金属学报  1964, Vol. 7 Issue (1): 43-57

论文 本期目录 | 过刊浏览 |

横锻及横轧时金属的变形与破裂的研究

张作梅;黎俊结

中国科学院光学精密机械研究所;中国科学院光学精密机械研究所

AN INVESTIGATION ON THE DEFORMATION AND CRACK FORMATION OF METALS IN CROSS FORGING AND CROSS ROLLING

CHANG TSO-MEI; LEE TSUN-JEH(Institute of Optics & Fine Mechanics; Academia Sinica)

张作梅;黎俊结. 横锻及横轧时金属的变形与破裂的研究[J]. 金属学报, 1964, 7(1): 43-57.
, . AN INVESTIGATION ON THE DEFORMATION AND CRACK FORMATION OF METALS IN CROSS FORGING AND CROSS ROLLING[J]. Acta Metall Sin, 1964, 7(1): 43-57.

摘要 参考文献 相关文章 Metrics 全文: PDF(2080 KB)   摘要: 在200—300毫米輥径的横軋机上于不同溫度、速度、变形程度、变形区长度与直径之比以及外端等条件下,用金相法和硬度法对各鋼种的圓棒的变形分布和中心破裂进行了研究。在冲床上用端面画有同心圓的鋁棒和鉛棒进行了常溫的旋轉橫鍛試驗,以了解横鍛横軋时金属的变形分布。試驗結果表明: 1.一次横鍛时,表面层的变形最大,越靠中心变形愈小。当压縮率不大时,中心处可能只发生弹性变形。 2.旋轉橫鍛时,表面层和中心区的塑性变形較大,过渡区的变形最小。当变形率很小时,塑性变形亦可能不致于深入到中心区。 3.横軋时金属的变形規律与旋轉橫鍛时相似,但在压縮很小时,断面中心只发生弹性变形。 4.横軋时,軋制溫度、軋制速度增高,压縮率及变形长度与直径比越大,外端越小,中心破裂愈易产生。 Abstract：The key to successful cross rolling is to understand fully the distribution of deformation and the mechanism of crack formation at the centre of the rolled material as well as the optimum parameters for the technological process. With these points in mind, the authors carried out investigations by means of microscopic examinations and hardness tests on the distribution of deformation and the mechanism of crack formation at the centre of certain steel specimens at various temperatures, various rates of deformation, different ratios between the length of the plastic zone and the specimen diameters as well as at different lengths of material at both ends of the plastic zone.As the deformation of metals in cross rolling is in many ways similar to that in cross forging, the authors carried out experiments on the cross forging of aluminium and lead which had been marked with concentric circles at the ends in a 35-ton mechanical press at room temperatures, and then compared the results thus obtained with those in the cross rolling of carbon and alloy steels.The results of these experiments show that:(1) With only one strike of the press in cross forging, the deformation is greatest at the surface and diminishes towards the centre of the specimen. When reduction is small, only elastic deformation occurs at the centre.(2) With several strikes of the press on rotating specimens, the deformation at the surface and in the centre is greater than that in the intermediate zone. When reduction is very small, plastic deformation also does not penetrate into the centre.(3) Similar to cross forging, the deformation of metal in cross rolling is also greatest at the surface, less at the centre and least in the intermediate zone. This distribution of deformation remains practically unchanged in different metals and various rolling temperatures as well as under other testing conditions mentioned above. Under conditions of the present experiments, when reduction is small, the deformation at the centre may be only elastic. In this case, the distribution of deformation is similar to that with only one strike of the press in cross forging.In cross rolling, the greater the reduction, the higher the rolling temperature, the higher the rate of deformation, the greater the ratio between the length of the plastic zone and the specimen diameter, and the shorter the length of the material on either side of the plastic zone, the greater is the tendency for crack formation at the centre. Alloy steels seem less liable to crack formation than carbon steels. 收稿日期: 1964-01-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 张作梅 黎俊结 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1964/V7/I1/43 [1] #12 [2] #12 [3] #12 [4] #12 [5] #12 [6] #12 [7] #12 [8] #12 [9] #12 [10] #12 [11] #12 No related articles found! Viewed Full text Abstract Cited   Shared      Discussed