Cu-Al-Zn-Mn-Ni合金马氏体形态和晶体结构对伪弹性的影响

杨建华;刘彩虹;赵连城;雷廷权

哈尔滨工业大学;哈尔滨工业大学;哈尔滨工业大学;哈尔滨工业大学

INFLUENCE OF MARTENSITE MORPHOLOGY AND CRYSTAL STRUCTURE ON THE PSEUDOELASTICITY IN A Cu-Al-Zn-Mn-Ni ALLOY

by YANG Jianhua; LIU Caihong; ZHAO Liancheng; LEI Tingquan (Harbin Institute of Technology) (Manuscript received 25 october; 1985; revised manuscript 15 July; 1986)

杨建华;刘彩虹;赵连城;雷廷权. Cu-Al-Zn-Mn-Ni合金马氏体形态和晶体结构对伪弹性的影响[J]. 金属学报, 1987, 23(6): 470-476.
, , , . INFLUENCE OF MARTENSITE MORPHOLOGY AND CRYSTAL STRUCTURE ON THE PSEUDOELASTICITY IN A Cu-Al-Zn-Mn-Ni ALLOY[J]. Acta Metall Sin, 1987, 23(6): 470-476.

摘要 参考文献 相关文章 Metrics 全文: PDF(1124 KB)   摘要: 本文研究了Cu-Al-Zn-Mn-Ni合金的伪弹性变形行为,并用金相和X射线衍射法观察分析了变形及时效前后马氏体组织结构的变化。结果表明,合金在母相状态时的伪弹性与其原始马氏体组织结构密切相关;通过改善原始马氏体组织结构的自协作性和适当的时效处理可以显著提高合金的伪弹性。 Abstract：The deformation behaviour of parent phase and the pseudo-elasticity were studied, and the variation of microstructure with aging and deforming was analyzed using optical microscopy and X-ray diffraction. The experimental results showed that the pseudoelasticity in parent phase state is closely related to the original martensite microstructures. The pscudoelasticity of the alloy can be considerably improved with the perfection of martensitic self-accommodation and proper ageing treatment. 收稿日期: 1987-06-18      基金资助:中国科学院科学基金资助的课题 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 杨建华 刘彩虹 赵连城 雷廷权 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1987/V23/I6/470 1 Abu-Arab A, Chandrasekaran M, Ahlers M. Scr Metall, 1984; 18: 709 2 赵连城,杨建华,刘乃华,雷廷权.稀有金属,1986,5:281 3 Yang J H, Zhao L C, Zhang C S, Lei T C. Scr Metall, 1987; 21(3) 4 赵连城,杨建华,刘乃华,张春生,雷廷权,顾华,何永枢.金属学报,1987;23A380: 5 Delaey L, Krishnan R V, Tas H, Warlimont H. J Mater Sci, 1974; 9: 1521 6 Van Humbeeck J. Janssen J, Mwamba-Ngoie, Delaey L. Scr Metall, 1984; 18: 893 7 Delaey L, Suzuki T, Van Humbeeck J. Scr Metall, 1984; 18: 899 No related articles found! Viewed Full text Abstract Cited   Shared      Discussed