金属学报  1958, Vol. 3 Issue (1): 47-54    
  论文 本期目录 | 过刊浏览 |
国产工业纯铁织构的磁转矩法研究
戴礼智;王建纲
北京钢铁研究所;北京钢铁研究所
A STUDY OF THE TEXTURES OF ARMCO IRON BY MAGNETIC TORQUE METHOD
TAI LI-CHI(L.C.TAI)AND WANG CHIEN-KANG Iron and Steel Research Institute
全文: PDF(522 KB)  
摘要: <正> 一、引言具有体心立方品格的α-Fe的织构早为许多研究者所注意,可是所用材料大多为低碳钢或Fe-Si合金。对于纯铁的数据比较少见.G.Kurdjumov和G.Sachs曾进行电解铁的轧制和再结晶织构的研究,压延率为98.5%,而没有叙及易磁向的再结晶织构.最近Haeβner和Weik用交叉轧制法研究化学方法制备的纯铁,经80%压延率在580℃熟炼150分后,得到易磁化取向.可是用普通方法轧制获得易磁向强构的资料就少见到.
Abstract:The rolling and recrystallization textures of armco iron are measured by magnetictorque method.Samples after hot-rolling are then cold rolled in three different ways;i.e.,thepercentages of the cold reduction are(i)73,(ii)65 and(iii)22.The class Ⅰ andclass Ⅲ material are annealed for one hour either at 700° or 850℃,and then givena second cold roll,the reduction of class Ⅰ material being this time 65 per cent andclass Ⅲ material being 55 per cent.All these samples in these three categories aregiven a final anneal at 870℃ in hydrogen for ten hours.The textures of the samples through one cycle of cold rolling are determined as(100)[011]and(112)[110].The textures of the material through two cycles ofcold rolling,with an intermediate anneal,are mainly(112)[110].The final annealedsamples with the possible exception of the class Ⅲ are estimated as having textures(110)[001]and(110)[001]+(100)[001].
收稿日期: 1958-01-18     

引用本文:

戴礼智;王建纲. 国产工业纯铁织构的磁转矩法研究[J]. 金属学报, 1958, 3(1): 47-54.
. A STUDY OF THE TEXTURES OF ARMCO IRON BY MAGNETIC TORQUE METHOD. Acta Metall Sin, 1958, 3(1): 47-54.

链接本文:

https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1958/V3/I1/47

[1] Wassermann,G.,Texturen metallischer Werkstoffe(1939) .
[2] Goss,N.P.,Trans.A.S.S.T.,16(1929) ,405.
[3] Stanley,J.K.,Trans.A.I.M.E.,158(1944) ,354.
[4] #12
[5] Kurdjumov,G.u Sachs,G.,ZS.für Physik,62(1930) ,592.
[6] Haeβner,F.u Weik,H.,Archiv des Eisenhüttenw.,27,Heft 3(1956) ,153.
[7] 戴礼智,张信钰,国产纯铁轧[制与再结晶织构,物理学报,第14卷,第1期.
[8] Bozorth,R.M.,Ferromagnetism(1951) ,ch.XII.q
No related articles found!