NdCl_3-MgCl_2-LiCl系液相限的研究
郑朝贵;靳军;叶于浦
北京大学化学系;北京大学;北京大学
LIQUIDUS OF NdCl_3-MgCl_2-LiCl SYSTEM
ZHENG Chaogui;JIN Jun;YE Yupu Peking University
引用本文:

郑朝贵;靳军;叶于浦. NdCl_3-MgCl_2-LiCl系液相限的研究[J]. 金属学报, 1989, 25(1): 147-149.
, , . LIQUIDUS OF NdCl_3-MgCl_2-LiCl SYSTEM[J]. Acta Metall Sin, 1989, 25(1): 147-149.

全文: PDF(199 KB)  
摘要: 本文借助于DTA研究了NdCl_3-MgCl_2-LiCl三元体系的液相限。发现:本体系内有对应于NdCl_3和α-固溶体(MgCl_2,LiCl)的两个液相面和一条带有最低点的二次结晶线,其最低点M的组成与温度为:68.5wt-%NdCl_3,2.7wt-%MgCl_2,28.8wt-%LiCl;441℃。
关键词 NdCl_3NdCl_3-MgCl_2-LiCl三元体系液相限    
Abstract:The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by meansof DTA. It was found that there are two surfaces corresponding to the primary crystallization ofNdCl_3 and α-(MgCl_2, LiCl) respectively, and an univariant line related to the secondary crystal-lization with a minimun point M (68.5 wt-% NdCl_3, 2.7 wt-% MgCl_2, 28.8 wt-% LiCl, 441℃)in the system.
Key wordsNdCl_3    NdCl_3-MgCl_2-LiCl    ternary system    liquidus
收稿日期: 1989-01-18     
1 张翊凤,郑朝贵,叶于浦.第四届全国熔盐化学及电化学学术会议论文集,郑州,1987:130
2 #12
3 Vogel G, Schneider A. Inorg Nucl Chem Lett, 1972; 8: 513
4 Sandonnini C. Atti Accad Naz Lincei Rend. Classe Sci Fis, Mat Nat, 1931; 22 (5) : 631
5 郑朝贵,张亚钢,陈集林,叶于浦.北京大学学报(自然科学版),1987;(6) :72
6 郑朝贵,叶于浦.高等学校化学学报,1988;9(5) :423
7 郑朝贵,靳军,叶于浦.中国稀土学报,(待发表
[1] 于锦;于永栗;王之昌. 火法气态传输分离混合稀土氯化物[J]. 金属学报, 1997, 33(4): 391-394.
[2] 刘淑祺;易涛. Au-Cu-Si三元系液相限[J]. 金属学报, 1990, 26(4): 153-154.
[3] 刘淑祺;易涛. Ag-Cu-Ge三元系液相限[J]. 金属学报, 1989, 25(2): 155-156.
[4] 刘淑祺;孙文庆. Ag-Cu-Bi三元系的液相限[J]. 金属学报, 1988, 24(5): 448-450.
[5] 张翊凤;郑朝贵;叶于浦. NdCl_3-LiCl-KCl体系相图的研究[J]. 金属学报, 1988, 24(4): 309-313.