In对Pd氢化的影响

陈仰霖

浙江大学

EFFECTS OF In ADDITION ON Pd HYDRIDING

CHEN Yanglin (Zhejiang University; Hangzhou 310027) (Manuscript received 1995-09-12; in revised form 1996-01-19)

陈仰霖. In对Pd氢化的影响[J]. 金属学报, 1996, 32(5): 489-494.
. EFFECTS OF In ADDITION ON Pd HYDRIDING[J]. Acta Metall Sin, 1996, 32(5): 489-494.

摘要 参考文献 相关文章 Metrics 全文: PDF(378 KB)   摘要: 本文使用超微高压天平装置，在压力为０．００１－３．５ＭＰａ，温度为３８１－６２１Ｋ范围内测得纯Ｐｄ和４种成分Ｐｄ－Ｉｎ合金的吸放氢等温线。结果表明：价电子浓度低于０．５，晶格膨胀占主导作用，氢的溶解度随Ｉｎ含量增加而升高；价电子浓度高于０．５，费米能升高占主导作用，氢溶解度随Ｉｎ含量增加而降低。这同对Ｐｄ－Ａｇ，Ｐｄ－Ｓｎ合金中Ａｇ，Ｓｎ的作用解释相似，即它们在合金中对氢的溶解度确有上述两种相反的影响。 关键词 ： 钯氢化,  Ｐｄ－Ｉｎ合金,  价电子浓度,  晶格膨胀,  费米能     Abstract：Hydrogen absorption and desorption isotherms were measured in a microbalance in the pressure range from 0.001 to 3.5 MPa and at seven temperatures from 381 to 621 K for four Pd-In alloys containing in from 3.6 to 15 atomin percent as well as pure Pd. The results are similar to those obtained for the analogous alloys Pd-Ag and Pd-Sn, and are interpreted in the same manner. In has two opposing effects upon the solubility of H in the Pd alloys: the first is the increase in the Fermi energy due to the donation of valence electrons and the second a lattice dilatation. When valence electron concentration is below 0.5, the lattice dilatation predominates and the H solubility is increased with addition of In. When valence electron concentration is above 0.5,the influence of the elevated Fermi energy predominates and the H solubility is lowered by additions of In. The molar enthalpy of Pd hydriding at infinite dilution is strongly increased with increasing in content, but the molar entropy is not affected abviously by the presence in In. The excess chemical potential of hydrogen at small hydrogen concentrations and at a given temperature increases with an increase in In content. The apparent H-H attractive interaction energy, w(HH) , is decreased by the presence of In. The trend is also similar to that found for the Pd-Ag-H and Pd-Sn-H system. Key words： palladium hydriding    valence electron    lattice dilatation    Fermi energy 收稿日期: 1996-05-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 陈仰霖 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1996/V32/I5/489 1BrodowskyH,PoeschelE．ZPhysChem,1965;NF44:1432BrodowskyH,HusemannH．ProcJpnInstMet．1980;21(Suppl):3653BrodowskyH．BerBunsengesPhysChem,1973;77:7424BrodowskyH,WickeE．EngelhardIndTechBull,1966;7(VL):415 WickeE,BrodowskyH,ZuchnerH．In:AlefeldG,VolklJ,eds．,HydrogeninMetalsII,Berlin:Springer-Verlag,1978:1186 BretschneiderTh,SchallerHJ．BerBunsengesPhysChem,1990;94:1857 ContardiV,MarazzaR,RambaidiG,ZanicchiG,FerroR．Z Metallk,1991;82:169 [1] 卢柯;刘学东;张皓月;胡壮麒. 纯镍纳米晶体的晶格膨胀[J]. 金属学报, 1995, 31(2): 74-78. Viewed Full text Abstract Cited   Shared      Discussed