Mg,RE复合微合金化Ni_3Al(B)-Cr基合金的中、高温性能

徐颂波;陈俊明

中国科学院上海冶金研究所

EFFECT OF MULTI-MICROALLOYING OF Mg AND RE ON MECHANICAL PROPERTIES OF Ni_3Al(B)-Cr BASE ALLOY AT ELEVATED TEMPERATURES

XU Songbo;CHEN Junming (Shanghai Institute of Metallurgy; Chinese Academy of Scicnces)(Manuscript received 18 January; 1994; in revised form 4 July; 1994)

引用本文:

徐颂波;陈俊明. Mg,RE复合微合金化Ni_3Al(B)-Cr基合金的中、高温性能[J]. 金属学报, 1994, 30(11): 521-524.
, . EFFECT OF MULTI-MICROALLOYING OF Mg AND RE ON MECHANICAL PROPERTIES OF Ni_3Al(B)-Cr BASE ALLOY AT ELEVATED TEMPERATURES[J]. Acta Metall Sin, 1994, 30(11): 521-524.

全文: PDF(328 KB)

摘要: 研究了Ｍｇ，ＲＥ复合微合金化Ｎｉ_３Ａｌ（Ｂ）－Ｃｒ基合金（合金Ⅱ）和加Ｚｒ的Ｎｉ３Ａｌ（Ｂ）－Ｃｒ基合金（合金Ⅰ）的中、高温性能．发现加入Ｍｇ，ＲＥ仍能保持合金反常的强度－温度特性．该两种合金在中、高温下的延伸率都有缓降区．剧降区及平稳区三个阶段，分别由位错阻碍，氧扩散及氧浓度稳定三种机制控制．合金Ⅱ比合金Ⅰ在更低的温度进入塑性剧降区可能和Ｍｇ，ＲＥ在晶界偏聚促进了氧的扩散有关．

关键词 ：Ｎｉ_３Ａｌ（Ｂ）－Ｃｒ基合金, Ｎｉ_３Ａｌ（Ｂ）－Ｃｒ－Ｍｇ－ＲＥ, 中高温性能

Abstract：Study was made of the mechanical properties at elevated temperatures of the Ni_3Al(B)-Cr base alloy multi-microalloyed by Mg and RE (alloy Ⅱ) or with additive of Zr (alloy Ⅰ). The temperature dependence on strength of the alloy Ⅱ, i.e., microalloyed by Mg and RE, keeps in abnormality. The temperature dependence on elongation of both alloys reveals into 3 regions:to drop slightly, sharply and then stably, which may be controlled by the mechanisms of dislocation barrier, oxygen diffusion and stable oxygen content respectively. The reason why the elongation of alloy Ⅱ falls into shaop drop region at lower temperature than that of alloy Ⅰ,may be that the oxygen diffusion is promoted by segregation of Mg and RE at grain boundaries. Correspondent:CHEN Junming, professor, Shanghai Institute of Metallurgy, Chinese Academy of Sciences, Shanghai 200050

Key words： microalloying Ni_3Al(B)-Cr base alloy Ni_3Al(B)-Cr-Mg-RE mechanical properties

收稿日期: 1994-11-18

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	徐颂波
	陈俊明
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y1994/V30/I11/521

1徐颂波,陈俊明．金属学报,1994,30:A,2212 PopeDP,EzzSS．IntMetallRev,1984,29:136-1673李辉,郭建亭,孙超,谭明晖,赖万慧,王淑荷．材料科学进展,1992;6:285-2894郭建亭,李辉,孙超,朱耀宵．金属学报,1989;25:A406-A415TienJK,Eng S,SanchenJ．In:StoloffNS,KochCC,LiuCT,IzumiOeds．,HighTemperatureOrderIntermetallicalloyⅡ,MaterResSocSympProc1987;81:183-1936 StoloffNS．IntMetallRev,1989;34:153-1847 HippsleyCA,StrangwoodM,DevanJH．ActaMetallMater,1990;38:2393-24108LjuCT,SikkaVK．J Met,1986;38:19-219 BirksN,MeierGH．IntroductiontoHighTemperatureOxidationofMetals．London:EdwardArnoldLtd．1983

[1]	徐颂波;陈俊明. Mg,RE复合微合金化提高Ni_3Al(B)-Cr基合金的室温塑性[J]. 金属学报, 1994, 30(5): 221-224.

Viewed

Full text

Abstract

Cited

Shared

Discussed