金属学报  2005, Vol. 41 Issue (1): 67-

论文 本期目录 | 过刊浏览 |

激光快速熔凝Zn--2%Cu包晶合金的显微组织

苏云鹏 王 猛 林 鑫 李华琳 黄卫东

西北工业大学凝固技术国家重点实验室; 西安 710072

Microstructure of Zn-2%Cu Alloy Under Laser Rapid Melting—Solidification

SU Yunpeng; WANG Meng; LIN Xin; LI Hualin; HUANG Weidong

State Key Laboratory of Solidification Processing; Northwestern Polytechnical University; Xi'an 710072

苏云鹏; 王猛; 林鑫; 李华琳; 黄卫东 . 激光快速熔凝Zn--2%Cu包晶合金的显微组织[J]. 金属学报, 2005, 41(1): 67-.
, , , , . Microstructure of Zn-2%Cu Alloy Under Laser Rapid Melting—Solidification[J]. Acta Metall Sin, 2005, 41(1): 67-.

摘要 参考文献 相关文章 Metrics 全文: PDF(351 KB)   摘要: 利用5 kW连续波CO2激光器对Zn--2%Cu包晶合金进行了表面快速熔凝实验研究, 扫描速率从6 mm/s至1207 mm/s。随着凝固速率的提高, 该合金微观组织形态由低速平界面向层片状组织、浅胞晶直至高速绝对稳定平界面转变。实验结果表明, 该合金微观组织演化规律与利用林鑫等的数值模型和Jackson--Hunt的共晶模型相结合所得到的界面响应函数作出的预测结果吻合较好。 关键词 ： Zn-2%Cu,  包晶合金,  激光表面熔凝     Abstract：Laser surface remelting experiments have been performed on Zn-2%Cu alloy with a 5 kW continous wave CO2 laser. With increasing scanning rate from 6 mm/s to 1207 mm/s, the microstructure transition from light band to lamellar structure, cell, and finally to absolute stability planar, has been clearly observed in the laser molten pool. The experiment results are in good agreement with the prediction of interface response function calculated with Lin's numerical model for cellular/dendritic growth and Jackson-Hunt model for eutectic growth. Key words： Zn-2%Cu    peritectic alloy    laser surface remelting 收稿日期: 2004-01-07      ZTFLH:  TG244   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 苏云鹏 王猛 林鑫 李华琳 黄卫东 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2005/V41/I1/67 [1] Wang M, Lin X, Su Y P, Shen S J, Huang W D. Mater Sci Eng, 2002; 1: 111(王猛,林鑫,苏云鵬,沈淑娟,黄卫东.材料科学与工程,2002;1:111) [2] Lee J H, Verhoeven J D. J Cryst Growth, 1994; 144: 353 [3] Busse P, Meissen F. Scr Mater, 1997; 36: 653 [4] Vandyoussefi M, Kerr H W, Kurz W. Acta Mater, 2000;48: 2297 [5] Xu W, Ma D, Feng Y P, Li Y. Scr Mater, 2001; 44: 631 [6] Liu Y C, Yang G C, Zhou Y H. J Cryst Growth, 2002;240: 603 [7] Singh J. J Mater Sci, 1994; 29: 5232 [8] Zimmerman M, Carrad M, Gremaud M, Kurz W. MaterSci Eng A, 1991; 134: 1278 [9] Gill S C, Zimmerman M, Kurz W. Acta Metall Mater,1992; 40: 2895 [10] Yang S, Huang W D, Liu W J, Su Y P, Zhou Y H. ChinJ Lasers, 2002; 29: 475(杨森,黄卫东,刘文今,苏云鹏,周尧和.