庄育智;倪国年. 钨-钼-锆三元系平衡图中1200℃恒溫截面的研究[J]. 金属学报, 1966, 9(2): 176-231.
, . A STUDY OF THE ISOTHERMAL SECTION AT 1200℃ OF THE TERNARY SYSTEM W-Mo-Zr[J]. Acta Metall Sin, 1966, 9(2): 176-231.

全文: PDF(1394 KB)  
摘要: 应用金相及X射线分析法研究了钨-钼-锆三元系1200℃恒温截面。确定在这个截面上存在三个极窄的单相区:钨-钼固溶体α、锆固溶体β、三元中间相ε和两个广阔的两相区:(α+ε)与(ε+β)。α相和β相具有体心立方结构;ε相则具有MgCu_2结构的三元Laves相Zr(W,Mo)_2。ε相的点阵常数由ZrW_2到ZrMo_2呈线性变化。合金硬度测量结果与金相及X射线分析结果相符。
Abstract:The isothermal section at 1200℃ of the ternary system W-Mo-Zr has been determined by metallographic and X-ray diffraction methods. Two terminal b.c.c, solid solutions based on W(Mo) and Zr respectively and an intermetallic compound Zr(W, Mo)_2 isomorphous with MgCu_2 structure have been identified. The lattice parameter of Zr(W, Mo)_2 varies linearly from 7.619 (?) for ZrW_2 to 7.589A for ZrMo_2. Vicker's hardness measurements support the metallographic and X-ray diffraction results.
收稿日期: 1966-02-18     
[1] Fahrenwald, F. A.: Trans. AIME, 1917, 54, 541. Fahrenwald, F. A.: Trans. AIME, 1917, 56, 612.
[2] Jeffries, Z.: Trans. AIME, 1917, 56, 600.
[3] Geiss, W., van Liempt, J. A. M.: Z. Anorg. Chem., 1923, 128, 355.
[4] Domagala, R. F., McPherson, D. J., Hansen, M.: Trans. A1ME, 1953, 197, 73.
[5] Semchyshen, M., Barr, R. Q.: Refractory Metals and Alloys, (Interscience, 1961) , p. 283.
[6] 庄育智、唐全红、庄祥麟:金属学报,1966,9,63.
[7] Geach, G. A., Slattery, G. F.: Trans. AIME, 1953, 197, 747.
[8] Semchyshen, M., McArdle, G. D., Barr, R. Q.: Development of Molybdenum-base Alloys, (WADC Tech. Rept., 1959, Oct.) p. 59-280.
[9] Chuang Yu-chih (庄育智), Chuang Tsiang-lin (庄祥麟), Wu Cheung-hang (吴昌衡): Sci. Sinica, 1964, 13, 1851.
[10] Cohen, N. U.: Rev. Sci. Instr., 1935, 6, 68. Cohen, N. U.: Rev. Sci. Instr., 1936, 7, 155.
[11] Claassen, A., Burgers, W. G.: Z. Krist., 1933, 86, 100.
[12] Pipitz, E., Kieffer, R.: Z. Metallle., 1955, 46, 187.
[13] Duwez, P., Jordan, C. B.: J. Am. Chem. Soc., 1951, 73, 5509.
[14] #12A
No related articles found!