金属学报  1986, Vol. 22 Issue (1): 87-150

论文 本期目录 | 过刊浏览 |

表面状态对TCⅡ钛合金热盐应力腐蚀的影响

虞炳西;张绥生;万晓景

中国科学院金属研究所;中国科学院金属研究所;中国科学院金属研究所

INFLUENCE OF SURFACE CONDITIONS ON HOT SALT STRESS CORROSION CRACKING OF Ti ALLOY TC11

YU Bingxi; ZHANG Suisheng; WAN Xiaojing (Institute of Metal Research; Academia Sinica; Shenyang)

虞炳西;张绥生;万晓景. 表面状态对TCⅡ钛合金热盐应力腐蚀的影响[J]. 金属学报, 1986, 22(1): 87-150.
, , . INFLUENCE OF SURFACE CONDITIONS ON HOT SALT STRESS CORROSION CRACKING OF Ti ALLOY TC11[J]. Acta Metall Sin, 1986, 22(1): 87-150.

摘要 参考文献 相关文章 Metrics 全文: PDF(1493 KB)   摘要: 本文测定了TC11钛合金在350—500℃范围内的热盐应力腐蚀临界应力及五种不同表面状态对热盐应力腐蚀的影响。结果表明在试验温度范围内存在热盐应力腐蚀敏感性。通过不同表面状态的对比实验,证实表面阳极氧化处理能有效地提高钛合金的热盐应力腐蚀性能。氧化膜起了减缓有害物质向金属基体扩散的作用,适当地增加膜的厚度有利于提高抗热盐应力腐蚀性能。同时从表面喷丸试样的研究中表明,表面压应力的存在也能够改善抗热盐应力腐蚀性能,在430℃以下效果较为显著,但是,随着温度的增加这种有益的影响将会逐渐消失。 Abstract：The evaluation of the threshold stress of hot salt stress corrosion cracking (HSSCC) of Ti alloy TC11 in temperature range from 350 to 500℃ under laboratory condition and of its susceptibility influenced by five different surface conditions was made. In comparison among them, it was believed that the susceptibility of Ti alloy TC11 to HSSCC may be effectively improved by anodizing its surface owing to retarding the aggressive materials diffused through the oxide layer into substrate. The surface treatment of shot peening may also improve the resistance to HSSCC, especially, at temperature below 430℃. However, no more improvement over its surface resistance by the compressive stress is noticed in increasing temperature. 收稿日期: 1986-01-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 虞炳西 张绥生 万晓景 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1986/V22/I1/87 1 Gray, H.R., Corrosion, 25 (1969) , 337． 2 虞炳西;张绥生;万晓景,金属学报,18 (1982) ,264． 3 崔树国;邹军军,金属研究所未发表资料,1982． 4 Ondrejcin, R.S., NASA CR-1829, 1971． 5 Ondrejcin, R.S., Metall. Trans., 1 (1970) , 3031． 6 Jostons, A.; Jenkins, A.E., Trans. Metall. Soc. AIME, 239 (1967) , 1318． No related articles found! Viewed Full text Abstract Cited   Shared      Discussed