中国激光,2002;29:475) [11] Kurz W, Fisher D J. Fundamentals of Solidification, Switzerland-Germany-UK-USA, Trans Tech Publications, 1989: 305 [12] Lin X, Li Y M, Liu Z X, Li T, Huang W D. Sci Technol Adv Mater, 2001; 2: 293 [13] Huang W D, Lin X, Wang M, Shen S J, Su Y P, Liu Z X. Sci Chin, 2002; 45E: 458 [14] Aziz M J. J Appl Phys, 1982; 53: 1158 [15] Jackson K A , Hunt J D. Trans Metall Soc AIME, 1996; 236: 1129 [16] Massalski T B. Binary Alloy Phase Diagram, Metals Park OH: American Society for Metals, 1986: 337 [17] Liu H Y, Jones H. Acta Metall Mater, 1992; 40: 229 [18] Cahn R W, Haasen P. Physical Metallurgy (4th edn), North-Holland: Amsterdam, 1996: 70 [19] Liu Z X, Huang W D, Yang S. Chin J Nonferrous Met, 2002; 12: 458(刘振侠,黄卫东,杨森.中国有色金属学报,2002;12:458) [20] Wang M, Lin X, Su Y P, Shen S J, Huang W D. ActaMetall Sin, 2002; 38: 337(王猛,林鑫,苏云鹏,沈淑娟,黄卫东.金属学报,2002;38:337) [21] Mullins W W, Sekerka R F. J Appl Phya, 1963; 34: 323 [22] Su Y P, Wang M, Lin X, Shen S J, Huang W D. Chin JNonferrous Met, 2003; 13: 1092 [23] Trivedi R, Kurz W. Int Mater Rev, 1994; 3949 [24] Yang S, Su Y P, Liu W J, Huang W D, Zhou Y H. ActaPhys Sin, 2003; 1: 81(杨森,苏云鹏,刘文今,黄卫东,周尧和.物理学报,2003;1:81) [1] 刘桐,骆良顺,张延宁,苏彦庆,郭景杰,傅恒志. 定向凝固Al-Y合金组织演化规律及小平面相生长*II. Al-53%Y包晶合金组织演化规律[J]. 金属学报, 2016, 52(7): 866-874. [2] 王灵水,沈军,商昭,王雷,傅恒志. 对流条件下定向凝固包晶合金的相和微观组织选择[J]. 金属学报, 2013, 49(7): 822-830. [3] 骆良顺 张宇民 苏彦庆 王新 郭景杰 傅恒志. 包晶合金定向凝固过程中的对流效应及带状组织形成机制 I.实验结果[J]. 金属学报, 2011, 47(3): 275-283. [4] 骆良顺 傅恒志 张宇民 李新中 苏彦庆 郭景杰. 包晶合金定向凝固过程中的对流效应及带状组织形成机制 II.理论分析[J]. 金属学报, 2011, 47(3): 284-290. [5] 吕海燕; 李双明; 钟宏; 刘林; 傅恒志 . 激光快速熔凝Cu-75%Sn过包晶合金中ε相向包晶η相的转变[J]. 金属学报, 2008, 44(7): 843-847 . [6] 苏彦庆; 李新中; 郭景杰; 吴士平; 傅恒志 . 定向凝固包晶相变微观组织演化的相场方法研究 II.形核控制的微观组织模拟[J]. 金属学报, 2006, 42(6): 606-610 . [7] 李新中; 苏彦庆; 郭景杰; 吴士平; 傅恒志 . 定向凝固包晶相变微观组织演化的相场方法研究 I.三相交节点的延伸[J]. 金属学报, 2006, 42(6): 599-605 . [8] 李新中; 郭景杰; 苏彦庆; 吴士平; 傅恒志 . 定向凝固包晶合金带状组织的形成机制及相选择 I.带状组织的形成机制[J]. 金属学报, 2005, 41(6): 593-598 . [9] 郭景杰; 李新中; 苏彦庆; 吴士平; 傅恒志 . 定向凝固包晶合金带状组织的形成机制及相选择 II.相选择[J]. 金属学报, 2005, 41(6): 599-604 . [10] 李双明; 马伯乐; 吕海燕; 刘林; 傅恒志 . Cu--70%Sn包晶合金高温度梯度定向凝固的组织及其尺度[J]. 金属学报, 2005, 41(4): 411-416 . [11] 李双明; 刘林; 李晓历; 傅恒志 . 包晶合金定向凝固平界面前沿的形核分析[J]. 金属学报, 2004, 40(1): 20-26 . [12] 王猛; 林鑫; 苏云鹏; 沈淑娟; 黄卫东 . Zn-Cu包晶合金定向凝固组织演化 II. 相选择的改进分析[J]. 金属学报, 2003, 39(8): 838-842 . [13] 王猛; 林鑫; 苏云鹏; 沈淑娟; 黄卫东 . Zn-Cu包晶合金定向凝固组织演化 I. 实验现象及分析[J]. 金属学报, 2003, 39(8): 831-837 . [14] 杨森; 黄卫东; 钟敏霖; 刘文今; 周尧和 . DD2单晶合金激光表面重熔过程中熔区组织预测[J]. 金属学报, 2002, 38(5): 507-511 . [15] 王猛; 林鑫; 苏云鹏; 沈淑娟; 黄卫东 . Zn-2%Cu包晶合金定向凝固的微观组织[J]. 金属学报, 2002, 38(4): 337-341 . Viewed Full text Abstract Cited   Shared      Discussed