SEM AND X-RAY STUDIES ON MECHANICAL ALLOYING

by ZHUANG Yi; ZHEN Bingsheng; HAN Linguang; SU Huiqin (Central Iron and Steel Research Institute; Ministry of Metallurgical Industry; Beijing) (Manuscript received 7 February; 1983; revised manuscript 1 August; 1983)

庄毅;曾炳胜;韩临光;苏惠芹. 机械合金化的扫描电镜和X射线研究[J]. 金属学报, 1984, 20(2): 176-222.
, , , . SEM AND X-RAY STUDIES ON MECHANICAL ALLOYING[J]. Acta Metall Sin, 1984, 20(2): 176-222.

摘要 参考文献 相关文章 Metrics 全文: PDF(1769 KB)   摘要: 本文用扫描电镜和X射线对一种复杂的弥散强化Ni基高温合金的机械合金化进行了研究。实验表明,采用高能球磨的方法可以使原料中的各种金属粉末间形成机械固溶体,实现合金化。在球磨过程中,原料中的Cr-Ni基母合金以及W,Mo,Ta等元素不断向Ni基体中周溶,使Ni基固溶体γ_(Ni)的点阵参数逐渐增大。同时,超细氧化物粒子在基体中也逐步达到理想的分布状态。这种机械固溶体虽存在一定的微区成分偏离,但可以通过某些有效措施使之显著减小。本文对机械合金化工艺参数也进行了分析和讨论。 Abstract：Studies were made of the mechanical alloying of an oxide dispersion strengthened majority γ'-phase Ni-base superalloy by analyses of SEM and X-rays. By a high energy ball milling technique, a mechanical solid-solution may be formed and the mechanical alloying may be realized from various raw metal powders, The CrNi-based masteralloy and elements such as W, Mo, Ta, etc. in the raw metal powders were continually solid-soluble into Ni matrix and the lattice parameter of Ni-base solid-solution was increased with processing time. Simultaneously, nearly random dispersion of the ultraflne oxide particles was obtained in the metal matrix. Although the micro-area compositions of the mechanical solid-solution is segregated, yet it may be improved by certain effective steps. The technical parameters of the mechanical alloying in aUoy studied were also analyzed and discussed. 收稿日期: 1984-02-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 庄毅 曾炳胜 韩临光 苏惠芹 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1984/V20/I2/176 1 Benjamin, J. S., Metall. Trans., 1(1970) , 2943． 2 Curwick, C. R., The Mechanical Alloying Process: Powder to Mill Product, Frontiers of High Temperature Materials Conference, Sponsored by Inco Limited, New York, May 18-21, 1981． 3 Benjamin, J. S., Sci. Am., 234(1976) , №5, 40． 4 Morse, J. P.; Benjamin, J. S., Mechanical Alloying, New Trends in Materials Processing, ASM, 1976, p. 165． 5 Nutting, J.; Ubhi, S.; Hughes, T. A., The Development of Microstructure in Incoloy MA 956, Frontiers of High Temperature Materials Conference, Sponsored by Inco Limited, New York, May 18-21, 1981． No related articles found! Viewed Full text Abstract Cited   Shared      Discussed