TENSILE DEFORMATION BEHAVIOUR OF CARBON STEEL UNDER MEDIUM-HIGH TEMPERATURE

Luo Xiyu (Central Iron and Steel Research Institute; Ministry of Metallurgical Industry; Beijing); Imamura Jun (Fundamental Research Laboraties; Nippon Steel Corporation; Japan)

罗锡裕;今村淳. 中高温区碳素钢的拉伸变形行为[J]. 金属学报, 1982, 18(5): 550-642.
, . TENSILE DEFORMATION BEHAVIOUR OF CARBON STEEL UNDER MEDIUM-HIGH TEMPERATURE[J]. Acta Metall Sin, 1982, 18(5): 550-642.

摘要 参考文献 相关文章 Metrics 全文: PDF(4295 KB)   摘要: 本文系统地研究了起始γ晶粒尺寸约800μm,含碳量分别为0.10,0.25,0.39,0.71％的四种碳素钢在试验温度700—1300℃,变形速率6.7×10~(-4)—6.7×10~(-2)S~(-1)下的拉伸变形行为。着重指明:由热激活过程决定的γ相区的变形方程符合(?)=Aσ_M~nexp(-Q/RT);γ相区最大变形应力随含碳量的增加而下降;在(α+γ)二相区稍低于A_3温度出现脆化;二相区的脆化随含碳量的增加而趋缓和。 Abstract：A systematical study was made of the tensile deformation behaviour of 4 different carbon steels, containing 0.10, 0.25, 0.39 and 0.71% C respectively, with initial austenite grain size 800μm under temperature 700—1300℃ at the strain rate 6.7×10~(-4)—6.7×10~(-2)S~(-1). It was indicated that the equation of deformation in the region of austenite phase controlled by the heat activation process is quite agreed with (?)=Aσ_M~nexp(-Q/RT) and the maximum deformation stress is decreased with the increasing of their C content. In the binary phase α+γ region, an embrittlement appears under temperature slightly lower than A_3 point and may become more or less to toughen as the increase of the C content. 收稿日期: 1982-05-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 罗锡裕 今村淳 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1982/V18/I5/550 1 田村今男,日本金属学会会报,16(1977) ,877． 2 铃木洋夫;山口重裕,日本铁钢基礎共同研究会,高温变形部会,1979,p.113． 3 Nakamura, T.; Uekl, M., Trans Iron Steel Inst Jpn., 15 (1975) , 185． 4 Wray, P. J.; Holmes, M. F., Metall. Trans., 6A (1975) , 1189． 5 Wray, P. J., Metall. Trans., 6A (1975) , 1197． 6 作井诚太;酒井拓;村濑曄夫,日本金属学会誌,39(1975) ,535． 7 作井诚太;酒井拓;沢田裕冶,日本金属学会誌,40(1976) ,1284． 8 作井诚太;酒井拓;武石和夫,铁钢,62(1976) ,856． 9 作井诚太;酒井拓;ibid.,63(1977) ,285． 10 铃木洋夫;中村泰,日本金属学会会报,18(1979) ,748． 11 铃木洋夫;西村哲;山口重裕,铁钢,65(1979) ,2038． 12 铃木洋夫;西村哲;今村淳,中村泰,ibid.,67(1981) ,1180． 13 Mintz, B.; Arrowsmith, J. M., Met. Technol., 6 (1979) , 25． 14 山中和夫;寺崎富久长;大谷泰夫;小田光雄;吉原正裕,铁钢,65(1979) ,1410． 15 酒井拓,日本金属学会会报,17(1978) ,195． 16 Mead, H. W.; Birehenall, C. E., J. Met., 8 (1956) , 1336． 17 今村淳;铃木洋夫;宫崎武志,铁钢,66(1980) ,s804． No related articles found! Viewed Full text Abstract Cited   Shared      Discussed