金属学报  1992, Vol. 28 Issue (5): 32-39

论文 本期目录 | 过刊浏览 |

冷轧Fe-P合金中磷的非平衡偏聚结构与取向间变化的关系

张立新;宁华;周敬;李黎光

中国科学院金属腐蚀与防护研究所腐蚀科学开放研究实验室;沈阳(110015)中国科学远金属腐蚀与防护研究所;中国科学院金属腐蚀与防护研究所腐蚀科学开放研究实验室;中国科学院金属研究所;中国科学院金属研究所

EFFECT OF NON-EQUILIBRIUM SEGREGATION OF P ON ORIENTATION VARIATION IN COLD ROLLED Fe-P ALLOY

ZHANG Lixin;NInG Hua;ZHOU Jing;LI Liguang Laboratory of Corrosion Science; Institute of Corrosion and Protection of Metals; Academia Sinica; Shenyang Institute of Metal Research; Academia Sinica; Shenyang Correspondent professor; Institute of corrosion and protection of Metals; Academia Sinica; Shenyang 110015).

张立新;宁华;周敬;李黎光. 冷轧Fe-P合金中磷的非平衡偏聚结构与取向间变化的关系[J]. 金属学报, 1992, 28(5): 32-39.
, , , . EFFECT OF NON-EQUILIBRIUM SEGREGATION OF P ON ORIENTATION VARIATION IN COLD ROLLED Fe-P ALLOY[J]. Acta Metall Sin, 1992, 28(5): 32-39.

摘要 参考文献 相关文章 Metrics 全文: PDF(1174 KB)   摘要: 用分析电镜及三维取向分布函数(ODF)法,研究Fe—P合金中磷的非平衡偏聚过程与取向变化的关系,结果表明,磷择优偏聚于{110}滑移面上,在450℃以上生成了重复周期为a=1.582nm的磷偏聚结构,合金在回复过程中已发生<001>∥ND取向减弱和<111>∥ND取向增强的变化,及{111}<110>转化为{111}<143>织构的倾向,再结晶后,{111}<143>取向转变为{111}<112>取向,本文提出磷的非平衡偏聚结构作用对取向变化的模型,获得满意解释。 关键词 ： Fe-P合金,  晶格像,  回复过程,  非平衡偏聚结构     Abstract：Using 3-dimensional orientation distribution function, study was made of theeffect of non-equilibrium segregation of P on the orientation variation in cold rolled Fe-P al-loy during annealing under analytical electron microscope. P is found to segregatepreferrentially on the {110} slip plane. The non-equilibriously sgregated P forms a structurewith repeat cycle a=1.582 nm over 450℃. The fiber texture may vary in decrease of <001>// ND and increase of <001>// ND, and transfer from {111} <110> to {111} <143> withtemperature raising during alloy recovery. After recrystallization, direction {111} <143>changes into {111} <112>. A proposed model about the formation of recrystallization tex-ture was fairly explained by structure of P non-equilibrium segregation. Key words： P non-equilibrium segregation structure    lattice image    recovery 收稿日期: 1992-05-18      基金资助:国家自然科学基金资助项目 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 张立新 宁华 周敬 李黎光 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1992/V28/I5/32 1 Grabke H J. Steel Res, 1986; 57: 178 2 Hu H. Metal Trans, 1977; 8A: 1567 3 张立新,曲哲,李黎光,魏文译.金属学报,1988;24:A336 4 宁华,张立新.金属学报,1990;26:A346 5 李正修,刘星浦,徐心和.控制与决策,1986;(3) :16 6 张立新,李黎光,魏文铎.见:师昌绪主编,汽车薄板及成形技术,中国薄钢板成形技术研究会,1990:300 7 梁志德,徐家桢,王福.织构材料的三维取向分析技术.沈阳:东北工学院出版社,1986:108| [1] 邓文;熊良钺;龙期威. Ni-Cr-Co高温合金回复行为的正电子湮没研究[J]. 金属学报, 1991, 27(6): 145-149. Viewed Full text Abstract Cited   Shared      Discussed