金属学报  1987, Vol. 23 Issue (4): 306-312

论文 本期目录 | 过刊浏览 |

含Al,Si反铁磁性γ-Fe-Mn基合金中的电阻极小

张彦生

大连铁道学院

RESISTIVITY MINIMUM IN ANTIFERROMAGNETIC γ-Fe-Mn BASE ALLOYS CONTAINING Al OR Si

by ZHANG Yansheng (Dalian Railway Lnstitute) (Manuscript received 2 June; 1986)

张彦生. 含Al,Si反铁磁性γ-Fe-Mn基合金中的电阻极小[J]. 金属学报, 1987, 23(4): 306-312.
. RESISTIVITY MINIMUM IN ANTIFERROMAGNETIC γ-Fe-Mn BASE ALLOYS CONTAINING Al OR Si[J]. Acta Metall Sin, 1987, 23(4): 306-312.

摘要 参考文献 相关文章 Metrics 全文: PDF(534 KB)   摘要: 本文研究Al,Si及Cr对反铁磁性γ-Fe-Mn基合金的Neel转变及电阻极小的影响.结果表明,Cr对Fe-Mn基合金的磁化率(X),X-T及ρ(电阻率)-T关系的影响较小,也不促进基体形成局域净磁矩.相反,Al,Si则显著改变γ-Fe-Mn合金的磁结构、X-T及ρ-T关系,在Neel温度T_N以下,随反铁磁转变的磁性电阻ρ_m的增大,出现电阻极小,随后出现负电阻温度系数.降温直至4.3k,γ-Fe-Mn及γ-Fe-Mn-Cr合金在试验精度内未呈现任何电阻反常变化,而固溶Al或Si后则观察到第二次电阻极小,电阻极小温度T_(min)~(2)与电阻极小深度△ρ(ρ_(4k)～ρ_(T_(min)))随Al,Si浓度的增大而增加,且在T_(min)~(2)—4k间,ρ随lgT的降低而线性增大.由此可以假定,反铁磁态γ-Fe-Mn中加入Al或Si,导致Fe离子处形成局域净磁矩,并发生ISDW-CSDW态转变,因而产生类似Kondo效应的低温电阻极小. Abstract：The effect of Al, Si and Cr on the temperature dependence of susceptibility, X, and resistivity, ρ, of γ-Fe-Mn (23.8-31.6at.-%) alloys containing Al, Si and Cr has been investigated over the temperature range of 77-750K and 4.3-48GK. respectively. The Cr was detected to be slightly influenced upon their x and X-T or ρ-T. And it does not enable the matrix to form a localized net moment associated with Fe atoms. While the addition of certain amount of Al or Si may remarkably modify the magnetic structure as well as the temperature dependence of X or ρ. With the increase of antiferromagnetic transition resistivity below the Neel temperature, a resistivity minimum appears and then present a negative tem- perature coefficient. Down to 4.3 K, neither anomaly for resistivity of γ-Fe-Mn and γ-Fe-Mn-Cr alloys was found within experimental accuracy, but the secondary resistivity minimum was observed in γ-Fe-Mn alloys containing Al or Si. The temperature of minimum T_(min)~(2), and the depth of minimum △ρ(ρ_(4k)—ρ_r_(min)~(2)) of resistivity increase with the increase of concentration of Al or Si. The resistivity increases linearly with the decrease of lgT between T_(min)~(2) and 4K. It seems to be proposed that the formation of a localized magnetic net moment on Fe atoms and the transition from the incommensurate SDW state to commensurate SDW one are caused by the resistivity minimum in antiferromagnetic γ-Fe-Mn alloys with an addition of Al or Si, thus the low temperature resistivity minimum is due to the Rondo-like effect. 收稿日期: 1987-04-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 张彦生 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1987/V23/I4/306 1 Kondo J. Prog Theor Phys, 1964; 32: 37 2 Katano S, Mori N. J Phys Soc Jpn, 1979; 46: 1265 3 Katano S, Mori N, Nakayama K. J Phys Soc Jpn, 1980; 48: 192 4 Arajs S, Dunmyre G R, Dechter S J. Phys Rev, 1967; 154: 448 5 Lomer W M. Proc Phys Soc 1962; 80: 489 6 Asano S, Yamashita J. J Phys Soc Jpn, 1971; 31: 1000 7 Endoh Y, Ishikswa Y. J Phys Soc Jpn, 1971; 30: 1614 8 张彦生.金属学报,1985;21:A295 9 张彦生.金属学报,1986;22 A470 10 张彦生.金属学报,1984;20:A313 11 Arajs S, Dunmyre G R. J Appl Phys, 1967; 38: 1157 12 Wolff P A. Phys Rev, 1961; 124: 1030 13 Suzuki T. J Phys Soc Jpn, 1966; 21: 442a No related articles found! Viewed Full text Abstract Cited   Shared      Discussed