抑制剂对取向硅钢再结晶行为的影响

何忠治;孙学范;帅仁杰

冶金工业部钢铁研究总院;冶金工业部钢铁研究总院;冶金工业部钢铁研究总院

BEHAVIOUR OF SECONDARY RECRYSTALLIZATION IN ORIENTED Si STEEL CONTAINING VARIOUS INHIBITORS

HE Zhongzhi;SUN Xuefan;SHU AI Renjie Central Iron and Steel Research Institute;Ministry of Metallurgical Industry;Beijing

何忠治;孙学范;帅仁杰. 抑制剂对取向硅钢再结晶行为的影响[J]. 金属学报, 1985, 21(2): 32-36.
, , . BEHAVIOUR OF SECONDARY RECRYSTALLIZATION IN ORIENTED Si STEEL CONTAINING VARIOUS INHIBITORS[J]. Acta Metall Sin, 1985, 21(2): 32-36.

摘要 参考文献 相关文章 Metrics 全文: PDF(397 KB)   摘要: 比较几种抑制剂对取向硅钢初次再结晶和二次再结晶行为的影响,证明AlN比MnS有更强的抑制作用.(110)[001]二次晶核优先发生在距热轧板表面1/5—1/4深度的薄层区域.含AlN钢的这类晶核呈饼状,二次晶粒长大是各向异性的.含MnS钢的二次品粒长大是各向同性的. Abstract：A comparison was made of the action of various inhibitors to certain highpermeability oriented Si steels on the behaviour of primary and secondary recrys-tallization.It is shown that the inhibitory action of AlN is superior to that ofMnS.The suitable average diameter of the primary grains is 15—20 or 10—12μm for two-stage or single-stage cold-rolling process respectively.The stability ofprimary recrystallized matrix is more important than primary grain size.The(110)[001]secondary grains nucleated preferentially at about 1/5-1/4 thick beneathsurface layer of the hot-rolled band.Such prior secondary recrystallizationnucleus of the steel containing AlN inhibitor is in pancake-like shape and the graingrowth is anisotropy.However,the secondary grain growth of the steel containingMnS inhibitor is isotropic.It seems that the secondary grains in the neighbourhoodof the identical(110)[001]orientation may grow into contact with each otherand coalesce to coarse secondary crystals. 收稿日期: 1985-02-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 何忠治 孙学范 帅仁杰 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1985/V21/I2/32 1 Littmann,M.F.;Dahlstrom,N.A.,J.Appl.Phys.,49(1978) ,2034． 2 Sakai,T.;Matsuo,M.;Tanino,M.;Shindo,T.;Shiozaki,M.,Proc.of the 6th Int.Conf.on Texture of Materials,Ed.Nagashima Shinichi,The Iron Steel Inst.Jpn,Tokyo,1981,p.938． 3 #12 4 Hu H.(胡郇),Recovery and Recrystallization of Metals,Ed.Himmel,L.,Interscience,New York,1963,p.311． 5 #12 6 Pease,N.C.;Jones,D.W.;Wise,M.H.L.;Hutchinson,W.B.,Met.Sci.,15(1981) ,203． No related articles found! Viewed Full text Abstract Cited   Shared      Discussed