含Co,Cr,Si的铜合金中Co_5Cr_3Si_2相的行为

庄应烘

南宁市广西大学物理系

BEHAVIOUR OF Co_5 Cr_3 Si_2 PHASE IN Cu-RICH ALLOYS CONTAINING Co, Cr AND Si

ZHUANG Yinghong Guangxi University; Nanning

庄应烘. 含Co,Cr,Si的铜合金中Co_5Cr_3Si_2相的行为[J]. 金属学报, 1988, 24(6): 521-523.
. BEHAVIOUR OF Co_5 Cr_3 Si_2 PHASE IN Cu-RICH ALLOYS CONTAINING Co, Cr AND Si[J]. Acta Metall Sin, 1988, 24(6): 521-523.

摘要 参考文献 相关文章 Metrics 全文: PDF(617 KB)   摘要: 本文研究了含Co,Cr,Si富Cu合金中Co_5Cr_3Si_2(x相)的行为。结果表明,合金的主要组成相有α-Cu基体,x相和Co_2Si相。x相属立方晶系,α-Mn型,α=0.8694nm。x相和合金的熔点分别为1265和1116℃。 关键词 ： 富铜合金(含Co,Cr,Si),  X相     Abstract：The major phases in the Cu-rich alloys containing Co. Cr and Si are α-Cu (asolid solution of Co. Cr and Si in Cu). X-phase (Co_5Cr_3Si_2) and Co_2Si. In comparison with ref-erence sample, it was detected that the Co_5Cr_3Si_2 is of cubic system, α-Mn type and α=0.8694nm. The melting temperatures of X-phase and the alloy are higher than that of pure Cu. name-ly, 1535 and 1389 K respectively. During aging treatment, the Co_2Si phase precipitates out fromα-Cu and X-phase simutaneously, but the hardening effect is mainly contributed by the precipi-tation from α-Cu. Key words： Cu-rich alloy    χ-phase 收稿日期: 1988-06-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 庄应烘 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1988/V24/I6/521 1 #12 2 #12 3 庄应烘,孙精勤,陈奇勇.稀有金属,(待发表) 4 1962; 3: 414--423 5 Boren B, Stahl S, Westgren A. Z Phys Chem, 1935; B29: 231--235 6 Schubert K, Pfisterer H. Z Metallk, 1950; 41: 438 7 Hansen M, Anderko K. Constitution of Binary Alloys, New York: McGraw-Hill, 1958 No related articles found! Viewed Full text Abstract Cited   Shared      Discussed