STRESS INDUCED TRANSFORMATION IN SUPERELASTIC NiTi ALLOY
by JIN Jialing; ZHANG Yi (Shanghai Institute of Iron and Steer Research)
引用本文:

金嘉陵;张一. 超弹性NiTi合金的应力诱发相变[J]. 金属学报, 1986, 22(4): 59-62.
, . STRESS INDUCED TRANSFORMATION IN SUPERELASTIC NiTi ALLOY[J]. Acta Metall Sin, 1986, 22(4): 59-62.

全文: PDF(1404 KB)  
摘要: <正> 我们新研制的51.6at.-%Ni-Ti合金可以通过热处理获取超弹特性,该合金的应力诱发相变过程包括两个阶段——预马氏体转变和马氏体转变,分别与σ-ε曲线的不同线段相对应,整个相变过程在卸载时完全可逆。这个结论与通常的解释不完全一致。本文对该相变过程作进一步的研究。 实验在H1TACH H-700型透射电镜上加载观察,其拉伸台由马达驱动,对样品作速度连续可调的单向拉伸,拉伸位移的指示精度为20μm/格。试样制成~3×5mm条
Abstract:The process of stress induced transformation in 51.6 at-%Ni-Ti alloy has been studied by means of X-ray diffraction and TEM equipped with loading attachment The results show that the process may proceed as two stages: premartensitie and martensitie transformations It seems to be reversible with unloading
收稿日期: 1986-04-18     
1 金嘉陵,金属学报,20(1984) ,A176.
2 徐祖耀,马氏体相变与马氏体,科学出版社,1980,p.502.
3 Perkins, J., Metall. Trans., 4 (1973) , 2709.
4 De Lange, R.G.; Zijderveld, J.A., J.Appl. Phys., 39 (1968) , 2195.
No related articles found!