金属学报  1981, Vol. 17 Issue (1): 44-49

论文 本期目录 | 过刊浏览 |

W和Co对Ni-20Cr基合金高温蠕变行为的影响

杨枏森;魏育环;傅宏镇;李文高;唐荣德

冶金工业部钢铁研究总院;冶金工业部钢铁研究总院;冶金工业部钢铁研究总院;冶金工业部钢铁研究总院;抚顺钢厂

INFLUENCE OF W AND Co ON HIGH TEMPERATURE CREEP BEHAVIOUR OF Ni-20Cr BASE ALLOYS

Yang Nansen; Wei Yuhuan; Fu Hongzhen and Zt Wengao (Central Institute of Iron and Steel Research; Ministry of Metallurgical Industry) and Tang Rongde (Pushun Steel Works)

杨枏森;魏育环;傅宏镇;李文高;唐荣德. W和Co对Ni-20Cr基合金高温蠕变行为的影响[J]. 金属学报, 1981, 17(1): 44-49.
, , , , . INFLUENCE OF W AND Co ON HIGH TEMPERATURE CREEP BEHAVIOUR OF Ni-20Cr BASE ALLOYS[J]. Acta Metall Sin, 1981, 17(1): 44-49.

摘要 参考文献 相关文章 Metrics 全文: PDF(371 KB)   摘要: 本文研究了不同W和Co含量的Ni-20Cr基合金的高温稳态蠕变行为。结果表明,W和Co均可提高合金的蠕变激活能Q_c,它服从Q_c=Ae~(kx/lge的关系.Ni-Cr-Co-W合金的稳态蠕变速率(?)_s也服从(?)_s=Cσ~mexp(-Q_c/RT)的关系。还指出,Ni-Cr-Co-W合金的稳态蠕变速率(?)_s与堆垛层错能γ之间,有(?)_s ∝γ~(1.4)的关系。 Abstract：The steady state creep behaviour of the Ni-20Cr base alloys with various contents of W and Co has been investigated in the temperature range of 940 to 1040℃. Both W and Co may raise the activation energy for creep, Qo, obeyed the relationship:Q_c=Ae~(kx/lg~(?)) where x is the atomic fraction of W or Co additions; A is a constant for the alloy composition and k is equal to 7.0 and 0.55 for W and Co additions respectively. The steady state creep rate (?)_s of Ni-Cr-Co-W alloys was predicated to be:(?)_s=Cσ~m exp (-Q_e/RT) where m=6.45±0.10 or 5.3 depending on whether μ phase is present or not. It was also shown that the (?)_s varies with the stacking fault energy γ according to the correlation:(?)_s∞γ~(1.4) 收稿日期: 1981-01-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 杨枏森 魏育环 傅宏镇 李文高 唐荣德 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1981/V17/I1/44 [1] 陈篪,邓枝生,吴伯群,丁树深,物理学报,23(1974) ,69．屯王 No related articles found! Viewed Full text Abstract Cited   Shared      Discussed