金属学报  1982, Vol. 18 Issue (6): 635-763

论文 本期目录 | 过刊浏览 |

高品位细磁精矿烧结矿还原粉化的研究

周取定;任允芙;杨旭辉

北京钢铁学院;北京钢铁学院;马鞍山钢铁公司

AN INVESTIGATION ON THE REDUCTION DISINTEGRATION OF SINTERS MADE FROM CHINESE MAGNETITE IRON ORE CONCENTRATES

Zhou Quding; Ren Yunfu (Beijing University of Iron and Steel Technology); Yang Xuhui (Ma'anshan Iron and Steel Company)

周取定;任允芙;杨旭辉. 高品位细磁精矿烧结矿还原粉化的研究[J]. 金属学报, 1982, 18(6): 635-763.
, , . AN INVESTIGATION ON THE REDUCTION DISINTEGRATION OF SINTERS MADE FROM CHINESE MAGNETITE IRON ORE CONCENTRATES[J]. Acta Metall Sin, 1982, 18(6): 635-763.

摘要 参考文献 相关文章 Metrics 全文: PDF(2275 KB)   摘要: 本文在模拟高炉条件下动态测定烧结矿还原粉化的热转鼓中,对我国高品位细磁精矿制成的不同碱度烧结矿进行了低温还原粉化率的测定。并与澳大利亚赤铁矿粉制成的烧结矿进行对比。通过测定发现我国高品位细磁精矿烧结矿在碱度1.7—1.8左右、还原温度为500℃时,有最高的还原粉化率,大于或低于此碱度的烧结矿,还原粉化率减轻。澳大利亚赤铁矿粉烧结矿在低碱度(R=0.9)时有严重的低温还原粉化率,但随着碱度上升,粉化率减轻。通过改变还原温度、以H_2代替CO作还原剂、同时对各种烧结矿还原前后的矿物组成及显微结构进行岩矿相鉴定,获得了烧结矿还原粉化的机理性说明。此外还在高炉内对烧结矿进行了还原粉化试验。 Abstract：An investigation was carried out on the reduction disintegration properties of two typical sinters made from Chinese high grade magnetite iron ore concentrates produced by Qian'an and Ma'anshan areas. The test was carefully compared with that of Australia hematite ore fines in a specially designed rotary tube. It was found that the worst resistance to the reduction disintegration seems to be displayed for the Chinese sinters with the basicity CaO/SiO_2 in the region about 1.7—1.8 and under temperature of reduction at 500℃, as weU as it has much improved since the CaO/SiO_2 ratio beyond the region, namely 1.0 or 2.5. WhiLst the reduction disintegration index of the Australia hematite sinter decreases with the increase of its basicity.By changing the test temperature of reduction and adopting H_2 as a reducing gas instead of CO, an examination of the sinters on the entire reduction process under petrographic microscope shows that the reduction disintegration properties of Chinese magnetite sinters with different basicities are closely related to their mineral composition and microtexture. The carbon deposition may bc also an important factor affecting their reduction strength. However, the phase transformation of Fe_2O_3 during reduction influenced them slightly due to its small content.Experiments were also made of the properties of the sinters in 55m~3 blast furnace, in which a perforate steel probe tube filled with several Myers of testing sinter and coke was inserted. The result is very conformable to that in the rotary tube. 收稿日期: 1982-06-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 周取定 任允芙 杨旭辉 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1982/V18/I6/635 1 Linder, R., J. Iron Steel Inst., 189(1958) , 233． 2 児玉惟孝;重见彰利;斧勝也;堀尾竹弘,铁钢,51(1965) ,2203． 3 管原欣一;佐滕勝彦,铁钢,55(1969) ,1107． 4 Bagnall, E. J., in Agglomeration 77, Ed. Sastry, K. V. S., AIME, New York, 1977． p. 587． 5 Clark, S. P. Handbook of Physical Constants, Geological Society of America Memoir 97, 1966, p. 81． 6 #12 7 Davis, W. R.; Slawson, R. J.; Rigby, G. R., Trans. Br. Ceram. Soc., 56(1957) , 67． 8 Edstrom, J. D., J. Iron Steel Inst., 175(1953) , 289． 9 Elkasabgy, T., A Study of the Mechanism of Degradation During Reduction of iron ore Pellets, Ph.D. Thesis, McMaster University, Canada, 1978． 10 周取定,冯志坚等,北京钢铁学院学报,(1981) ,№.3,18 No related articles found! Viewed Full text Abstract Cited   Shared      Discussed